DP8810NS-GREEN-490ML

Scotch-Weld™ Low Odor Acrylic Adhesives DP8805NS Green • DP8810NS Green • DP8825NS Green Technical Data Sheet Product Description May 2019 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives are high performance, twopart acrylic adhesives that offer excellent shear, peel, and impact performance. These toughened products provide improved adhesion to many plastics and metals, including those with slightly oily surfaces. These durable products feature a fast rate of strength build, providing structural strength in minutes. Their low odor and non-flammability feature also makes them easier to incorporate into a manufacturing process. Review UL File QOQW2. MH17478 and Sign Components Manual (SAM) File E464624 for certification of these adhesive systems in electrical equipment. DP8810NS Green has been tested for surface flammability, smoke, toxic gas generation, and caloric content per ASTM E162, ASTM E662, ASTM E1354, Bombardier SMP 800-C, and Boeing BSS 7239 test methods. DP8805NS Green and DP8825NS Green should yield similar results. Product Features • • • • Toughened Excellent shear strength High peel and impact strength 10:1 mix ratio • Variety of open times available • Increased cure speed with applied heat • Contain glass beads (0.010" diameter) to control bond line thickness Note: Unless otherwise indicated, all properties measured at 72°F (22°C). Typical Uncured Physical Properties Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP8805NS Green DP8810NS Green DP8825NS Green Base (B) Off-White Color Accelerator (A) Blue 1 Base (B) 45,000 cP 45,000 cP 40,000 cP Viscosity Accelerator (A) 15,000 cP 15,000 cP 15,000 cP 3 3 3 2 Base (B) 1.06 g/cm 1.06 g/cm 1.12 g/cm Density 3 3 3 Accelerator (A) 1.08 g/cm 1.08 g/cm 1.08 g/cm By volume 10 Parts B : 1 Part A Mix ratio By weight 10 Parts B : 1 Part A Note: Cure times are approximate and depend on adhesive temperature. Property Work life 3 4 Open time 5 Time to handling strength 6 Time to structural strength 3–5 minutes 8–12 minutes 22–24 minutes 4–6 minutes 6–8 minutes 8–10 minutes 8–12 minutes 16–20 minutes 19–23 minutes 20–22 minutes 42–46 minutes 50–56 minutes Page 1 of 7 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP8805NS Green • DP8810NS Green • DP8825NS Green 1. Viscosity measured using cone-and-plate viscometer; reported viscosity at 3.8 sec-1 shear rate. 2. Density measured using pycnometer. 3. Maximum time that adhesive can remain in a static mixing nozzle and still be expelled without undue force on the applicator. 4. Maximum time allowed after applying a small amount of adhesive to one substrate before bond must be closed and fixed in place. 5. Minimum time required to achieve 50 psi of overlap shear strength. 6. Minimum time required to achieve 1,000 psi of overlap shear strength. Typical Mixed Physical Properties Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Property Typical Cured Physical Properties 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP8805NS Green DP8810NS Green Color Blue-Green Full cure time 24 hours DP8825NS Green Viscosity 45,000 cP 45,000 cP 40,000 cP Density 1.06 g/cm 1.06 g/cm 1.12 g/cm3 3 3 Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Overlap Shear (psi)7 Substrate 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP8805NS Green DP8810NS Green DP8825NS Green Aluminum 3,900 CF 3,600 CF 3,100 CF Stainless steel 3,500 CF 3,400 CF 2,700 CF PVC 2,000 SF 1,800 SF 1,400 SF ABS 1,200 SF 1,200 SF 1,300 SF Acrylic 1,100 SF 1,100 SF 1,000 SF Polycarbonate 800 AF 1,000 CF 900 CF Polystyrene 400 AF 550 AF 550 AF Polyester (fiber-reinforced) 650 AF 1,000 AF 900 AF 3,300 CF 3,400 CF 2,700 CF Epoxy resin (fiber-reinforced) Aluminum (tested at -40°F) 800 AF 900 AF 1,000 AF Aluminum (tested at 180°F) 900 CF 900 CF 700 CF 7. Overlap shear values measured using ASTM D1002; 1 min open time; adhesive allowed to cure for 24 hours at room temperature; 1/2" overlap; 0.010" bond line thickness; samples pulled at 0.1 in/min for metals and 2 in/min for plastics; all surfaces prepared with light abrasion and solvent clean; substrates used were 1/16" thick metals and 1/8" thick plastics; failure modes: AF: adhesive failure CF: cohesive failure SF: substrate failure Note: Environmental aging tests have shown that these adhesives may accelerate the corrosion of certain bare metals (such as cold rolled steel, copper, brass, and bronze), leading to low bond strength values and early bond failure. These adhesives also have relatively low adhesion to low surface energy plastics (such as polypropylene, polyethylene, TPO, and PTFE). Applications involving any of these materials should be carefully evaluated by the end user for suitability. Note: The presence of oxygen inhibits the cure of acrylic structural adhesives. Therefore, any exposed surfaces of the mixed adhesive will cure much more slowly than adhesive contained within the bond line. With methyl methacrylate (MMA) acrylic adhesives, any uncured adhesive on the surface flashes off immediately, leaving a surface that feels dry to the touch. With these low odor acrylic adhesives, uncured adhesive on exposed surfaces does not evaporate away quickly, leaving a wet film of partially cured material. For manufacturing processes that need a dry surface quickly, such as for subsequent sanding or painting operations, consider instead the standard acrylic adhesives (DP8405NS Green, DP8410NS Green, DP8425NS Green, and Metal Bonder DP8407NS Green). Page 2 of 7 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP8805NS Green • DP8810NS Green • DP8825NS Green Typical Cured Physical Properties (continued) Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Mechanical Properties8 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive Property DP8805NS Green DP8810NS Green DP8825NS Green Tensile modulus (psi) 140,000 125,000 Not tested Tensile strength (psi) 1,800 1,650 Not tested Tensile strain at break (%) 8.5 6.5 Not tested 8. Tensile properties measured using ASTM D638; adhesives allowed to cure for 2 weeks at room temperature; 1/8" thick Type I test specimens; samples pulled at 0.2 in/min. Environmental Resistance9 Condition Substrate 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP8805NS Green DP8810NS Green DP8825NS Green 300°F (149°C) 100% 100% 100% -40°F (-40°C) 100% 95% 95% 120°F (49°C) + 80% relative humidity 70% 65% 75% 150°F (66°C) + 80% relative humidity 65% 70% 70% 185°F (85°C) + 85% relative humidity 50% 50% 30% Water 70% 75% 60% 55% 55% 45% 120°F (49°C) Water 35% 35% 35% Salt water (5 wt% in water) 75% 75% 75% Diesel fuel 95% 90% 95% Motor oil 100% 95% 100% Antifreeze (50 wt% in water) 85% 90% 95% Isopropyl alcohol 60% 50% 65% Bleach (10 wt% in water) 65% 65% 75% 90°F (32°C) Water Aluminum Page 3 of 7 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP8805NS Green • DP8810NS Green • DP8825NS Green Typical Cured Physical Properties (continued) Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Condition Substrate 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP8805NS Green DP8810NS Green DP8825NS Green -40°F (-40°C) 100% 100% 85% 120°F (49°C) + 80% relative humidity 100% 95% 90% 150°F (66°C) + 80% relative humidity 100% 100% 90% 95% 100% 85% Water 100% 100% 100% Salt water (5 wt% in water) 100% 100% 100% Hydrochloric acid (16 wt% in water) 100% 95% 100% Sodium hydroxide (10 wt% in water) 90% 95% 65% 185°F (85°C) + 85% relative humidity PVC 9. Values indicate overlap shear test performance retained after 1,000 hours of continuous exposure relative to a control sample left at room temperature; samples conditioned for 24 hours at room temperature and 50% relative humidity prior to tests. Note: Fully-cured structural adhesives can withstand short-term incidental contact with almost any solvent, chemical, or environmental condition. However, long-term continuous exposure of these Acrylic Adhesives to the following liquids should be avoided: 1. Elevated temperature (>100°F) water 2. Ketone-type solvents (acetone, MEK) 3. Gasoline and similar liquids Floating Roller Peel (lb/inch width)10 Substrate Aluminum 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP8805NS Green DP8810NS Green DP8825NS Green 25 CF 35 CF 30 CF 10. Floating roller peel values measured using ASTM D3167; adhesives allowed to cure for 24 hours at room temperature; 1" wide samples; 0.017" bond line thickness; samples pulled at 6 in/min; aluminum surfaces etched; substrates used were 1/16" thick and 0.020" thick aluminum; failure modes: AF: adhesive failure CF: cohesive failure SF: substrate failure Note: The data in this sheet were generated using the 3M™ EPX Applicator System equipped with an EPX static mixer, according to manufacturer’s directions. Thorough hand-mixing will afford comparable results. Page 4 of 7 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP8805NS Green • DP8810NS Green • DP8825NS Green Directions for Use 1. To obtain the highest strength structural bonds, paint, oxide films, oils, dust, mold release agents, and all other surface contaminants must be completely removed. The amount of surface preparation depends on the required bond strength and environmental aging resistance desired by user. For suggested surface preparations on common substrates, see the section on surface preparation. 2. Mixing For Duo-Pak Cartridges Store cartridges with cap end up to allow any air bubbles to rise towards the tip. To use, simply insert the cartridge into the EPX applicator and start the plunger into the cylinders using light pressure on the trigger. Then remove the cap and expel a small amount of adhesive to ensure material flows freely from both sides of cartridge. For automatic mixing, attach an EPX mixing nozzle to the cartridge and begin dispensing the adhesive. For hand mixing, expel the desired amount of adhesive and mix thoroughly. Mix approximately 15 seconds after obtaining a uniform color. Mixing For Bulk Containers Mix thoroughly by weight or volume in the proportion specified on the product label or in the typical uncured properties section. Mix approximately 15 seconds after obtaining a uniform color. 3. Apply adhesive and join surfaces within the open time listed for the specific product. Larger quantities and/or higher temperatures will reduce this working time. 4. The adhesive and all materials should be at 60°F (16°C) or above prior to assembly. Allow adhesive to cure at 60°F (16°C) or above until completely firm. Applying heat up to 150°F (66°C) will increase cure speed. 5. Keep parts from moving during cure. Apply contact pressure or fixture in place if necessary. Optimum bond line thickness ranges from 0.005 to 0.020 inch; shear strength will be maximized with thinner bond lines, while peel strength reaches a maximum with thicker bond lines. 6. Excess uncured adhesive can be cleaned up with ketone-type solvents.* *Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow the manufacturer’s precautions and directions for use. Page 5 of 7 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP8805NS Green • DP8810NS Green • DP8825NS Green Surface Preparation 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives are designed to be used on painted or coated metals, most plastics, and some bare metals. The following cleaning methods are suggested for common surfaces: Painted/coated metals: 1. Wipe surface free of dust and dirt with clean cloth and pure isopropyl alcohol.* 2. Sandblast or lightly abrade using clean fine grit abrasives. Do not completely remove the paint layer or coating down to bare steel. 3. Wipe again with clean cloth and pure isopropyl alcohol to remove loose particles.* Aluminum/stainless steel: 1. Wipe surface free of dust and dirt with clean cloth and pure acetone.* 2. Sandblast or lightly abrade using clean fine grit abrasives. 3. Wipe again with clean cloth and pure acetone to remove loose particles.* Plastics: 1. Wipe surface free of dust and dirt with clean cloth and pure isopropyl alcohol.* 2. Lightly abrade using fine grit abrasives. 3. Wipe again with clean cloth and pure isopropyl alcohol to remove loose particles.* *Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow the manufacturer’s precautions and directions for use. Page 6 of 7 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives DP8805NS Green • DP8810NS Green • DP8825NS Green Storage Store product at 80°F (27°C) or below. Refrigeration at 40°F (4°C) will help extend shelf life. Do not freeze. Allow product to reach room temperature prior to use. Shelf Life 3M™ Scotch-Weld™ DP8805NS, DP8810NS and DP8825NS Low Odor Acrylic Adhesives in Duo-Pak cartridges and 1 and 5 gallon pails have a shelf life of 24 months from date of manufacture in unopened original containers kept at recommended storage conditions. 55 gallon drums have a shelf life of 12 months from date of manufacture in unopened original containers kept at recommended storage conditions. Precautionary Information Refer to Product Label and Material Safety Data Sheet for health and safety information before using this product. For additional health and safety information, call 1-800-364-3577 or (651) 737-6501. Technical Information The technical information, guidance, and other statements contained in this document or otherwise provided by 3M are based upon records, tests, or experience that 3M believes to be reliable, but the accuracy, completeness, and representative nature of such information is not guaranteed. Such information is intended for people with knowledge and technical skills sufficient to assess and apply their own informed judgment to the information. No license under any 3M or third party intellectual property rights is granted or implied with this information. Product Selection and Use Many factors beyond 3M’s control and uniquely within user’s knowledge and control can affect the use and performance of a 3M product in a particular application. As a result, customer is solely responsible for evaluating the product and determining whether it is appropriate and suitable for customer’s application, including conducting a workplace hazard assessment and reviewing all applicable regulations and standards (e.g., OSHA, ANSI, etc.). Failure to properly evaluate, select, and use a 3M product and appropriate safety products, or to meet all applicable safety regulations, may result in injury, sickness, death, and/or harm to property. Warranty, Limited Remedy and Disclaimer Unless a different warranty is specifically stated on the applicable 3M product packaging or product literature (in which case such warranty governs), 3M warrants that each 3M product meets the applicable 3M product specification at the time 3M ships the product. 3M MAKES NO OTHER WARRANTIES OR CONDITIONS, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO, ANY IMPLIED WARRANTY OR CONDITION OF MERCHANTABILITY, FITNESS FOR A PARTICULAR PURPOSE, OR ARISING OUT OF A COURSE OF DEALING, CUSTOM, OR USAGE OF TRADE. If a 3M product does not conform to this warranty, then the sole and exclusive remedy is, at 3M’s option, replacement of the 3M product or refund of the purchase price. Limitation of Liability Except for the limited remedy stated above, and except to the extent prohibited by law, 3M will not be liable for any loss or damage arising from or related to the 3M product, whether direct, indirect, special, incidental, or consequential (including, but not limited to, lost profits or business opportunity), regardless of the legal or equitable theory asserted, including, but not limited to, warranty, contract, negligence, or strict liability. ISO 9001 This Industrial Adhesives and Tapes Division product was manufactured under a 3M quality system registered to ISO 9001 standards. Industrial Adhesives and Tapes Division 3M Center, Building 225-3S-06 St. Paul, MN 55144-1000 Phone 800-362-3550 Fax 877-369-2923 Web 3M.com/StructuralAcrylics 3M and Scotch-Weld are trademarks of 3M Company. © 3M 2016. All rights reserved. Page 7 of 7