4-5-LSE-160WF

3M™ VHB™ Tape LSE Series Product Data Sheet October 2019 Supersedes: August 2019 3M™ VHB™ Tape LSE Series is a white, conformable, double-coated acrylic foam tape with a high initial tack and a soft foam. Its design enables bonding of many low surface energy substrates/materials. 3M VHB Tape LSE is a white tape available in three different thicknesses with a 3M branded red siliconised polyethylene film liner. Product Description • • • Key Features • • • • • Applications & Benefits • Double-coated acrylic foam tape 100% closed-cell acrylic foam Multi material bonding for high, medium or low surface energy substrates including many metals (e.g. stainless steel). composites and plastics (e.g. PP, PA) Enables bonding of many LSE substrates without primer Good low temperature tack Soft foam enables stress relaxation & an easy application High initial tack For indoor and outdoor applications Capability to bond to many LSE substrates without primer makes it a good fit for applications in many industries such as plastics processing, transportation, appliances and signage Physical Properties LSE-060WF Adhesive & Carrier LSE-110WF LSE-160WF Modified Acrylic on Conformable Acrylic Foam (closed-cell) Thickness acc. to ASTM D-3652 0.60 mm Density 1.10 mm 1.60 mm 715 kg/m³ Release Liner 3M branded red siliconised polyethylene film Tape Colour White Page 1 of 3 3M™ VHB™ LSE Series October 2019 Performance Characteristics Type LSE-060WF LSE-110WF LSE-160WF 30 N/cm 44 N/cm 54 N/cm 24 N/cm 42 N/cm 51 N/cm 29 N/cm 43 N/cm 51 N/cm 24 N/cm 40 N/cm 47 N/cm 90 ° Peel adhesion to Stainless Steel acc. to ASTM D3330, 90° peel angle @ RT, after 72h @ RT dwell 90 ° Peel adhesion to Polypropylene acc. to ASTM D3330, 90° peel angle @ RT, after 72h @ RT dwell 90 ° Peel adhesion to Glass acc. to ASTM D3330, 90° peel angle @ RT, after 72h @ RT dwell 90 ° Peel adhesion to ABS acc. to ASTM D3330, 90° peel angle @ RT, after 72h @ RT dwell Static Shear Strength on Stainless Steel 23 °C - 1000 g 70 °C – 550 g 90 °C – 250 g acc. to ASTM D3654, after 72h @ RT dwell (Weight held for 10.000 minutes, 3.22cm² (0.5in²), vertical test direction Static Shear Strength on Polypropylene 23 ° C - 1000 g 70 °C – 500 g 90 ° C - 500 g acc. to ASTM D3654, after 72h @ RT dwell (Weight held for 10.000 minutes, 3.22cm² (0.5in²), vertical test direction Limited by substrate Dynamic Shear acc. to ASTM D1002 on stainless steel, after 72h @ RT dwell 525 N /6.54cm² 382 N /6.54cm² 347 N /6.54cm² 365 N /6.54cm² 309 N /6.54cm² 290 N /6.54cm² Normal Tensile (T-Block) acc. to ASTM D897 to Aluminium @ RT, after 72h @ RT dwell, test speed 50 mm/min Temperature Performance Application Temperature Short term (minutes, hours): 150 °C Long term (days, weeks): 90 °C Ideal application temperature range 10 °C to 38 °C. For certain applications and substrates 3M™ VHB™ Tape LSE can be applied at temperatures as low as 0 °C if the surface is frost free. Testing on application-specific substrates is recommended to confirm adhesion at temperatures