184MLR100K

MLR Epoxy Dipped Radial Lead Metallized Polyphenylene Sulphide Film Capacitors • • • Temperature stable High temperature RoHS compliant -40°C to +125°C ±10% at 1kHz, 20°C 100 For T> +105°C the applied voltage must be decreased by 1.5% per °C Freq. (kHz) 1 100 .1% .3% 15000MΩ Minimum, 100VDC applied for 60 seconds 1,000 hours at 125% of rated VDC and at 105°C Capacitance Change ≤5% of initial measured value ≤200% of maximum specified value >50%of mimimum specified value • Automotive • Audio • Polycarbonate alternative Operating Temperature Range Capacitance Tolerance Rated Voltage Dissipation Factor (max) at 20°C Insulation Resistance VDC Load Life Test Dissipation Factor Insulation Resistance 500 hours at 40°C ±2°C with 90-95% relative humidity and 100% of rated WVDC Damp Heat Test Capacitance Change Dissipation Factor Insulation Resistance ≤5% change from initial value. ≤0.005 at 1kHz and 25°C >33%of minimum specification ≤1 nH/mm along the capacitor pitch and lead wire length. 150% of rated WVDC applied between the terminals for 60 seconds Self-inductance Dielectric Strength Capacitance Drift Factor Temperature Coefficient Dielectric Electrodes Construction Leads Coating 200% of rated WVDC applied to the terminals and the case for 1 to 5 seconds ≤1.0% up to 40°C after 2 years 0 ppm/°C, ± 100ppm/°C Polyphenylene sulphide Vacuum deposited metal layers Wound Metalized film Lead free Tinned copper wire Flame retardant epoxy sealed resin (UL 94V-O) Capacitance (µF) 0.1 0.12 0.15 0.18 0.22 0.27 0.3 0.33 0.36 WVDC PART NUMBER 104MLR100K 124MLR100K 154MLR100K 184MLR100K 224MLR100K 274MLR100K 304MLR100K 334MLR100K 364MLR100K dv/dt (v/µs) Maximum RMS current 1kHz,20°C. LxHxT (mm) S (mm) d (mm) L max T max H max G 100 100 100 100 100 100 100 100 100 15 15 15 15 15 15 15 15 15 0.18 0.16 0.12 0.1 0.09 0.072 0.06 0.05 0.04 13x9x5.5 13x9.5x6 13x9.5x6 13x10x6 13x10x6 13x11x7 13x12x7.5 13x12x8 13x12x8 8.0 8.0 8.0 8.0 8.0 8.0 8.0 9.0 9.0 0.6 0.6 0.6 0.6 0.6 0.6 0.6 0.6 0.6 15 min. d S±1.5 ® 3757 W. Touhy Ave., Lincolnwood, IL 60712 • (847) 675-1760 • Fax (847) 673-2850 • www.illcap.com 1 MLR Epoxy dipped Radial lead Metallized Polphenylene Sulphide Film Capacitors Enviromental and frequency characterisitc graphs Temperature vs Capacitance Capacity Change (%) Temperature vs tanδ 5 4 3 2 1 0 -1 -2 -3 -4 -5 -40 -30 -20 -10 0 10 20 30 40 50 60 70 80 90 100 110 120 130 (°C) Temperature Dissipation Factor (tanδ) vs Frequency. Frequency Character 0.5 0.4 0.3 0.2 0 -0.1 -0.2 -0.3 -0.4 -0.5 -0.6 -0.7 -0.8 -0.9 -1.0 Capacity Change (%) 1.0 Dissiapation Factor (%) 0.1 0.1 103 2 5 104 2 45 105 2 5 106 103 2 5 104 2 5 105 2 5 106 0.01 Frequency (Hz) ® 3757 W. Touhy Ave., Lincolnwood, IL 60712 • (847) 675-1760 • Fax (847) 673-2850 • www.illcap.com