000824-000

Altera™ MT5000 Flexible, Modified Polyolefin, Heat - Shrinkable Tubing This specification covers the requirements for one type of single wall, electrical insulating, extruded tubing whose diameter will reduce to a predetermined size upon application of heat in excess of 110°C (230°F). The tubing is fabricated from modified polyolefin crosslinked by irradiation. It shall be homogenous and essentially free from flaws, defects, pinholes, seams, cracks or inclusions. The tubing is fabricated from materials which meet the requirements of U.S. Pharmacopeia Class VI Plastics. Color shall be black or clear unless otherwise specified. Table 1: Dimensions As Supplied Size 3/64 1/16 3/32 1/8 3/16 1/4 3/8 1/2 3/4 1 1-1/2 2 Recovered Inside Diameter Minimum (D) mm. in. .046 1.17 .063 1.60 .093 2.36 .125 3.18 .187 4.75 .250 6.35 .375 9.53 .500 12.70 .750 19.05 1.000 25.40 1.500 38.10 2.000 50.80 Inside Diameter Maximum (d) mm. in. .023 0.58 .031 0.79 .046 1.17 .062 1.58 .093 2.36 .125 3.18 .187 4.75 .250 6.35 .375 9.53 .500 12.70 .750 19.05 1.000 25.40 Wall Thickness(Inches, Millimetres) (W) Minimum Maximum Nominal .013 0.33 .019 0.48 .016 0.40 .014 0.35 .020 0.50 .017 0.43 .017 0.43 .023 0.58 .020 0.50 .017 0.43 .023 0.58 .020 0.50 .017 0.43 .023 0.58 .020 0.50 .022 0.56 .028 0.71 .025 0.64 .022 0.56 .028 0.71 .025 0.64 .022 0.56 .028 0.71 .025 0.64 .027 0.69 .033 0.84 .030 0.76 .030 0.76 .040 1.01 .035 0.88 .034 0.86 .046 1.17 .040 1.01 .038 0.96 .052 1.32 .045 1.14 Specification Control Drawing TE Connectivity 300 Constitutional Drive Menlo Park, CA 94025 USA TE Connectivity reserves the right to amend this drawing at any time. Users should evaluate the suitability of the product for their application Cage Code: Scale: Size: 06090 None ™ Altera MT5000 Flexible, Modified Polyolefin, Heat - Shrinkable Tubing Title: A Document No : MT5000 Rev. Date: Rev.: Sheet: 15-Apr-11 B1 1 of 2 Print Date: 12-May-11 If this document is printed it becomes uncontrolled. Check for the latest revision. Table 2: Properties Property Physical * Dimensions * Longitudinal Change * Concentricity as supplied * Tensile Strength * Ultimate Elongation Secant Modulus Heat Resistance 168 hours at 125°C (257°F) Followed by test for: Ultimate Elongation Electrical Dielectric Strength Dielectric Withstand 3000V, 60 Hz Chemical Fluid Resistance 24 hours at 23 ± 3°C (77 ± 5°F) Isopropyl Alcohol 5% Saline Solution Cidex** Followed by tests for: Dielectric Strength Unit Requirement Test Method Inches (mm) Percent Percent PSI (MPa) Percent PSI (MPa) In accordance with Table 1 +0, -10 maximum 70 minimum 1800 minimum (12.4) 200 minimum 4 2.5 x 10 maximum (172) ASTM D 2671 ASTM D 2671 ASTM D 2671, 20"/ minute ASTM D 2671 Percent 100 minimum ASTM D 2671, 20"/minute Volts/mil (volts/mm) 500 minimum (19.680) ASTM D 2671 sec 60 minimum ASTM D 2671 ASTM D 2671 Volts/mil (volts/mm) PSI (MPa) ppm Tensile Strength Heavy Metals Analysis Cadmium Mercury Lead Bismuth Antimony 500 minimum (19,680) ASTM D 2671 1800 minimum (12.4) 1 maximum (total of all metals) ASTM D 2671 USP XXII Physicochemical Tests-Plastics (Note 1) * Denotes lot acceptance test **Trademark of Johnson & Johnson Company Note 1: Sample preparation and extraction is per USP XXII. Metals analysis may be colorimetric as described in USP XXII or by equivalent quantitative analytical method. Raychem reserves the rights to amend this specification at any time. Users should evaluate the suitability of the product for their application. Rev. Date: Rev.: Document No. Sheet: 15-Apr-11 B1 MT5000 2 of 2 Print Date: 12-May-11 If this document is printed it becomes uncontrolled. Check for the latest revision.