KOA SPEER ELECTRONICS, INC.
SS-224 R5
AHA 10/27/04
Multilayer Ferrite Chip Bead Array Type FBA
1. Scope of Application Noise suppression in signal I/O lines and other circuits that require multiple chip beads for noise suppression. 1.1 Applications
I I
CERTIFIED
Computers Peripherals
I I
Telecommunications equipment Data communications
2. Features The Multilayer Ferrite Chip Bead Array retains all the features of Multilayer Ferrite Chip Beads. In addition, it provides multiple circuits in a single package, which reduce the required land space on PCB and reduce the cost for assembly. 3. Dimension and Structure
a W t Protective Coating Solder Plating L p b
Type
(Inch Size Code)
L .126±.008 (3.2±0.2)
W .063±.008 (1.6±0.2)
Dimensions inches (mm) t a .031±.008 (0.8±0.2) .014±.008 (0.35±0.2)
b .012±.008 (0.3±0.2)
p .031±.008 (0.8±0.2)
1J (0603)
3.1 Circuit
PAGE 1 OF 8 Bolivar Drive
I
P.O. Box 547
I
Bradford, PA 16701
I
USA
I
814-362-5536
I
Fax 814-362-8883
I
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
4. Ordering and Specifying Information*
FBA
Type
1J
Size
1J (0603)
4
Circuits
Number of Circuits
A
Characteristics
A: Standard B: High Speed
T
Termination Material
T: Sn L: SnPb
TE
Packaging
TE: 7" Embossed Plastic 3000 pcs/reel
300
Impedance
2 significant figure + 1 multipler Ex: 300 = 30Ω
P
Tolerance
P: ±25%
* Please note: KSE’s part numbers do not contain any spaces or hyphens.
5. Standard Applications Ordering Code FBA1J4ATE300P FBA1J4ATE600P FBA1J4ATE121P FBA1J4ATE221P FBA1J4ATE301P FBA1J4ATE601P FBA1J4ATE102P FBA1J4BTE100P FBA1J4BTE220P FBA1J4BTE470P FBA1J4BTE600P FBA1J4BTE121P FBA1J4BTE221P FBA1J4BTE471P FBA1J4BTE601P Impedance @ 100MHz Ω 30 60 120 220 300 600 1,000 10 22 47 60 120 220 470 600 Maximum DC Resistance Ω 0.1 0.25 0.3 0.3 0.4 0.5 0.7 0.15 0.25 0.3 0.3 0.5 0.55 0.55 0.65 Allowable DC Current (mA) 200 400 350 250 250 100 200 200 200 150 350 100 100 100 100 -55°C to 125°C Operating Temperature
PAGE 2 OF 8 Bolivar Drive
I
P.O. Box 547
I
Bradford, PA 16701
I
USA
I
814-362-5536
I
Fax 814-362-8883
I
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
6. Graphs*
*
|Z| XL R
PAGE 3 OF 8
I
Bolivar Drive
I
P.O. Box 547
Bradford, PA 16701
I
USA
I
814-362-5536
I
Fax 814-362-8883
I
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
6. Graphs* (continued)
*
|Z| XL R
PAGE 4 OF 8
I
Bolivar Drive
I
P.O. Box 547
Bradford, PA 16701
I
USA
I
814-362-5536
I
Fax 814-362-8883
I
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
6. Graphs* (continued)
*
|Z| XL R
PAGE 5 OF 8
I
Bolivar Drive
I
P.O. Box 547
Bradford, PA 16701
I
USA
I
814-362-5536
I
Fax 814-362-8883
I
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
6. Packaging Specifications KOA’s multilayer components are provided on tape-and-reel for use in pick-and-place machines. The reel size is 7 inch. 7. Dimensions - inches (mm)
Do Po
P2
t
Tape 1J4
Ao
Bo
Ko
E F Bo
0.071±0.002 0.138±0.002 0.048±0.002 (1.8±0.1) (3.5±0.1) (1.2±0.1)
W
Tape 1J4
E
F
W
D1 P1 Ao Ko
0.069±0.004 0.138±0.002 0.318±0.002 (1.75±0.10) (3.50±.005) (8.1±0.1)
Tape 1J4
P1
Po
P2
Do
D1
t 0.009±0.001 (0.23±0.02)
0.157±0.004 0.157±0.004 0.079±0.002 0.059±0.004 0.039 min. (4.0±0.1) (4.0±0.1) (2.00±0.05) (1.5+0.1/-0.0) (1.0 min.)
8. Chip Quantities Per Reel Chip Size 1J4 Parts on 7 inch (178mm) Reel 3,000
9. Characteristics
Item Operating Temperature Storage Temperature Requirement -55°C ~ +125°C 40°C @ 70% Humidity Sealed plastic bags with desiccant shall be used to reduce the potential of oxidation on the terminations during storage. Flux: 5-10 sec dip After Flux: Air dry for 15 sec Preheat: 150°C ±10°C Preheat Time: 60 sec Solder Temp: 260°C ±5°C Dip Time: 10 ±1 sec Conditions
Resistance to Solder Heat
Change in Impedance: Relative to value before test ±20%. Appearance: There shall be no cracking Solder Coverage: More than 75% of the terminal electrode shall be covered with solder.
PAGE 6 OF 8 Bolivar Drive
I
P.O. Box 547
I
Bradford, PA 16701
I
USA
I
814-362-5536
I
Fax 814-362-8883
I
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
9. Characteristics (continued)
Item Solderability Requirement Solder Coverage: More than 95% of the termination shall be covered with solder. Conditions Flux: 5-10 sec dip After Flux: Air dry for 15 sec Solder Temp: 245°C ±5°C Dip Time: 5 ±0.5 sec The bead shall be subjected to the following 5 steps for the period of time shown below. The 5 steps constitute one (1) rotation. 4 rotations shall be carried out. 1) Flux: 5-10 sec 2) After Flux: Air dry for 15 sec 3) Solder Temp: 230°C ±5°C 4) Dip Time: 5 ±0.5 sec 5) Cool: Air cool for 60 seconds
Leach Resistance
Appearance: There shall be no visible signs of physical or mechanical damage (i.e. no cracks) Terminations: Termination must not be leached away for more than 5%.
Insulation Resistance Solvent Resistance
Insulation Resistance: Min 1G ohms Change in Impedance: Relative to value before test ±10%. Cleaning by: Washer: Ultrasonic washer (100W) Solvent: Isopropyl alcohol Time: 3 minutes Type 1206 Type 1206 W(kgf) 1.5 W(kgf) 2.3 Time 30 sec ±2 sec Time 60 sec
Terminal Strength (hanging test) Terminal Strength (push test) Bending Strength
Appearance: The terminal electrode shall not break off, nor shall there be damage to the body. Appearance: There shall be no evidence of mechanical degradations to terminals or body. Appearance: There shall be no physical or mechanical damage Impedance: Relative to initial value before test ±10% Appearance: There shall be no physical or mechanical damage Impedance: Relative to initial value before test ±10% Impedance: Relative to initial value ±10%
Board: 90x40x1.6mm Bend: 1mm Time: 5 sec
Mechanical Shock
Force: 50G Time: 11 msec There shall be 3 shocks in each of 6 directions (18 shocks total). Only endurance conditioning by sweeping shall be made. The entire frequency range from 10-2,000Hz and return to 10Hz in 20 minutes (this shall constitute one cycle). Amplitude: 1.5mm The test shall have a 15G peak and shall be applied for a period of 4 hours (12 cycles) in each of 3 mutually perpendicular directions (a total of 36 cycles within a total of 12 hours).
Vibration
PAGE 7 OF 8 Bolivar Drive
I
P.O. Box 547
I
Bradford, PA 16701
I
USA
I
814-362-5536
I
Fax 814-362-8883
I
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
9. Characteristics (continued)
Item Thermal Shock Requirement Appearance: There shall be no physical or mechanical damage. Impedance: Relative to initial value ±20%. DCR: The DCR shall not exceed initial specified value. Testing of the parts will be made at 0 hours, 250 hours and 500 hours. Before testing the parts shall be allowed to cool to room temperature for 24 hours. Load Humidity Appearance: There shall be no physical or mechanical damage Impedance: Relative to initial value ±15% Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above. Life Test Appearance: There shall be no physical or mechanical damage Impedance: Relative to initial value ±15% Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above. Temperature: 85°C ±2°C Time: 1,000 hours total Apply: 100% rated current Conditions Step 1-start 2-hold 3-transfer 4-hold 5-transfer Temperature -40°C ±2°C -40°C ±2°C — +105°C ±2°C — Time — 30 min ±5 min 0.5 min max. 30 min ±5 min 0.5 min max.
Steps 1 thru 5 constitute one complete cycle and the test shall consist of a total of 500 cycles. Temperature: 85°C ±2°C Relative Humidity: 85% Time: 1,000 hours total Apply: 100% rated current
10. Recommended PC Board Land Patterns - inches (mm)
Soldering Pad BW A E L Chip Component C Chip Component Size Size L W 1206 (3216) .126 (3.2) .063 (1.6) A B C E
.030 .120 .016 .031 (0.762) (3.048) (0.406) (0.787)
PAGE 8 OF 8 Bolivar Drive
I
P.O. Box 547
I
Bradford, PA 16701
I
USA
I
814-362-5536
I
Fax 814-362-8883
I
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.