22-1X36YD

Scotch® Vinyl Electrical Tape 22 Data Sheet Product Description June 2022 Scotch® Vinyl Electrical Tape 22 is a black, professional grade, 10-mil (0.254 mm) thick electrical insulating tape composed of an elastic vinyl (PVC) film backing coated on one side with a noncorrosive, rubber-based pressure-sensitive adhesive.  Commonly used in these types of applications:  UL510: As primary insulation on applications up to 600V at max temperature of 80°C (176°F) on joints and splices in wires and cables in accordance with NFPA 70, National Electrical Code  CSA C22.2 No.197: As primary insulation on applications up to 1000V at max temperature of 80°C (176°F) and a min temperature of -7°C (19°F) on joints and splices in wires and cables in accordance with Canadian Electrical Code, Part 1  IEC 60454-3-1: Classification Type 2, Designation IEC 60454-3-1-2/F-PVCP/60 for thermal index of 60°C (140°F) and min temperature rating of -10°C (14°F)  Residential, commercial and industrial environments.  Where Flame Retardant rating is required – UL510  Cable jacket repair (up to 600V (UL) / 1000V (CSA) as primary insulation) and as mechanical protection when overwrapping rubber splicing, and mastic tapes used on LV/MV/HV joints and splices  Critical indoor and outdoor operations as determined by end-user where use of a general use vinyl electrical tape is not recommended  Where compatibility with most solid dielectric cable insulations, rubber and synthetic splicing compounds is required  Where reducing moisture ingress is needed, best results achieved when used as an overwrap in combination with a rubber splicing or mastic tape product.  For harnessing and bundling of wires and cable for faster build-up  Country of Origin: USA Properties Physical Properties Color – Visual Adhesive Backing Mechanical Properties Thickness3 Black Adhesion to Steel3 - Minimum 73° F (23°C) Rubber-based Adhesion to Backing3 - Minimum 73°F (23°C) Vinyl (PVC) Flame Retardant UL510 Temperature Rating UL5101- Maximum CSA - C22.2 No. 1972 IEC 60454-3-1 - Type 2 Electrical Properties Voltage Rating - Maximum UL5101 / CSA C22.2 No. 1972 Dielectric Strength3 - Minimum Standard Condition V/mil High Humidity Insulation Resistance3 - Minimum (High Humidity) Notes: 1. 2. 3. 4. Value Imperial (Metric) Tensile Strength3,4 – Minimum Pass 176°F (80°C) 19°F to 176°F (-7°C to 80°C) 14°F to 140°F (-10°C to 60°C) Value Imperial (Metric) Elongation3 - Minimum 73°F (23°C) 600 V / 1000 V 1000 V/mil (39.4 kV/mm) 90% of std. 1x1012 ohms In accordance with NFPA 70, National Electrical Code In accordance with CSA C22.1, Canadian Electrical Code, Part 1 ASTM D1000 Test Method - properties measured at room temperature 73°F (23°C) unless otherwise stated Tensile Strength “lb/in (N/cm)” values for reference only, based on nominal tape thickness of 10 mils 1 of 3 Value Imperial (Metric) 10 mils +/- 1 (0.254 +/- 0.025 mm) 18 oz/in (2.0 N/cm) 18 oz/in (2.0 N/cm) 2400 psi / 24 lb/in (42 N/cm) 150% Scotch® Vinyl Electrical Tape 22 Agency Approvals & Self Certifications     UL Listed: UL510 Standard “Insulating Tape”, Category OANZ, File No. E129200 CSA Listed: CSA-C22.2 No.197 “PVC Insulating Tape”, File No. 048769, Class 9052-02 VDE Marks License no. 130462 for Type 2: IEC 60454-3-1-2/F-PVCP/60 3M Test report RPT-839539 available to UL510 Standard testing  For Regulatory information including RoHS, REACH, please visit www.3M.com/regs Installation Techniques Scotch® Vinyl Electrical Tape 22 shall be applied in half-lapped layers with sufficient tension to produce a uniform wind (for most applications this tension will reduce the tape width to approximately 5/8 of original width). On pigtail splices, the tape shall be wrapped beyond the end of the wires and then folded back, leaving a protective cushion to resist cut-through. Wrap tape up-hill, taping from a smaller diameter surface to a larger diameter surface. Apply the tape with no tension on the last wrap to help prevent flagging. Shelf Life & Storage This product has a 5-year shelf life (from date of manufacture) when stored in humiditycontrolled storage (50°F/10°C to 80°F/27°C and