DP810NS-TAN-200ML

Scotch-Weld™ Low Odor Acrylic Adhesives DP810 • DP810 Black • DP810NS Technical Data June 2019 Product Description 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. These adhesives have excellent shear and peel strength along with good impact resistance and durability. They can quickly bond to most metals, ceramics, rubbers, plastics and wood with minimal surface preparation. Features • Tough, durable bonds • Low odor acrylic adhesive • Minimal surface prep • 10-minute work life • 20-minute time to handling strength • 1:1 mix ratio • Bonds stainless steel • Excellent shear and peel strength Typical Uncured Physical Properties Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive Property DP810 DP810 Black DP810NS Color Base (B) Accelerator (A) Green White Black White Blue/Green White Lbs./gal. Base (B) Accelerator (A) 8.7 - 9.1 8.7 - 9.1 8.7 - 9.1 8.7 - 9.1 8.7 - 9.1 8.7 - 9.1 Viscosity (cps)(1) Base (B) Accelerator (A) 18,000 - 22,000 18,000 - 22,000 18,000 - 22,000 17,000 - 21,000 90,000 - 95,000 95,000 - 100,000 Base Resin Base (B) Accelerator (A) Acrylic Acrylic Acrylic Acrylic Acrylic Acrylic Mix Ratio (Volume) (Weight) 1:1 1:1 1:1 1:1 1:1 1:1 Time to Handling Strength (50 psi) 20 minutes 20 minutes 20 minutes Full Cure @ 73°F (23°C) 8 - 24 hours 8 - 24 hours 8 - 24 hours Work Life @ 73°F (23°C) 10 minutes 10 minutes 10 minutes For footnotes, see Test Methods and Footnotes on Page 4. 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP810 • DP810 Black • DP810NS Typical Performance Characteristics Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Overlap Shear Strength (psi)(2), tested @ 73°F (23°C) 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive Substrate DP810 DP810 Black DP810NS Etched Aluminum 4200 CF 4200 CF 4200 CF Abraded Aluminum 3900 CF 3750 CF 3700 CF Bare Aluminum 3800 CF 3850 CF 4100 CF CRS 3100 CF 3600 CF 3100 CF Oily CRS 3450 CF 3450 CF 3500 CF Stainless Steel 3400 CF 3500 CF 3400 CF Green FRP 3800 CF 3000 CF 1900 CF Acrylic 1100 SF 550 MM 700 SF PVC 1000 SF 1000 SF 800 SF Polycarbonate 850 MM 500 MM 500 MM ABS 600 MM 700 MM 900 MM Overlap Shear Strength (psi), tested @ temperature 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive Temperature DP810 DP810 Black DP810NS -20°F (-29°C) 1750 MM 2000 MM 1000 AF 75°F (24°C) 3650 CF 3550 CF 3700 CF 120°F (49°C) 2000 CF 2000 CF 2350 CF 180°F (82°C) 550 CF 500 CF 1000 CF T-Peel Strength (piw)(3), tested @ 73°F (23°C) 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive Substrate Etched Aluminum SF = Substrate Failure/Break CF = Cohesive Failure AF = Adhesive Failure MM = Mixed (Mode of AF and CF) For footnotes, see Test Methods and Footnotes on Page 4. -2- DP810 DP810 Black DP810NS 30 20 23 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP810 • DP810 Black • DP810NS Environmental Resistance(4) Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Overlap Shear Strength (psi), tested @ 73°F (23°C) 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive Time DP810 DP810 Black DP810NS Control 14 Days 3900 CF 3750 CF 3700 CF 160°F (71°C)/100% RH 14 Days 1500 MM 1500 MM 1250 AF 160°F (71°C)/Soak 14 Days 1750 MM 1650 MM 1600 AF 20% Bleach 14 Days 3450 CF 3250 CF 3750 CF IPA 14 Days 3150 CF 3050 CF 3200 CF 50% Antifreeze 14 Days 3850 CF 3900 CF 4000 CF Gasoline 14 Days 2550 CF 2550 CF 3000 CF Diesel Fuel 14 Days 4000 CF 3950 CF 4050 CF Toluene 14 Days 2650 CF 2600 CF 3400 CF MEK 14 Days 50 CF 75 CF 1000 CF Acetone 14 Days 75 CF 50 CF 900 CF Condition CF = Cohesive Failure MM = Mixed (Mode of AF and CF) AF = Adhesive Failure Typical Rate of Strength Build-Up Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Overlap Shear Strength (psi), tested @ 73°F (23°C) at various times after bonding. 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP810 DP810 Black DP810NS 10 minutes 50 30 500 20 minutes 1500 1150 1750 1 hour 2250 2200 2850 2 hours 2750 2700 3350 4 hours 2950 2900 3700 8 hours 3350 3200 3850 24 hours 3600 3550 4000 Condition For footnotes, see Test Methods and Footnotes on Page 4. -3- 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP810 • DP810 Black • DP810NS Test Methods and Footnotes 1) Viscosity obtained by Brookfield, DV-II, #7 Spindle, 20 rpm at 75°F (24°C). 2) Overlap Shear Test Method: overlap shear test for adhesion determined in accordance to ASTM D1002-72, sample dimensions were 1" x 4" x 1/8", with a 1/2 square inch area of overlap, bonded to themselves unless otherwise noted, allowed to cure for at least 6 hours at 75°F (24°C) before testing. Data were collected using a Sintech 5GL Mechanical Tester with a 2000# or 5000# load cell. Test rate was 0.1"/minute. Strength determined at 75°F (24°C) unless otherwise noted. 3) Peel tests (ASTM D1876-61T) on FPL etched, 0.032” gauge aluminum, with a .017" bondline thickness. Jaw separation rate 20"/min. All bonds were allowed to cure for at least 6 hours at 75°F (24°C) before testing. 4) Environmental tests were conducted by immersing bonded coupons prepared in accordance to description in footnote 2. -4- 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP810 • DP810 Black • DP810NS Handling/Curing Information Directions for use: Apply adhesive to clean, dry substrates, which are free of paint, oxide films, oils, dust, mold release agents and all other surface contaminants. See the Surface Preparation section for specific substrate preparation method. 48.5 ml cartridge: Place Duo-Pak cartridge in 3M™ EPX Applicator. Remove cap. Dispense and discard a small amount of adhesive to assure even ratio and free flow. Clear orifice if necessary. Attach mixing nozzle. Apply adhesive to clean surfaces, join parts, secure until adhesive sets. 200/400 ml cartridge: While holding Duo-Pak cartridge in an upright position, remove and discard the insert from the cartridge by unscrewing plastic nut and removing metal washer. Place cartridge in a 1:1 200/400 ml EPX applicator. Dispense and discard a small amount of adhesive to ensure even ratio and free flow. Attach mixing and nozzle and secure with plastic retaining nut. Apply adhesive to clean surfaces, join parts, secure until adhesive sets. Clean-up: Excess adhesive can be removed with solvent such as MEK*. Edge tack on a finished part or bond line can be removed with isopropyl alcohol.* *Note: When using solvents, extinguish all ignition sources and follow the manufacturer’s precautions and directions for use. Heat Cure: Full cure can be attained by raising the bondline temperature to 120°F (49°C) for 30 minutes or to 150°F (66°C) for 10 minutes. -5- 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP810 • DP810 Black • DP810NS Surface Preparation 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives can bond oily metal, plastic and other substrates with very little surface preparation. However, for the most consistent results and environmental resistance, all substrates should be clean, dry and free of paint, oxide films, dust, mold release agents and all other surface contaminants. The amount of surface preparation directly depends on the bond strength and environmental resistance desired by the user. The following cleaning methods are suggested for common surfaces. Steel and Aluminum 1) Wipe free of dust with oil-free solvent such as acetone or isopropyl alcohol. 2) Sandblast or abrade using clean fine grit abrasives (180 grit or finer). 3) Wipe again with solvent to remove loose particles. 4) If a primer is used, it should be applied within 4 hours after surface preparation (or see instructions pertinent to a specific primer). Note: Aluminum may also be acid etched. Follow the manufacturer’s precautions and directions for this procedure. Plastic/Rubber 1) Wipe with isopropyl alcohol.* 2) Abrade using fine grit abrasives (180 grit or finer). 3) Remove residue by wiping again with isopropyl alcohol.* *Note: When using solvents, extinguish all ignition sources and follow the manufacturer’s precautions and directions for use. -6- 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP810 • DP810 Black • DP810NS Storage For maximum shelf life, store Duo-Pak cartridges and bulk containers at 32°F (0°C) to 40°F (4°C). Do not freeze. Shelf Life When stored at the recommended temperatures in the original unopened containers, this product has a shelf life of 15 months from date of manufacture when in cartridges; and 12 months from date of manufacture when in pails. Precautionary Information Refer to Product Label and Material Safety Data Sheet for health and safety information before using this product. For additional health and safety information, call 1-800-364-3577 or (651) 737-6501. Technical Information The technical information, guidance, and other statements contained in this document or otherwise provided by 3M are based upon records, tests, or experience that 3M believes to be reliable, but the accuracy, completeness, and representative nature of such information is not guaranteed. Such information is intended for people with knowledge and technical skills sufficient to assess and apply their own informed judgment to the information. No license under any 3M or third party intellectual property rights is granted or implied with this information. Product Selection and Use Many factors beyond 3M’s control and uniquely within user’s knowledge and control can affect the use and performance of a 3M product in a particular application. As a result, customer is solely responsible for evaluating the product and determining whether it is appropriate and suitable for customer’s application, including conducting a workplace hazard assessment and reviewing all applicable regulations and standards (e.g., OSHA, ANSI, etc.). Failure to properly evaluate, select, and use a 3M product and appropriate safety products, or to meet all applicable safety regulations, may result in injury, sickness, death, and/or harm to property. Warranty, Limited Remedy, and Disclaimer Unless a different warranty is specifically stated on the applicable 3M product packaging or product literature (in which case such warranty governs), 3M warrants that each 3M product meets the applicable 3M product specification at the time 3M ships the product. 3M MAKES NO OTHER WARRANTIES OR CONDITIONS, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO, ANY IMPLIED WARRANTY OR CONDITION OF MERCHANTABILITY, FITNESS FOR A PARTICULAR PURPOSE, OR ARISING OUT OF A COURSE OF DEALING, CUSTOM, OR USAGE OF TRADE. If a 3M product does not conform to this warranty, then the sole and exclusive remedy is, at 3M’s option, replacement of the 3M product or refund of the purchase price. Limitation of Liability Except for the limited remedy stated above, and except to the extent prohibited by law, 3M will not be liable for any loss or damage arising from or related to the 3M product, whether direct, indirect, special, incidental, or consequential (including, but not limited to, lost profits or business opportunity), regardless of the legal or equitable theory asserted, including, but not limited to, warranty, contract, negligence, or strict liability. Industrial Adhesives and Tapes Division 3M Center, Building 225-3S-06 St. Paul, MN 55144-1000 800-362-3550 • 877-369-2923 (Fax) www.3M.com/structuraladhesives 3M and Scotch-Weld are trademarks of 3M Company. ©3M 2011 -7-