PFR03S-000-XNH

CYNTEC CO., LTD. 乾坤科技股份有限公司 DOCUMENT : RK000000NH REVISION : A4 PAGE : 1 OF 9 1/20W, 0201 Series Thick Film Chip Resistor (Lead / Halogen free) 1. Scope This specification applies to 0.3mm x 0.6mm (0201) size, fixed metal film chip resistors rectangular type for use in electronic equipment. 2. Type Designation PFR03 S (1) Where — □□□□ — □ NH (2) (3) (4) (1) Series No. (2) Nominal resistance value : For example – Three digits of number (E-24 Series) 000 = Jumper 100 = 10 102 = 1k Four digits of number (E-96 Series) 11R3 = 11.3 1131 =1.13k (3) Tolerance of Resistance X = Jumper(Below 50m) D =  0.5% F =  1.0% G =  2.0% J =  5.0% (4) NH = Sn plating ( Lead free / Halogen free) CYNTEC CO., LTD. 乾坤科技股份有限公司 DOCUMENT : RK000000NH REVISION : A4 PAGE : 2 OF 9 3. Electrical Specifications Table 1. : *Power rating 1/20W Resistance Values E-24 series , E-96 series Resistance Tolerance  0.5%(D) Resistance Range (  ) Temperature Coefficient of Resistance ppm/℃ 100~100K 1.0 ~ 9.76 10 ~ 91 +600 ~  200  300 -200 E-24 series  1.0%(F)  5.0%(J)  2.0%(G) ,  5.0%(J) 100 ~ 1M  200 1.0 ~ 9.1 +600 ~ -200 10 ~ 91 100 ~ 10M  300  200  55℃ to  125℃ Operating temperature range Max. operating voltage** 25V Note: *Package Power Temperature Derating Curve RATED LOAD(%) 100 0 -55 70 125 AMBIENT TEMPERATURE(℃) Figure 1.：Power Temperature Derating Curve Note: **Resistors shall have a rated DC or AC(rms.) continuous operating voltage corresponding to the power rating, as calculated from the following formula V  PR Where V : Rated voltage (V) P R : Rated power (W) : Nominal resistance () If the voltage so obtained exceeds the maximum operating voltage, this maximum voltage shall be the rated voltage. Table 2. : Jumper: Resistance Tolerance Rated current Operating Temperature Range Below 50 mΩ 1A -55℃ to 125℃ CYNTEC CO., LTD. 乾坤科技股份有限公司 DOCUMENT : RK000000NH REVISION : A4 PAGE : 3 OF 9 4. Construction and Physical Dimension L a a Code Letter Dimension L 0.6  0.03 W 0.3  0.03 t 0.23  0.03 a 0.10  0.05 b 0.15  0.05 Unit : mm W t b 5. Marking No marking on the protect coating 6. Life Tests 6-1 Electrical Specification and Requirement Item Resistor Test Method (Refer to JIS C 5201) Jumper Short Time Overload △R: (2%+ 0.1) Max. 50m Without damage by flashover, spark, arcing, burning or breakdown (1) Applied voltage: 2.5 x rated voltage or 2 x maximum operating voltage which ever is less (2) Test time : 5 seconds Insulation Resistance Over 100 M on Overcoat layer face up Over 1,000 M on Substrate side face up (1) Setup as figure 2 (2) Test voltage: 100 VDC (3) Test time: 60 + 10 / -0 seconds Voltage Proof Max. 50m △R:  (2%+ 0.1) Without damage by flashover, spark, arcing, burning or breakdown (1) Setup as figure 2 (2) Test voltage: 100 VAC(rms.) (3) Test time: 60 +10 / -0 seconds Pressure Rod (Metal) Insulation Plate Spring Measurement Point A (R=0.5 mm) Substrate Over coat Film A B Sample Electrode Voltage Supply Metal Block Measurement Point B Substrate Side Figure 2 : Measurement Setup CYNTEC CO., LTD. 乾坤科技股份有限公司 DOCUMENT : RK000000NH REVISION : A4 PAGE : 4 OF 9 6-2 Mechanical Specification and Requirement Item Resistor Solderability Jumper Test Method (Refer to JIS C 5201) The surface of terminal immersed shall be Solder bath: minimum of 95% covered with a new After immersing in flux, dip in coating of solder 245  5℃ molten solder bath for 2  0.5 seconds Resistance to Solder △R: (1.0%+ 0.05) Heat Without distinct deformation in appearance Max. 50m (1) Pre-heat: 100~110℃ for 30 seconds (2) Immersed at solder bath of 270  5℃ for 10  1 seconds (3) Measuring resistance 1 hour after test Vibration △R: (0.5%+ 0.05) Without mechanical damage such as break (1) Vibration frequency: 10Hz to 55Hz to10Hz in 60 seconds as a period (2) Vibration time: period cycled for 2 hours in each of 3 mutual perpendicular directions (3) Amplitude: 1.5mm Shock △R: (0.25%+ 0.05) Without mechanical damage such as break (1) Peak value: 490N (2) Duration of pulse: 11ms (3) 3 times in each positive and negative direction of 3 mutual perpendicular directions Bending Test △R: (1.0%+ 0.05) Without mechanical damage such as break Bending value: 3 mm for 30  1 seconds Solvent Resistance Marking should be legible Without mechanical and distinct damage in appearance (1) Solvent: Trichloroethane or Isopropyl alcohol (2) Immersed in solvent at room temperature for 90 seconds Max. 50m CYNTEC CO., LTD. 乾坤科技股份有限公司 DOCUMENT : RK000000NH REVISION : A4 PAGE : 5 OF 9 6-3 Endurance Specification and Requirement Item Resistor Thermal Shock Jumper △R: (1.0%+ 0.05) Max. 50m Without distinct damage in appearance Moisture with Load △R: (5.0%+ 0.1) Max. 50m Without distinct damage in appearance Marking should be legible Test Method (Refer to JIS C 5201) (1) Repeat 5 cycle as follow: (-55  3℃,30minutes) (Room temperature, 2~3 minutes)  (+125  2℃,30minutes) (Room temperature, 2~3 minutes) (2) Measuring resistance 1 hour after test (1) Environment condition: 40  2℃,90~95% RH (2) Applied Voltage: rated voltage (3) Test period: (1.5 hour ON) (0.5 hour OFF) cycled for total 1,000 + 48 / - 0 hours (4) Measuring resistance 1 hour after test Load Life Max. 100m △R: (5.0%+ 0.1) Without distinct damage in appearance (1) Test temperature: 70  2℃ (2) Applied Voltage: rated Voltage (3) Test period: (1.5 hour ON) (0.5 hour OFF) cycled for total 1,000 + 48 / - 0 hours (4) Measuring resistance 1 hour after test Low Temperature Store Max. 100m △R: (5.0%+ 0.1) Without distinct damage in appearance High Temperature Store Max. 100m △R: (5.0%+ 0.1) Without distinct damage in appearance (1) Store temperature: -55  3℃ for total 1,000 + 48 / - 0 hours (2) Measuring resistance 1 hour after test (1) Store temperature: +125  2℃ for total 1,000 + 48 / - 0 hours (2) Measuring resistance 1 hour after test CYNTEC CO., LTD. 乾坤科技股份有限公司 DOCUMENT : RK000000NH REVISION : A4 PAGE : 6 OF 9 7. Recommend Land Pattern Dimensions A C A 0.3 B 1.0 C 0.3 ~ 0.7 Unit : mm B CYNTEC CO., LTD. 乾坤科技股份有限公司 DOCUMENT : RK000000NH REVISION : A4 PAGE : 7 OF 9 8. Packaging 8-1 Dimensions 8-1-1 Tape packaging dimensions 8-1-2 Reel dimensions 2.00.5 +0 φ180-1.5 φ60+1 -0 φ130.2 φ210.8 9.0+0.3 -0.0 Unit : mm 11.4 1.0 CYNTEC CO., LTD. 乾坤科技股份有限公司 DOCUMENT : RK000000NH 8-2 Peel force of top cover tape The peel speed shall be about 300 mm/min. The peel force of top cover tape shall be between 0.1 to 0.5 N. Top Cover Tape 0.1N~0.5N 165~180° 8-3 Numbers of taping 10,000 pieces/reel 8-4 Making The following items shall be marked on the reel. (1) Type designation. (2) Quantity (3) Manufacturing date code (4) Manufacturer’s name REVISION : A4 PAGE : 8 OF 9 CYNTEC CO., LTD. 乾坤科技股份有限公司 DOCUMENT : RK000000NH REVISION : A4 PAGE : 9 OF 9 9. Care note 9-1 Care note for storage (1) Chip resistor shall be stored in a room where temperature and humidity must be controlled. (temperature 5 to 35℃, humidity 45 to 85% RH) However, a humidity keep it low, as it is possible. (2) Chip resistor shall be stored as direct sunshine doesn’t hit on it. (3) Chip resistor shall be stored with no moisture, dust, a material that will make solderability inferior, and a harmful gas (Chloridation hydrogen, sulfurous acid gas, and sulfuration hydrogen) 9-2 Care note for operating and handling (1) It is necessary to protect the edge and protection coat of resistors from mechanical stress. (2) Handle with care when printing circuit board (PCB) is divided or fixed on support body, because bending of printing circuit board (PCB) mounting will make mechanical stress for resistors. (3) Resistors shall be used with in rated range shown in specification. Especially, if voltage more than specified value will be loaded to resistor, there is a case it will make damage for machine because of temperature rise depending on generating of heat, and increase resistance value or breaks. (4) In case that resistor is loaded a rated voltage, it is necessary to confirms temperature of a resistor and to reduce a load power according to load reduction curve, because a temperature rise of a resistor depends on influence of heat from mounting density and neighboring element. (5) Observe Limiting element voltage and maximum overload voltage specified in each specification (6) If there is possibility that a large voltage (pulse voltage, shock voltage) charge to resistor, it is necessary that operating condition shall be set up before use.