10614
SPECIFICATION CONTROL DRAWING
CHEMINAX
77 OHM, AWG 24, 19 STRANDS OF AWG 36, EMP HARDENED,
DATA BUS CABLE, MIL-STD-1553
Date:
2-13-18
Revision:
K
THIS SPECIFICATION SHEET FORMS A PART OF THE LATEST ISSUE OF RAYCHEM SPECIFICATION 1200.
CONSTRUCTION DETAILS
ELECTRICAL CHARACTERISTICS
DIMENSIONS ARE NOMINAL VALUES IN INCHES, UNLESS OTHERWISE CHARACTERISTIC IMPEDANCE
DESIGNATED.
.0250
(.635 mm)
.048 ± .002
(1.22 ± .05 mm)
.032
(.813 mm)
CONDUCTORS
AWG 24,
19 Strands of AWG 36,
Silver-Coated HighStrength Copper Alloy
30.0 pF/ft. (98.4 pF/m) (maximum)
ATTENUATION
1.4 dB/100 ft. (4.59 dB/100 m) (maximum)
at 1 MHz
SURFACE TRANSFER IMPEDANCE 0.2 milliohms/meter (maximum)
(Per SAE AS85485)
at 30 MHz
ADDITIONAL REQUIREMENTS
COMPONENT WIRE PRIOR TO CABLING
DIELECTRICS
(Test procedures per SAE AS22759)
Radiation-Crosslinked,
CONDUCTOR RESISTANCE
26.5 ohms/1000 ft. (86.9 ohms/km) (nominal)
Modified ETFE
Colors - Light Blue/White CROSSLINKING PROOF TEST
300 ± 3°C for 1 hour,
.500 inch (12.7 mm) mandrel,
FILLERS
.375 lb (170 g), 2.5 kV dielectric test
Radiation-Crosslinked,
INSULATION
(DIELECTRIC)
Modified ETFE
ELONGATION
50% (minimum)
TENSILE STRENGTH
5000 lbf/in2 (34.5 N/mm2) (minimum)
INSULATION FLAWS
SPARK TEST
IMPULSE TEST
.113
(2.87 mm)
77 ± 5 ohms, Method C at 1 MHz
MUTUAL CAPACITANCE
1st SHIELD
AWG 38,
Tin-Coated Copper,
Optimized
3.0 kV (rms)
8.0 kV (peak)
INSULATION RESISTANCE
5000 megohms for 1000 ft.
(1524 megohms-km) (minimum)
LOW TEMPERATURE-COLD BEND
-65 ± 3°C for 4 hours,
.750 inch (19.1 mm) mandrel,
1.00 lb (454 g), 2.5 kV dielectric test
SHRINKAGE
200 ± 3°C for 1 hour,
.125 inch (3.18 mm) (maximum)
in 12 inches (305 mm)
FINISHED CABLE
(Test procedures per NEMA WC 27500, unless otherwise specified)
BLOCKING
200°C for 6 hours
CABLE LAY LENGTH
.75 inch (19.1 mm) (minimum),
1.25 inches (31.8 mm) (maximum)
CROSSLINKED VERIFICATION
300 ± 5°C for 6 hours,
6.00 inch (152 mm) mandrel
2nd SHIELD
.142
AWG 38,
FLAMMABILITY
3 seconds (maximum);
(3.61 mm)
Tin-Coated Copper,
(Method B of Spec 1200)
3 inches (76.2 mm) (maximum);
Optimized
no flaming of facial tissue
JACKET
ELONGATION
50% (minimum)
TENSILE STRENGTH
5000 lbf/in2 (34.5 N/mm2) (minimum)
JACKET FLAWS
JACKET
.158
SPARK TEST
1.0 kV (rms)
Radiation-Crosslinked,
(4.01 mm)
IMPULSE TEST
6.0 kV (peak)
Modified ETFE
JACKET THICKNESS
.008 inch (.203 mm) (nominal)
LOW TEMPERATURE-COLD BEND -55 ± 5°C for 4 hours,
6.00 inch (152 mm) mandrel
VOLTAGE WITHSTAND
1000 volts (rms) (minimum)
(DIELECTRIC)
WRAP
.002 inch (.051 mm) thick (nominal),
25% overlap (minimum)
The conductor AWG size and outer jacket color will be appended to
29.1 lbs/1000 ft. (43.3 kg/km) (maximum)
the part number. Unless otherwise specified, outer jacket color will WEIGHT
be white designated by a "-9" in accordance with MIL-STD-681,
CABLE IDENTIFICATION: Outer jacket shall be marked in contrasting color at 12
(e.g. 10614-24-9).
inch (305 mm) (nominal) intervals between marks as follows: "10614 RAYCHEM"
.125
(3.18 mm)
WRAP
Mu-Metal
Other codes and suffixes may be added to the part number, as
necessary, to capture any additional requirements imposed by the
purchase order.
ENGINEERING REFERENCE
TEMPERATURE RATING
150°C (maximum)
Users should evaluate the suitability of this product for their application. Specifications are subject to change without notice. TE Connectivity also reserves the
right to make changes in materials or processing, which do not affect compliance with any specification, without notification to Buyer.
Page 1 of 1
Cheminax, Raychem, TE Connectivity, and TE connectivity (logo) are trademarks.
Raychem Wire & Cable
501 Oakside Avenue
Redwood City, California 94063-3800
Phone: 1-800-522-6752 Fax: 1-650-361-6297
THIS SPECIFICATION SHEET TAKES PRECEDENCE OVER DOCUMENTS REFERENCED HEREIN.
REFERENCED DOCUMENTS SHALL BE OF THE ISSUE IN EFFECT ON DATE OF INVITATION FOR BID.
© 2009-2018 TE Connectivity Ltd. family of companies. All Rights Reserved.