Multi Layer Ferrite Power Beads Type CZP
1. General ■ Designed to reduce noise at high frequencies ■ Standard EIA Packages: 1J, 2A, 2B ■ Nickel barrier with solder overcoat for excellent solderability ■ Magnetically shielded
CERTIFIED
CERTIFIED
2. Dimensions
W L Solder Plating Ni Plating Silver Metallization d
Table 1 Dimensions - inches (mm) Part
1J (0603) 2A (0805) 2B (1206)
L
0.063±0.006 (1.60±0.15) 0.079±0.008 (2.00±0.20) 0.126±0.008 (3.20±0.20)
W
0.031±0.006 (0.80±0.15) 0.049±0.008 (1.25±0.20) 0.063±0.008 (1.60±0.20)
t
0.031±0.006 (0.80±0.15) 0.035±0.008 (0.90±0.20) 0.043±0.008 (1.10±0.20)
d
0.014±0.006 (0.36±0.15) 0.020±0.010 (0.51±0.25) 0.020±0.010 (0.51±0.25)
t
Terminations (Metallization Bands)
d
Electrodes
3. Type Designation The type designation shall be in the following for m: New Type
CZP
Type
2A
Size
1J 2A 2B
F
Permability Code
F P
T
Termination Material
T: Sn (Other termination styles available, contact factory for options)
TD
Packaging
TD: 7" Paper Tape (1J, 2A: 4,000 pcs/reel) TE: 7" Embossed Plastic (2B: 3,000 pcs/reel)
500
Impedence
2 significant figures + 1 multiplier
P
Tolerance
P: ±25%
PAGE 1 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e .
SS-220 R12 CZP
12/7/06
11:54 AM
Page 2
SS-220 R12
4. Standard Applications
Part Designation CZP1JFTTD300P CZP1JFTTD600P CZP1JFTTD121P CZP1JFTTD301P CZP2AFTTD300P CZP2AFTTD400P CZP2AFTTD450P CZP2AFTTD600P CZP2AFTTD800P CZP2AFTTD221P CZP2AFTTD301P CZP2AFTTD601P CZP2AFTTD102P CZP2BFTTE190P CZP2BFTTE260P CZP2BFTTE300P CZP2BFTTE310P CZP2BFTTE500P CZP2BFTTE650P CZP2BFTTE700P CZP2BFTTE800P CZP2BFTTE900P CZP2BFTTE101P CZP2BFTTE121P CZP2BPTTE700P CZP2BFTTE601P CZP2BPTTE101P CZP2BPTTE121P CZP2BPTTE601P Impedance @ 100MHz () 30 60 120 300 30 40 45 60 80 220 300 600 1000 19 26 30 31 50 65 70 80 90 100 120 70 600 100 120 600 DC Resistance Maximum () 0.03 0.04 0.10 0.10 0.015 0.03 0.025 0.04 0.05 0.15 0.20 Allowable DC Current Maximum (mA) 3000 2000 2000 3000 2000 3000 2000 -55°C to +125°C -55°C to +125°C Operating Temperature Range
1000
0.02
3000
0.025 0.03 2000 -55°C to +125°C 0.10 1000 3000 1000 3000 1500
0.20 0.03 0.04 0.10
PAGE 2 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e .
SS-220 R12 CZP
12/7/06
11:54 AM
Page 3
SS-220 R12
5. 0603 (1J) Graphs
PAGE 3 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e ci fi c a t io n s g ive n h e r e i n m a y b e ch a n g e d a t a n y ti m e w i th o u t p r i o r n o t i ce . P l e a s e c o n f ir m t e ch n ic a l s p e c i fi ca ti o n s b e fo r e yo u o r d e r a n d /o r u se .
SS-220 R12 CZP
12/7/06
11:54 AM
Page 4
SS-220 R12
5. 0805 (2A) Graphs
PAGE 4 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e .
SS-220 R12 CZP
12/7/06
11:54 AM
Page 5
SS-220 R12
5. 1206 (2B) Graphs
PAGE 5 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e .
SS-220 R12 CZP
12/7/06
11:54 AM
Page 6
SS-220 R12
5. 1206 (2B)Graphs (continued)
PAGE 6 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e .
SS-220 R12 CZP
12/7/06
11:54 AM
Page 7
SS-220 R12
5. Characteristics
Item Operating Temperature Storage Temperature Requirement -55°C ~ +125°C 40°C @ 70% Humidity Sealed plastic bags with desiccant shall be used to reduce the potential of oxidation on the ter minations during storage. Flux: 5-10 sec dip After Flux: Air dry for 15 sec Preheat: 150°C ±10°C Preheat Time: 60 sec Solder Temp: 260°C ±5°C Dip Time: 10 ±1 sec Flux: 5-10 sec dip After Flux: Air dry for 15 sec Solder Temp: 245°C ±5°C Dip Time: 5 ±0.5 sec The bead shall be subjected to the following 5 steps for the period of time shown below. The 5 steps constitute one (1) rotation. 4 rotations shall be carried out. 1) Flux: 5-10 sec 2) After Flux: Air dry for 15 sec 3) Solder Temp: 230°C ±5°C 4) Dip Time: 5 ±0.5 sec 5) Cool: Air cool for 60 seconds Conditions
Resistance to Solder Heat
Change in Impedance: Relative to value before test ±20%. Appearance: There shall be no cracking Solder Coverage: More than 75% of the terminal electrode shall be covered with solder.
Solderability
Solder Coverage: More than 95% of the termination shall be covered with solder.
Leach Resistance
Appearance: There shall be no visible signs of physical or mechanical damage (i.e. no cracks). Terminations: Ter mination must not be leached away for more than 5%.
Insulation Resistance Solvent Resistance
Insulation Resistance: Min 1G ohms Change in Impedance: Relative to value before test ±10%. Cleaning by: Washer: Ultrasonic washer (100W) Solvent: Isopropyl alcohol Time: 3 minutes Type 1J 2A 2B Type 1J 2A 2B W(kgf) 0.5 1.0 1.5 W(kgf) 1.4 1.8 2.3 Time 30 sec ±2 sec 30 sec ±2 sec 30 sec ±2 sec Time 60 sec 60 sec 60 sec
Terminal Strength (hanging test)
Appearance: The terminal electrode shall not break off, nor shall there be damage to the body.
Terminal Strength (push test)
Appearance: There shall be no evidence of mechanical degradations to terminals or body.
Bending Strength
Appearance: There shall be no physical or mechanical damage. Impedance: Relative to initial value before test ±10%.
Board: 90x40x1.6mm Bend: 1mm Time: 5 sec
PAGE 7 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e ci fi c a t io n s g ive n h e r e i n m a y b e ch a n g e d a t a n y ti m e w i th o u t p r i o r n o t i ce . P l e a s e c o n f ir m t e ch n ic a l s p e c i fi ca ti o n s b e fo r e yo u o r d e r a n d /o r u se .
SS-220 R12 CZP
12/7/06
11:54 AM
Page 8
SS-220 R12
5. Characteristics (continued)
Item Mechanical Shock Requirement Appearance: There shall be no physical or mechanical damage. Impedance: Relative to initial value before test ±10%. Impedance: Relative to initial value ±10%. Conditions Force: 50G Time: 11 msec There shall be 3 shocks in each of 6 directions (18 shocks total). Only endurance conditioning by sweeping shall be made. The entire frequency range from 10-2,000Hz and return to 10Hz in 20 minutes (this shall constitute one cycle). Amplitude: 1.5mm The test shall have a 15G peak and shall be applied for a period of 4 hours (12 cycles) in each of 3 mutually per pendicular directions (a total of 36 cycles within a total of 12 hours). Step 1-start 2-hold 3-transfer 4-hold 5-transfer Temperature -40°C ±2°C -40°C ±2°C — +105°C ±2°C — Time — 30 min ±5 min 0.5 min max. 30 min ±5 min 0.5 min max.
Vibration
Thermal Shock
Appearance: There shall be no physical or mechanical damage. Impedance: Relative to initial value ±20%. DCR: The DCR shall not exceed initial specified value. Testing of the par ts will be made at 0 hours, 250 hours and 500 hours. Before testing, the par ts shall be allowed to cool to room temperature for 24 hours.
Steps 1 thru 5 constitute one complete cycle and the test shall consist of a total of 500 cycles. Temperature: 85°C ±2°C Relative Humidity: 85% Time: 1,000 hours total Apply: 100% rated current
Load Humidity
Appearance: There shall be no physical or mechanical damage. Impedance: Relative to initial value ±15%. Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above.
Life Test
Appearance: There shall be no physical or mechanical damage Impedance: Relative to initial value ±15% Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above.
Temperature: 85°C ±2°C Time: 1,000 hours total Apply: 100% rated current
PAGE 8 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e .
SS-220 R12 CZP
12/7/06
11:54 AM
Page 9
SS-220 R12
6. Packaging Specifications KOA’s multilayer components are provided on tape-and-reel for use in pick-and-place machines. The reel size is 7 inch. 7. Dimensions - inches (mm)
Dimensions - inches (mm) Tape 1J 0603 2A 0805 2B 1206 A 0.075±0.002 (1.9±0.1) 0.093±0.002 (2.4±0.1) 0.138±0.002 (3.5±0.1) B 0.043±0.002 (1.1±0.1) 0.063±0.002 (1.6±0.1) 0.071±0.002 (1.8±0.1) W 0.318±0.002 (8.1±0.1) 0.318±0.002 (8.1±0.1) 0.318±0.002 (8.1±0.1) P1 0.157±0.004 (4.0±0.1) 0.157±0.004 (4.0±0.1) 0.157±0.004 (4.0±0.1) T1 0.043±0.002 (1.1±0.1) 0.046±0.002 (1.2±0.1) 0.071±0.002 (1.8±0.1)
Dimensions - inches (mm) Tape 1J 0603 2A 0805 2B 1206 7 (178) 0.827 (21) 0.079 (2.0) øa ød e
PAGE 9 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e .
SS-220 R12 CZP
12/7/06
11:54 AM
Page 10
SS-220 R12
9. Recommended PC Board Land Patterns - mm (inches)
Chip Size 1J (0603) 2A (0805) 2B (1206) L 2.6 (0.102) 3.0 (0.118) 4.4 (0.173) G 0.6 (0.023) 1.0 (0.039) 2.2 (0.087) H 0.8 (0.031) 1.0 (0.039) 1.4 (0.055)
G L H
10. Recommended Temperature Profiles for Soldering
Recommended Temperature Profile for Wave Soldering
Preheat 100 Seconds Max. 250°C Soldering 10 Seconds Max. Natural Cooling 250°C 200°C 150°C 60 Seconds Max. 150°C 60 Seconds Max.
Recommended Temperature Profile for Reflow Soldering
Preheat 100 Seconds Max. Soldering 10 Seconds Max. Natural Cooling
20 Seconds Max.
PAGE 10 OF 10 Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e .
很抱歉,暂时无法提供与“CZP2BFTTE190P”相匹配的价格&库存,您可以联系我们找货
免费人工找货