22759/35-26-6

SCD SPECIFICATION CONTROL DRAWING 55A0814 Date Revision WIRE, RADIATION-CROSSLINKED, MODIFIED ETFE-INSULATED, 1-12-17 NORMAL WEIGHT, GENERAL PURPOSE, 600 VOLT This specification sheet forms a part of the latest issue of Raychem Specification 55A. Title N PRIMARY INSULATION - RADIATION-CROSSLINKED, MODIFIED ETFE Primary insulation shall be of a contrasting pigmentation to that of the jacket. CONDUCTOR - SILVER-COATED HIGH-STRENGTH COPPER ALLOY JACKET - RADIATION-CROSSLINKED, MODIFIED ETFE TABLE I. CONSTRUCTION DETAILS PART NUMBER 1/ WIRE SIZE (AWG) DIAMETER OF STRANDED CONDUCTOR (inch) CONDUCTOR STRANDING (number x AWG) FINISHED WIRE MINIMUM MAXIMUM MAXIMUM RESISTANCE AT 20°C (ohms/1000 ft.) DIAMETER (inch) MAXIMUM WEIGHT (lbs/1000 ft.) 55A0814-26-* 26 19 x 38 .018 .020 44.8 .040 ± .002 1.70 55A0814-24-* 24 19 x 36 .023 .024 28.4 .045 ± .002 2.30 55A0814-22-* 22 19 x 34 .029 .031 17.5 .050 ± .002 3.30 55A0814-20-* 20 19 x 32 .037 .039 10.7 .058 ± .002 4.80 55A0814-18-* 18 19 x 30 .046 .050 6.8 .070 ± .003 7.50 TABLE II. PERFORMANCE DETAILS PART NUMBER 1/ MANDREL DIAMETER (inch) (± 3%) LIFE CYCLE, IMMERSION, AND ACCELERATED AGING WEIGHT (lb) (± 3%) COLD BEND LIFE CYCLE, IMMERSION, AND ACCELERATED AGING COLD BEND 55A0814-26-* .375 1.00 .500 3.00 55A0814-24-* .500 1.00 .750 3.00 55A0814-22-* .500 1.00 1.00 3.00 55A0814-20-* .500 1.00 1.50 4.00 55A0814-18-* .750 1.50 2.00 4.00 Users should evaluate the suitability of this product for their application. Specifications are subject to change without notice. Tyco Electronics Corporation also reserves the right to make changes in materials or processing, which do not affect compliance with any specification, without notification to Buyer. 1/ COLORS AND COLOR CODE DESIGNATORS SHALL BE IN ACCORDANCE WITH MIL-STD-681. OTHER CODES AND SUFFIXES MAY BE ADDED TO THE PART NUMBER, AS NECESSARY, TO CAPTURE ANY ADDITIONAL REQUIREMENTS IMPOSED BY THE PURCHASE ORDER. Raychem, TE Connectivity, TE Connectivity (logo), and TE (logo) are trademarks. Page 1 of 2 DIMENSIONS ARE IN INCHES AND, UNLESS OTHERWISE DESIGNATED, ARE NOMINAL. THIS SPECIFICATION SHEET TAKES PRECEDENCE OVER DOCUMENTS REFERENCED HEREIN. REFERENCED DOCUMENTS SHALL BE OF THE ISSUE IN EFFECT ON DATE OF INVITATION FOR BID. Raychem Wire & Cable 501 Oakside Avenue Redwood City, CA 94063-3800 Phone: 1-800-522-6752 Fax: 1-650-361-6297 © 2008-2017 Tyco Electronics Corporation. All rights reserved. Page SPECIFICATION CONTROL DRAWING 2 of 2 Revision SCD N 55A0814 WIRE RATINGS AND ADDITIONAL REQUIREMENTS TEMPERATURE RATING: 200°C Maximum continuous conductor temperature VOLTAGE RATING: 600 volts (rms) at sea level ACCELERATED AGING (CROSSLINKING PROOF): 300 ± 3°C for 7 hours BLOCKING: 230 ± 3°C for 24 hours COLOR: White preferred CONCENTRICITY: 70% (minimum) FLAMMABILITY: Procedure 1, 3 seconds (maximum), 3 inches (maximum); no flaming of facial tissue HUMIDITY RESISTANCE: Insulation Resistance, 5000 megohms for 1000 ft. (minimum) IDENTIFICATION, COLOR STRIPING, AND BAND DURABILITY: 125 cycles (250 strokes) (minimum), 500 g weight IMMERSION: Diameter increase 5% (maximum); no cracking, no dielectric breakdown INSULATION ELONGATION AND TENSILE STRENGTH: Elongation, 125% (minimum) for primary insulation 75% (minimum) for total insulation (primary insulation & jacket) Tensile Strength, 5000 lbf/in2 (minimum) for primary insulation 5000 lbf/in2 (minimum) for total insulation (primary insulation & jacket) INSULATION FLAWS: Primary Insulation, Spark Test, 1.5 kV (rms) at 60 Hz; 4.2 kV (rms) at 3 kHz Impulse Dielectric Test, 6.0 kV (peak) Finished Wire, Spark Test, 5.7 kV (rms) at 3 kHz Impulse Dielectric Test, 8.0 kV (peak) INSULATION RESISTANCE: 5000 megohms for 1000 ft. (minimum) INSULATION THICKNESS: 0.003 in. (minimum) for primary insulation 0.004 in. (minimum) for outer jacket 0.009 in. (minimum) for total insulation LIFE CYCLE: 230 ± 3°C for 500 hours LOW TEMPERATURE-COLD BEND: -65 ± 3°C for 4 hours SHRINKAGE: 230 ± 3°C for 6 hours, 0.125 in. (maximum) in 12 inches SMOKE TEST: 250 ± 5°C, no visible smoke SOLDERABILITY: Per MIL-STD-202, Method 208, except without steam aging SURFACE RESISTANCE: 500 meghoms-in. (minimum), both readings THERMAL SHOCK RESISTANCE: 200 ± 3°C, 0.060 in. (maximum) VOLTAGE WITHSTAND (Post Environmental): 2500 volts (rms), 60 Hz WICKING: 2.25 in. (maximum) WRAP TEST: 313 ± 3°C for 2 hours 1/ PART NUMBER: The "*" in the part numbers in Tables I and II shall be replaced by a color code designator. Example: AWG 22, white: 55A0814-22-9 AWG 22, white with a black stripe: 55A0814-22-90 1/ See footer section on page 1