A11329-001

URHT Ultra-high Ratio Heat-Shrink Tubing Table 1: Dimensions, inch (mm) PART DESCRIPTION (See Adhesive) URHT-200 URHT-300 (A) Min. Exp. ID (B) Max. Rec’d. ID (C) Ref. Rec’d. Wall Thickness 2.00 (51) 3.00 (76) 0.23 (6) 0.34 (9) 0.14 (3.5) 0.14 (3.5) Unrestricted Full Recovered Length (D) ± .25 (6) 3, 4, 6, 10 (76, 102, 152, 254) 3, 4, 6, 10 (76, 102, 152, 254) Material: Flame retarded, black, cross linked polyolefin. Adhesive (optional): Factory hot melt adhesive may be applied. Specify adhesive type number /42 (e.g. URHT-200/4/42-0). Customer Drawing Tyco Electronics Corporation 305 Constitution Drive Menlo Park, CA 94025 USA Raychem Tubing Tyco Electronics reserves the right to amend this drawing at any time. Users should evaluate the suitability of the product for their application. UNLESS OTHERWISE SPECIFIED DIMENSIONS ARE IN INCHES. METRIC DIMENSIONS ARE SHOWN IN BRACKETS. DRAWN BY: U.NGUYEN CAGE CODE: 06090 Org. Date: File name: 01/09/02 URHT-X.doc Title: URHT Ultra-High Ratio Heat-Shrink Tubing Document No. URHT-X Rev: Rev. Date: E November 13, 2007 SCALE: None ©2004-2007 Tyco Electronics Corporation. All rights reserved If this document is printed it becomes uncontrolled. Check for the latest revision. SIZE: SHEET: A 1 of 2 Table 2: Properties Property Tensile Strength Ultimate Elongation Specific Gravity Water Absorption Hardness Flammability Corrosion Resistance Low Temperature Flexibility 4 hours at –67 ± 2°F (-55 ± 1°C) Heat Resistance 168 hours at 347 ± 2°F (175 ± 1°C) Heat Shock 4 hours at 437 ± 5°F (225 ± 2°C) Elastic Memory Physical Dielectric Strength Volume Resistivity Chemical Fluid Resistance Electrical Operating Temperature Performance 1200 psi (8.3 Mpa) minimum 250% minimum 1.4 maximum 0.5% maximum 35 ± 5 Shore D Pass Pass Pass Test Method ASTM D-412 ASTM D-412 ASTM D-792 ASTM D-570 A ASTM D-2240 ASTM D-635 MIL-I-81765 MIL-I-81765 Ultimate elongation, 200% minimum Tensile strength, 1000 psi (6.9 Mpa) minimum No cracking, dripping or flowing MIL-I-81765 MIL-I-81765 275% minimum expansion to 4 inch (10 cm) of a fully recovered test specimen and 93% recovery of expanded specimen after oven conditioning for 1 minute at 302 ± 4°F (150 ± 2°C) 200 v/mil (7880 v/mm) minimum ASTM D-149 1012 ohm-cm minimum ASTM D-257 Ultimate elongation, 200% minimum MIL-I-81765 Tensile strength, 750 psi (5.2 Mpa) minimum -131 to + 275°F (-55 to +135° C) without adhesive Customer Drawing Rev. Date: Rev: Document No. November 13, 2007 E URHT-X If this document is printed it becomes uncontrolled. Check for the latest revision. Sheet: 2 of 2