EPS-400-.700-48-BLACK-BOX 数据手册
3M™ Heat Shrink Tubing EPS-400
Adhesive-Lined, 4:1, Semi-Rigid, Polyolefin
Data Sheet
Description
November 2018
3M Heat Shrink Tubing EPS-400 is a medium-wall, semi-rigid tubing offering the
advantages of integral, adhesive-lined construction. The tubing is made from flameretardant, flexible polyolefin with an internal layer of special thermoplastic adhesive.
The heat-shrinkable outer wall is selectively cross-linked, while the adhesive
maintains high flow and excellent adhesion characteristics.
When heated in excess of 121ºC (250ºF), EPS-400 tubing rapidly shrinks to a
skintight fit, forcing the melted adhesive to flow and cover the substrate. Upon
cooling, the adhesive solidifies, forming a permanent, non-drying, flexible and water
resistant barrier. Adhesive reflow will occur at temperatures above 80ºC (176ºF).
Agency Approvals &
Self Certifications
Meets requirements of:
•
UL Recognized, UL File E-157227 at 600 Volts and 125 ºC maximum
•
CSA Recognized, CSA File LR38227
•
For RoHS and REACH information, please visit www.3M.com/regs
Applications
3M EPS-400 tubing offers excellent environmental protection for electronic
components, wire splices, wire bundles and harness breakouts. Automotive, truck
and marine wire splices and harness breakouts are also quickly and easily protected
from a variety of harsh environments.
Shrink Ratio
3M EPS-400 tubing has a 4:1 shrink ratio. When fully recovered, the tubing will
shrink 25% of its as-supplied diameter. The recovered wall thickness of the tubing is
proportional to the degree of recovery.
The operating temperature range is from -55ºC (-67ºF) to 110 ºC (230ºF), with a
shrink temperature minimum of 121ºC (250 ºF).
Standard Sizes and
Dimensions
Ordering
Size
(Nominal)
.300
.350
.450
.700
Expanded I.D.
(Minimum)
In.
.300
.350
.450
.700
(mm)
(7,62)
(8,89)
(11,43)
(17,78)
1 of 3
Recovered I.D.
(Maximum
In.
(mm)
.060 (1,52)
.080 (2,03)
.105 (2,67)
.175 (4,45)
Total Recovered
Wall Thickness
(Nominal)
In.
.033
.038
.043
.060
(mm)
(0,84)
(0,97)
(1,09)
(1,52)
Meltable
Recovered Wall
Thickness
In.
(mm)
.028 (0,71)
.033 (0,84)
.053 (1,35)
.055 (1,40)
3M™ Heat Shrink Tubing EPS-400
Typical Properties
Not for specifications. Values are typical, not to be considered minimum or maximum.
Properties measured at room temperature 73°F (23°C) unless otherwise stated.
Physical Property
Typical Value
US units (metric)
Color
Black and other colorcoded sizes
Tensile Strength
1900 PSI
Ultimate Elongation
400%
Longitudinal Change
+1, -10%
Secant Modulus (2%)
33,000 PSI
Specific Gravity
1.25
Heat Aging (outer wall only)
168 hrs @ 175ºC
Elongation 175%
Heat shock (outer wall only)
4 hrs @ 250 ºC
No dripping, flowing,
cracking
Low Temperature Flexibility (outer wall only)
4 hrs @ -55 ºC
No cracking
Flammability
Self-extinguishing
Electrical Property (Test Method)
Typical Value
US units (metric)
Dielectric Strength
700 V/mil
Volume Resistivity
1014 ohm/cm
Chemical Property (Test Method)
Typical Value
US units (metric)
Corrosion Resistance (Copper mirror)
Non-corrosive
Fungus Resistance
Non-nutrient
Water Absorption
0.3%
Fluid Resistance
Excellent
Adhesive
Typical Value
Peel Strength, pli
Polyethylene
PVC
Lead
Aluminum
30
10
15
40
Corrosive Effect (Copper mirror)
Non-corrosive
2 of 3
3M™ Heat Shrink Tubing EPS-400
Shelf Life & Storage
3M Heat Shrink Tubing EPS-400 has a 10-year shelf life from date of manufacture