Product Description
Finite Element Analysis (FEA) data is available for this product at: 3m.com/FEA
3M™ VHB™ Adhesive Transfer Tape F9469PC utilizes the 3M™ High Performance Acrylic Adhesive 100MP,
which has excellent long term holding power with much higher adhesion strength than typical pressure
sensitive adhesive systems. This 3M™ VHB™ Adhesive Transfer Tape is transparent and is ideal for use in
many interior and exterior industrial applications to replace rivets, spot welds, liquid adhesives, and other
permanent fasteners.
3M™ VHB™ Adhesive Transfer Tape F9469PC
Technical Information Note
The following technical information and data should be considered representative or typical only and should not be used for speci cation purposes.
Typical Physical Properties
Property
Values
Notes
Adhesive Thickness
0.13 mm
5.2 mil
Density
1.012 g/cm³
0.04 lb/in³
Liner
58# Polycoated Kraft
Liner Thickness
0.106 mm
The thickness listed is based on a calculation
from manufacturing controlled adhesive coat
weights using a density of 1.012 g/cc. While
past data pages have listed nominal
thicknesses, the coat weight (and theoretical
caliper) has not changed.
4.2 mil
UL Listing
3M™ Adhesive 100MP has UL 746C listings with di erent temperature ratings on many commonly used substrate materials as indicated in the table below.
Quali cation for this listing requires high strength retention after extended exposure to high temperatures, humidity, cold, and cyclic conditions.
Substrates Temperature Rating
Stainless Steel, Glass/Epoxy, Enameled Steel, Ceramic, Phenolic, Nickel Plated Steel: 110°C
ABS, Polycarbonate, Aluminum, Galvanized Steel: 90°C
Unplasticized PVC: 75°C
Our testing has shown that 3M™ Adhesive 100MP yielded 92% retention of peel adhesion after the roll was aged for more than 5 years at an elevated temperature of
150°F (65°C). The initial tack and liner release properties were still excellent. This testing result suggests that the tape is relatively una ected by long-term exposure to
elevated temperatures. Bonds made with 3M™ Adhesive 100MP can tolerate periodic short-term exposures to temperatures up to 500°F (260°C).
3M™ Adhesive 100MP is thermoplastic in nature, becoming softer as temperature increases and rmer as temperature decreases. As the adhesive becomes rmer, the
performance generally increases. This performance increase is demonstrated graphically in Figure 1 for 3M™ VHB™ Adhesive Transfer Tape F9473PC. It shows the
breakaway and peel forces as a function of temperature. The exception of the performance increase is at very low temperatures when high impact stresses along with
high frequencies are encountered. At low temperatures, the tape becomes very rm and glassy; the ability to absorb impact energy is reduced.
3M™ VHB™ Adhesive Transfer Tape F9469PC
Dynamic Mechanical Properties
For engineers who have to use adhesive properties for modeling and analysis purpose, we suggest a Young’s modulus of 4.5 × 102 kPA (measured at 23°C & 1 Hz) and
a Poisson’s ratio of 0.499. For detailed adhesive modulus and damping properties, please refer to the nomograph for 3M™ VHB™ Adhesive Transfer Tapes, which is
available upon request through our technical service group. The nomograph presents adhesive modulus and damping properties as functions of temperature and
frequency.
Typical Performance Characteristics
Additional Test notes
3M™ VHB™ Adhesive Transfer Tapes F9460PC, F9469PC, and F9473PC are made from the same adhesive system and are thermoplastic in nature, becoming softer
as temperature increases and rmer as temperature decreases. As the adhesive becomes rmer, the adhesion performance generally increases. At low temperatures
(lower than -40°F [-40°C]), the 3M™ VHB™ Adhesive Transfer Tape becomes very rm and glassy; the ability to absorb impact energy is reduced. In contrast,
adhesion strength reduces with increasing temperatures. Typical adhesive strength properties at room temperatures are shown below.
Solvent Resistance
No apparent degradation when exposed to splash testing of many common solvents and uids including gasoline, JP-4 fuel, mineral spirits, motor oil, ammonia
cleaner, acetone and methyl ethyl ketone.
(3 splash testing cycles: 20 seconds submersion, & 20 seconds air dry.)
Property Values
Method
Dwell
Dwell/CureTime
Time
Units
72
hr
Substrate Backing
180°
14 N/cm
Peel
Adhesion
128
oz/in
ASTM
D3330
Stainless
Steel
Normal
Tensile
690 kPa
100
lb/in²
ASTM
D897
Aluminum
Overlap 550 kPa
Shear
Strength
80
lb/in²
ASTM
D1002
Stainless
Steel
Short
260 °C
Term
Temperature
500 °F
Notes
Test
Condition
2 mil
12 in/min (305 mm/min)
Aluminum
Foil
4-hour
conditioning
at the
indicated
Resistance
temperature
with
100 g
static
load.
Table continued on next page
3M™ VHB™ Adhesive Transfer Tape F9469PC
Typical Performance Characteristics (continued)
Property Values
Long
149 °C
Term
Temperature
Method
Dwell
Dwell/CureTime
Time
Units
Substrate Backing
Notes
300 °F
Maximum
temperature
where
tape
supports
250 g
in
static
shear
for
10,000
minutes.
Tolerance
Note
Test
Condition
Static
shear
measured
at
various
temperatures
and
gram
loadings
on
stainless
steel.
1/2 sq.
yd (3.22
cm²)
overlap.
Will
hold
listed
weight
for
10,000
minutes.
Table continued on next page
3M™ VHB™ Adhesive Transfer Tape F9469PC
Typical Performance Characteristics (continued)
Property Values
Method
Dwell
Dwell/CureTime
Time
Units
Substrate Backing
Test
Condition
Notes
UV
Excellent
Resistance UV
resistance
through
outdoor
weathering
tests
and
weatherO-meter
tests.
Static Shear
Test Condition
1000 g
Room Temperature
1000 g
66°C (150°F)
1000 g
93°C (200°F)
1000 g
121°C (250°F)
500 g
149°C (300°F)
500 g
177°C (350°F)
Property: Static Shear
Method: ASTM D3654
Available Sizes
Property
Values
Note
Subject to Minimum Order Requirements
Standard Roll Length
55 m
60 yd
Normal Slitting Tolerance
0.8 mm
±1/32 in
Maximum Length
Width
55 m
60 yd
1/4 in to 3/8 in widths
220 m
240 yd
3/8 in to 1 in widths
330 m
360 yd
1 in to 3 in
330 m
360 yd
3 in and wider
Property: Maximum Length
3M™ VHB™ Adhesive Transfer Tape F9469PC
Electrical and Thermal Properties
Property
Values
Method
Insulation Resistance
> 1 × 10^6 MΩ/in²
ASTM D1000
Thermal Conductivity
0.16 W/m/K
Coe cient of Thermal Expansion
770 × 10^-6 m/m/°C
Dielectric Strength
1.1 (btu-in)/(h-ft²-°F)
ASTM C177
Method
Test Condition
3000 V
ASTM D149
Room Temperature
2600 V
ASTM D149
125°C
1900 V
ASTM D149
175°C
4.08
ASTM D150
1kHz, 86°F(30°C)
Property: Dielectric Strength
Weight Loss and Outgassing Performance
Property
Values
Method
Total Mass Loss
1.29 %
ASTM E595-77/84/90
Volatile Condensible Materials
0.02 %
ASTM E595-77/84/90
Note
The testing was done per ASTM E595-77/84/90 as
indicated in the NASA Reference Publication 1124,
Revision 4, “Outgassing Data for Selecting Spacecraft
Materials”, June 1997. The results are reported as
percentage of total mass loss (TML) and percentage of
Volatile Condensible Materials (VCM), respectively, as
shown below.
Handling/Application Information
Application Techniques
Bond strength is dependent upon the amount of adhesive-to-surface contact developed. Firm application pressure helps develop better adhesive contact and improve
bond strength.
To obtain optimum adhesion, the bonding surfaces must be clean, dry, and well uni ed. Some typical surface cleaning solvents are isopropyl alcohol/water mixture or
heptane.*
Ideal tape application temperature range is 70°F to 100°F (21°C to 38°C). Initial tape application to surfaces at temperatures below 50°F (10°C) is not recommended
because the adhesive becomes too rm to adhere readily. However, once properly applied, low temperature holding is generally satisfactory.
*Note: Be sure to follow the manufacturer’s precautions and directions for use when using solvents.
3M™ VHB™ Adhesive Transfer Tape F9469PC
Storage and Shelf Life
Humidity controlled storage: 60° to 80°F (16° to 27°C) and 40-60% R.H.
If stored properly, product retains its performance and properties for 24 months from date of manufacture. If the products have been exposed to severe weather
conditions, we suggest to precondition the products at the above storage conditions for at least 24 hours before using them.
Industry Speci cations
UL 746C
Trademarks
3M and VHB are trademarks of 3M.
References
Property
Values
3m.com Product Page
https://www.3m.com/3M/en_US/company-us/all-3m-products/~/3M-VHBAdhesive-Transfer-Tape-F9469PC?N=5002385+3293241823&rt=rud
Safety Data Sheet (SDS)
https://www.3m.com/3M/en_US/company-us/SDS-search/results/?
gsaAction=msdsSRA&msdsLocale=en_US&co=ptn&q=F9469PC
Family Group
F9460PC
F9469PC
F9473PC
Adhesive Thickness (mm)
0.06
0.13
0.26
Liner
58# Polycoated Kraft
58# Polycoated Kraft
58# Polycoated Kraft
Liner Thickness (mm)
0.106
0.106
0.1
ISO Statement
This Industrial Adhesives and Tapes Division product was manufactured under a 3M quality system registered to ISO 9001 standards.
Recognition/Certi cation
TSCA: These products are de ned as articles under the Toxic Substances Control Act and therefore, are exempt from inventory listing requirements.
MSDS: These products are not subject to the MSDS requirements of the Occupational Safety and Health Administration’s Hazard Communication Standard, 29 C.F.R.
1910.1200(b)(6)(v). When used under reasonable conditions or in accordance with the 3M directions for use, the products should not present a health and safety
hazard. However, use or processing of the products in a manner not in accordance with the directions for use may a ect their performance and present potential
health and safety hazards.
Note: One of 3M’s core values is to respect our social and physical environment. 3M is committed to comply with ever-changing, global, regulatory and consumer
environmental, health, and safety (EHS) requirements. As a service to our customers, 3M is providing information on the regulatory status of many 3M products.
Further regulation information including that for OSHA, USCPSI, FDA, California Proposition 65, READY and RoHS, can be found at 3M.com/regs.
3M™ VHB™ Adhesive Transfer Tape F9469PC
Information
Technical Information: The technical information, guidance, and other statements contained in this document or otherwise provided by 3M are based upon records,
tests, or experience that 3M believes to be reliable, but the accuracy, completeness, and representative nature of such information is not guaranteed. Such
information is intended for people with knowledge and technical skills su cient to assess and apply their own informed judgment to the information. No license under
any 3M or third party intellectual property rights is granted or implied with this information.
Product Selection and Use: Many factors beyond 3M’s control and uniquely within user’s knowledge and control can a ect the use and performance of a 3M product
in a particular application. As a result, customer is solely responsible for evaluating the product and determining whether it is appropriate and suitable for customer’s
application, including conducting a workplace hazard assessment and reviewing all applicable regulations and standards (e.g., OSHA, ANSI, etc.). Failure to properly
evaluate, select, and use a 3M product and appropriate safety products, or to meet all applicable safety regulations, may result in injury, sickness, death, and/or harm
to property.
Warranty, Limited Remedy, and Disclaimer: Unless a di erent warranty is speci cally stated on the applicable 3M product packaging or product literature (in which
case such warranty governs), 3M warrants that each 3M product meets the applicable 3M product speci cation at the time 3M ships the product. 3M MAKES NO
OTHER WARRANTIES OR CONDITIONS, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO, ANY IMPLIED WARRANTY OR CONDITION OF
MERCHANTABILITY, FITNESS FOR A PARTICULAR PURPOSE, OR ARISING OUT OF A COURSE OF DEALING, CUSTOM, OR USAGE OF TRADE. If a 3M product
does not conform to this warranty, then the sole and exclusive remedy is, at 3M’s option, replacement of the 3M product or refund of the purchase price.
Limitation of Liability: Except for the limited remedy stated above, and except to the extent prohibited by law, 3M will not be liable for any loss or damage arising from
or related to the 3M product, whether direct, indirect, special, incidental, or consequential (including, but not limited to, lost pro ts or business opportunity),
regardless of the legal or equitable theory asserted, including, but not limited to, warranty, contract, negligence, or strict liability.
3M United States
3M Center
St. Paul, MN 55144-1000
800-362-3550
www.3M.com