Technical Data | August 2016
3M™ Low Static Polyimide Film Tape 5433 (Linered)
Product Description
3M™ Low Static Polyimide Film Tape 5433 is a clear PET linered version of 3M™ Low Static Polyimide Film Tape 5419.
It is a translucent, polyimide film-backed amber silicone adhesive tape with extremely low electrostatic discharge
properties.
Key Features
•
•
•
•
•
Polyimide film does not soften at elevated temperatures, thus the film provides an excellent release surface at
elevated temperatures
Dimensionally stable at high temperatures to help prevent rework and enable high productivity
Flame retardant, chemical and radiation resistant to help protect surfaces and reduce replacement costs
Silicone adhesive's high temperature performance reduces adhesive transfer to help eliminate cleaning,
enabling high productivity
Halogen Free*
*Halogen Free is defined as having maximum 900ppm bromine, maximum 900ppm chlorine, and maximum 1500ppm total bromine
and chlorine, per 61429-2-21
Key Attributes
3M™ Low Static Polyimide Film Tape 5433 (Linered)
Features
Advantages
Polyimide film
Silicone adhesive
Low static
Unique release liner
Dimensionally stable at high temperatures
Flame retardant and chemical resistant
High temperature performance reduces
adhesive transfer
Virtually eliminates circuit board
degradation due to electrostatic discharge
Easy release from silicone adhesive
Benefits
Helps promote high productivity
Protects surfaces, helping reduce replacement
Helps promote high productivity
Helps reduce costly board waste due to
component failure
Capability to product die cut parts
Product Construction/Material Description
Note: The following technical information and data should be considered representative or typical only and should not be used for
specification purposes.
3M™ Low Static Polyimide Film Tape 5433 (Linered)
Property
Value
Backing Material
Adhesive Type
Tape Color
Liner
Product Form
Standard Roll Length
Polymide
Silicone
Amber
Clear PET
Roll
36 yards (33 meters)
Applications
•
•
Mask for printed circuit boards during wave solder or solder dip process
Used as release surface in fabrication of parts cured at elevated temperatures
3M™ Low Static Polyimide Film Tape 5433 (Linered)
Typical Physical Properties and Performance Characteristics
Note: The following technical information and data should be considered representative or typical only and should not be used for
specification purposes. Final product specifications and testing methods will be outlined in the products Certificate of Analysis
(COA) that is shipped with the commercialized product.
3M™ Low Static Polyimide Film Tape 5433 (Linered)
Property
Method*
Adhesion to Steel
Tensile Strength at Break
D-3330
D-3759
Elongation at Break
Backing Thickness
Liner Thickness
Total Tape Thickness
Temperature Use Range
Dielectric Strength
Insulation Resistance
Static Charge
D-3759
D-3652
D-3652
D-3652
D-149
-
Removal from Liner
Removal from PWB
-
Outgassing
Flame Retardancy
E-595
per UL-510 product category:
OANZ2 File E230409
Value
20 oz./in. width (22 N/100 mm)
33 lbs./in. width (578 N/100 mm)
60%
1 mil (0.03 mm)
3 mil (0.08 mm)
2.7 mil (0.07 mm)
-73° to 260°C) -100° to 500°F
7000 volts
>1*106 ohms
(measured at 50% RH, 70°F (21°C) in an ESD
controlled environment)