SJ5208

Technical Data | July 2015 3M™ Bumpon™ Protective Products Resilient Rollstock SJ5200 • SJ5800 • SJ5900 • SJ6000 • SJ6200 Series Product Description 3M™ Bumpon™ Resilient Rollstock Products are opaque, colored polyurethane materials produced with aggressive pressure-sensitive adhesives. 3M™ Bumpon™ Resilient Rollstock Product Thickness Inches mm Polyurethane Hardness, Shore M Polyurethane Surface Finish SJ5216 SJ5208 1/16 1/8 1.6 3.2 36 (soft foam) matte 29 (soft foam) SJ5832 SJ5801 SJ5816 SJ5808 1/32 3/64 1/16 1/8 0.8 1.0 1.6 3.2 72 72 matte 72 72 SJ5916 SJ5908 SJ5904 1/16 1/8 1/4 1.6 3.2 6.4 40 (medium foam) 36 (medium foam) matte 36 (medium foam) A-20 (acrylic) SJ6032 SJ6016 SJ6008 SJ6005 1/32 1/16 1/8 1/5 0.8 1.6 3.2 5.0 72 72 matte 72 72 A-20 (acrylic) SJ6232 SJ6216 SJ6208 1/32 1/16 1/8 0.8 1.6 3.2 72 72 matte 72 R-25 (synthetic rubber) Adhesive Type R-25 (synthetic rubber) R-30 (natural rubber) Polyurethane Pressure Sensitive Adhesive Polyester Release Liner 3M™ Bumpon™ Protective Products Resilient Rollstock SJ5200 • SJ5800 • SJ5900 • SJ6000 • SJ6200 Series Features • Can be die cut to a variety of shapes and sizes. • Excellent skid-resistance, high coefficient of friction. • Excellent resistance to marring or staining.* • Long aging resiliency – will not crack or harden.* • Excellent cushioning properties. • Excellent abrasion resistance. • Vibration and shock dampening. • Easy application – pressure-sensitive backing. *Resulting from a urethane composition. Application Ideas • Die cut into circles or squares for use as skid-resistant feet on hand held or desktop computers, calculators, electric housewares, electronic equipment, desk top items and medical devices. • Die cut for gasket application. • Skid-resistant surface on floor. • Cushions or spacers within electronic devices. • Selective masking for sandblast operation. • Spacer or stop to prevent surface damage. • Anti-rattle spacer to fill gaps, dampen noise and reduce vibration. • Door kick pads. • Corner protection strips. • Roll covering for textile industry and other web feed machinery. • Die cut cushioning stop for cabinetry (3M™ Bumpon™ Resilient Rollstock SJ5200 and SJ5900 Foam). (2) 3M™ Bumpon™ Protective Products Resilient Rollstock SJ5200 • SJ5800 • SJ5900 • SJ6000 • SJ6200 Series Product Construction 3M™ Bumpon™ Resilient Rollstock Series SJ5800 SJ5900 SJ6000 SJ5200 Elastomer Elastomer Finish Release Liner Adhesive SJ6200 Polyurethane (foam) Polyurethane (solid) Polyurethane (foam) Polyurethane (solid) Polyurethane (solid) matte matte matte matte matte 4 mil, silicone coated, translucent polyester (PET), with printed 3M logo 4 mil, silicone coated, translucent polyester (PET), with printed 3M logo 4 mil, silicone coated, translucent polyester (PET), with printed 3M logo 4 mil, silicone coated, translucent polyester (PET), with printed 3M logo 4 mil, silicone coated, translucent polyester (PET), with printed 3M logo R-25 (synthetic rubber) R-30 (natural rubber) A-20 (acrylic) A-20 (acrylic) R-25 (synthetic rubber) 3M™ Bumpon™ Resilient Rollstock Product   Color SJ5216 SJ5208 SJ5832 SJ5801 SJ5816 SJ5808 SJ5916 SJ5908 SJ5904 SJ6032 SJ6016 SJ6008 SJ6005 SJ6232 SJ6216 SJ6208 Light Brown Light Brown Black Black Brown Black Brown Black Black Black Black Brown Black Brown Black Brown Black Brown White Black Black Black Black Thickness* in. in. (mm) 1/16 0.062 (1.6) 1/8 0.125 (3.2) 1/32 0.031 (0.8) 3/64 0.039 (1.0) 1/16 0.062 (1.6) 1/8 0.125 (3.2) 1/16 0.062 (1.6) 1/8 0.125 (3.2) 1/4 0.250 (6.4) 1/32 0.031 (0.8) 1/16 0.062 (1.6) 1/8 0.125 (3.2) 1/5 0.20 (5.0) 1/32 0.031 (0.8) 1/16 0.062 (1.6) 1/8 0.125 (3.2) Thickness ± in. Tolerance ± (mm) 0.010 (0.25) 0.015 (0.38) 0.005 (0.13) 0.006 (0.15) 0.007 (0.18) 0.010 (0.25) 0.010 (0.25) 0.015 (0.38) 0.020 (0.50) 0.005 (0.13) 0.007 (0.18) 0.010 (0.25) 0.012 (0.31) 0.05 (0.13) 0.007 (0.18) 0.010 (0.25) 36 36 72 72 36 36 36 36 18 72 36 36 24 72 36 36    Standard in. (mm) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3) 4.5 (114.3)    Minimum in. (mm) 0.5 (12.7) 0.5 (12.7) 0.5 (12.7) – – 0.5 (12.7) 1 (25.4) 0.5 (12.7) 0.5 (12.7) 1 (25.4) 0.5 ((12.7) 0.5 (12.7) 1 (25.4) – – 0.5 (12.7) 0.5 (12.7) 1 (25.4)    Maximum in. (mm) Roll Length yd. Roll Width** Slitting ± in. Tolerance ± in. ± (mm) 9 9 (228.6) (228.6) 1/32 0.031 (0.8) 9 9 (228.6) (228.6) 9 9 (228.6) (228.6) 9 9 (228.6) (228.6) 1/32 0.031 (0.8) 9 9 (228.6) (228.6) 1/32 0.031 (0.8) 9 9 9 (228.6) (228.6) (228.6) 1/32 0.031 (0.8) 9 (228.6) 9 9 (228.6) (228.6) 1/32 0.031 (0.8) *Tested in accordance with ASTM D-3767 method, procedure A (3.2 psi) measured without liner. **Non-standard sizes may be subject to minimum order requirements. Custom Rollstock Products Custom Thickness: 3M can customize thickness to your specifications. Note: The capability range for 3M™ Bumpon™ Resilient Rollstock Series SJ5800, SJ6000, and SJ6200 is 1/32 in. (0.031) minimum and 1/4 in. (0.250) maximum. The capability range for 3M™ Bumpon™ Resilient Rollstock Series SJ5900 is 1/16 in. (0.062) minimum and 5/16 in. (0.312) maximum. Custom Color: 3M can match most colors to your specifications. Note: Special products require a qualifying minimum order quantity, and one-time color matching charge. For more information please contact your local 3M sales rep or distributor. (3) 3M™ Bumpon™ Protective Products Resilient Rollstock SJ5200 • SJ5800 • SJ5900 • SJ6000 • SJ6200 Series Typical Physical Properties and Performance Characteristics Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Property Test Method*** SJ5200 3M™ Bumpon™ Resilient Rollstock Series SJ5800 SJ5900 SJ6000 Hardness, Shore M ASTM-D-2240 36 (SJ5216) 72 29 (SJ5208) Approximate Density, lb/ft3 (g/cm3) Kinetic Coefficient of Friction* ASTM-D-1894 Stainless Steel Glass Formica® laminate Wood 40 (SJ5916) 72 36 (SJ5908, SJ5904) SJ6200 72 40 (0.64) 80 (1.3) 40 (0.64) 80 (1.3) 80 (1.3) * * * * > 1 > 1 0.9 - 1.4 0.9 - 1.4 > 1 > 1 0.8 - 1.4 0.8 - 1.4 > 1 > 1 0.9 - 1.4 0.9 - 1.4 >1 >1 0.9 - 1.4 0.9 - 1.4 * Two important laws of friction applicable to 3M™ Bumpon™ Resilient Rollstock are: (1) Friction is independent of the area of contact between solids. (2) Friction is proportional to the load between solid surfaces. Thus, if the load (weight) is doubled, the force required to cause surface sliding is also doubled. This is expressed mathematically as follows: Sliding force = (kinetic coefficient of friction) x (weight) Abrasion Resistance Taber H 18, 1 kg, g/1000 cycles Tensile, * 1.7 - 1.9 1.8 - 2.0 1.7 - 1.9 1.7 - 1.9 lb/in2 ASTM-D-412, Die A * (kPa) 600 (4140) 120 (830) 600 (4140) 600 (4140) Elongation, % Compression Set, % Dielectric Strength, volts/mil ASTM-C-501 ASTM-D-412, Die A * 100 100 100 100 ASTM-D-1056 (50% deflection) ASTM-D-395 (25% deflection) 8 10 – – – – 3 4 12 14 – – – – 3 4 – – 3 4 ASTM-D-1000 * 200 Flammability Listing UL Classification * UL94HB 140 200 200 UL94HBF UL94HB UL94HB (except SJ5916) Stain Resistance** 3M - 24 hrs. @ 158°F against white paint, 7 days exposed to UV No staining observed Ozone and Oxygen Resistance** 3M - 30 days @ 50 ppm ozone No visual deterioration Solvent and Fuel Resistance** 3M - 24 hr. immersion    5% Detergent in water    25% Ammonia in water    Bleach    Hydrochloric Acid (1 normal solution)    Diesel Fuel    Auto Oil    Isopropyl Alcohol    Heptane    Toluene (Toluol)    Lacquer Thinner Load Tolerance No apparent effect No apparent effect No apparent effect No apparent effect No apparent effect No apparent effect Slight effect (swelling) Slight effect (swelling) Considerable effect (swelling) Considerable effect (swelling)  he recommended maximum load which Bumpon Resilient Rollstock series SJ5800, SJ6000 T and SJ6200 will support is 100 psi (690 kPa) at 70°F (21°C) to 120°F (49°C). Environmental Performance Bumpon Resilient Rollstock is intended for interior applications where resilience and all other physical properties will remain unchanged. When exposed to UV light for extended periods, some discoloration may occur. Bumpon resilient rollstock may be used outdoors in a protected area with some discoloration and chalking possible. * = Not tested for Bumpon SJ5200 Series (soft foam) ** = Reference test for time periods specified only. Results may vary for different product application conditions. *** = When ASTM method is listed, data was collected in accordance with ASTM test method. (4) 3M™ Bumpon™ Protective Products Resilient Rollstock SJ5200 • SJ5800 • SJ5900 • SJ6000 • SJ6200 Series Relative Adhesive Performance Characteristics Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. SJ5800 Series 3M™ Bumpon™ Resilient Rollstock SJ5900 Series SJ6000 Series SJ5200 Series SJ6200 Series Adhesive: Natural Rubber R-30 Acrylic A-20 Synthetic Rubber R-25 Good Good Poor Good Excellent Excellent Excellent Fair Poor Excellent Excellent Excellent Excellent Good Fair Good Good Poor Fair Excellent Excellent Adhesion (Peel)   Low Surface Energy:   High Surface Energy: Static Shear     75°F (25°C): 120°F (49°C):   158°F (70°C): Initial Adhesion   Low Surface Energy:   High Surface Energy: Solvent Resistance: Good Excellent Good Age Life: Good Excellent Good Adhesive Performance Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. The following table on peel adhesion provide representative performance characteristics of the adhesive systems used in the construction of 3M™ Bumpon™ Resilient Rollstock SJ5200, SJ5800, SJ5900, SJ6000, and SJ6200 series products. 90° Peel Adhesion Substrate: Peel Force, oz. per 1/2 inch SJ5800 Series 3M™ Bumpon™ Resilient Rollstock SJ5900 Series SJ6000 Series SJ5200 Series SJ6200 Series Natural Rubber R-30 Acrylic A-20 Synthetic Rubber R-25 Polypropylene 25   3 52 Polystyrene 25 11 55 ABS 25 25 55 Stainless Steel 22 25 55 Aluminum 22 25 55 3M Test Method TM-2011; 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216. (5) 3M™ Bumpon™ Protective Products Resilient Rollstock SJ5200 • SJ5800 • SJ5900 • SJ6000 • SJ6200 Series Adhesive Description Natural Rubber (R-30) – Used in the construction of 3M™ Bumpon™ Resilient Rollstock SJ5800 Series products. This high tack adhesive system provides excellent initial adhesion and is designed for providing excellent adhesion to a wide variety of surfaces including many low surface energy surfaces such as polypropylene, polyethylene and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures. Acrylic (A-20) – Used in construction of 3M™ Bumpon™ Resilient Rollstock SJ5900 and SJ6000 Series products. This high strength adhesive system provides excellent shear strength properties. The adhesive is designed for providing excellent adhesion to many high surface energy substrates such as metals, ABS, polycarbonate and acrylic. When adhesion is required on low surface energy substrates (ie, polypropylene, polyethylene, etc.) acrylic-based adhesives do not perform as well as rubber-based adhesives. Synthetic Rubber (R-25) – Used in the construction of 3M™ Bumpon™ Resilient Rollstock SJ6200 Series products. This very high tack adhesive system provides excellent initial adhesion and is designed for providing excellent adhesion to a wide variety of surfaces including many low surface energy surfaces such as polypropylene, polyethylene and powder coated paints. Improved die-cutting performance with new polyester (PET) release liner. This adhesive system shows reduced shear properties at elevated temperatures. Application Techniques Application Temperature: 40°F (5°C) to 125°F (52°C) Service Temperature: - 30°F (-34°C) to 150°F (66°C) 225°F (107°C) intermittent exposure To obtain maximum adhesion, surfaces should be flat, dry, and free of contaminants. Surface contact is essential to adhesive performance. To maximize contact on a substrate: • Clean surfaces with low strength solvent such as isopropyl alcohol (rubbing alcohol) or heptane. Note: Be sure to follow the solvent manufacturer’s precautions and directions for use when using solvents. • Apply firm pressure to help increase the cold flow and contact of the adhesive with the substrate. • Allow time (dwell) to increase the surface contact and adhesion (see illustration below). Adhesive Surface Contact Rubber Adhesive vs. Acrylic Adhesive Bond Build-up Initial Contact (Minimal Contact) Adhesive Rubber High ylic Acr Adhesion Bonding Surface After Rubdown (More Contact) Adhesive Bonding Surface After Dwell Time (Excellent Contact) Adhesive Low Bonding Surface 0 24 48 Dwell Time – Hours 72 Note:  Product selection is ultimately the responsibility of the user and should conduct their own tests under actual use and storage conditions to determine whether product is fit for a particular purpose and user’s method of application. (6) 3M™ Bumpon™ Protective Products Resilient Rollstock SJ5200 • SJ5800 • SJ5900 • SJ6000 • SJ6200 Series Die Cut Considerations • Very important that knives be sharp. •  Although rotary die cutting can be used for thicker materials (≥ 1/16 inches), distortion in the die cut shape is possible using this die cutting method. Flat bed die cutting is recommended for thicker materials. • The R-25 (synthetic rubber) adhesive system is very firm (tough). It can be more difficult to die cut versus the R-30 and A-20 adhesive systems. Also, the R-25 adhesive system is inherently stringy; as a result, if the adhesive is not thoroughly cut, the adhesive may have a tendency to string-out when the die cut parts are removed from the release liner quickly or by using a snapping motion. The adhesive string-out will not diminish the performance of the product. • Some re-welding (tendency of the adhesive system to flow back together after die cutting) is possible with the R-25 adhesive system. Exposure to high temperature (greater than the recommended storage temperature of 60° to 80°F [16° to 27°C]) in combination with time and pressure will increase the tendency of re-welding. Die Cut Examples 3M™ Bumpon™ Resilient Rollstock Products can be die cut to a variety of shapes and sizes. The following examples illustrate just a few of the possibilities. Storage and Shelf Life The shelf life of 3M™ Bumpon™ Protective Products is 18 months from the date of manufacture when stored in the original packaging materials and stored at 16-27°C (60-80°F) and 50% relative humidity. (7) 3M™ Bumpon™ Protective Products Resilient Rollstock SJ5200 • SJ5800 • SJ5900 • SJ6000 • SJ6200 Series Regulatory: For regulatory information about this product, contact your 3M representative. Technical Information: The technical information, recommendations and other statements contained in this document are based upon tests or experience that 3M believes are reliable, but the accuracy or completeness of such information is not guaranteed. Product Use: Many factors beyond 3M’s control and uniquely within user’s knowledge and control can affect the use and performance of a 3M product in a particular application. Given the variety of factors that can affect the use and performance of a 3M product, user is solely responsible for evaluating the 3M product and determining whether it is fit for a particular purpose and suitable for user’s method of application. Warranty, Limited Remedy, and Disclaimer: Unless an additional warranty is specifically stated on the applicable 3M product packaging or product literature, 3M warrants that each 3M product meets the applicable 3M product specification at the time 3M ships the product. 3M MAKES NO OTHER WARRANTIES OR CONDITIONS, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO, ANY IMPLIED WARRANTY OR CONDITION OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE OR ANY IMPLIED WARRANTY OR CONDITION ARISING OUT OF A COURSE OF DEALING, CUSTOM OR USAGE OF TRADE. If the 3M product does not conform to this warranty, then the sole and exclusive remedy is, at 3M’s option, replacement of the 3M product or refund of the purchase price. Limitation of Liability: Except where prohibited by law, 3M will not be liable for any loss or damage arising from the 3M product, whether direct, indirect, special, incidental or consequential, regardless of the legal theory asserted, including warranty, contract, negligence or strict liability. Electronics Materials Solutions Division 3M Center, Building 224-3N-11 St. Paul, MN 55144-1000 1-800-251-8634  phone   651-778-4244  fax www.3M.com/electronics 3M and Bumpon are trademarks of 3M Company. Formica is a registered trademark of the Formica Corporation. Please recycle. ©3M 2015. All rights reserved. 60-5002-0523-6 (8)