MCL2BHTTER47

SS-223 R9 12/6/06 11:26 AM Page 1 SS-223 R9 AHA 12/06/06 Multi Layer Ferrite Inductors Type MCL 1. General ■ Monolithic structure for closed magnetic path eliminates CERTIFIED CERTIFIED crosstalk and provides high reliability in a wide range of temperature and humidity ranges ■ Standard EIA packages: 1J, 2A, 2B ■ Nickel barrier with solder overcoat for excellent solderability ■ Magnetically shielded 2. 2.1 Dimensions L W Solder Plating Ni Plating Silver Metallization d Size Code 1J (0603) 2A (0805) 2B (1206) L .063±.006 (1.6±0.15) .079±.008 (2.0±0.2) .126±.008 (3.2±0.2) W .031±.006 (0.8±0.15) .049±.008 (1.25±0.2) .063±.008 (1.6±0.2) t .031±.006 (0.8±0.15) .035±.008 (0.9±0.2) .043±.008 (1.1±0.2) d .014±.006 (0.36±0.15) .02±.01 (0.51±0.25) .02±.01 (0.51±0.25) t Terminations (Metallization Bands) d Electrodes 3. Ordering and Specifying Information* MCL Type 1J Size 1J 2A 2B H Material Per meability Code: H J T Termination Material T: Sn (Other termination styles available, contact factory for options) TE Packaging TD: 7" Paper Tape (1J - 4,000 pcs/reel; 2A - 0.047µH - 2.2µH = 4,000 pcs/reel) TE: 7" Embossed Plastic (2A - 2.7µH - 10µH = 3,000 pcs/reel; 2B - 3,000 pcs/reel) R10 Nominal Inductance 047 = .047µH R10 = .100µH J Tolerance K: ±10% M: ±20% * Please note: KSE’s part numbers do not contain any spaces or hyphens. 4. Standard Applications Part Designation MCL1JHTTD047M MCL1JHTTD068M MCL1JHTTD082M MCL1JHTTDR10* MCL1JHTTDR12* MCL1JHTTDR15* MCL1JHTTDR18* MCL1JHTTDR22* MCL1JHTTDR27* Inductance L (µH) 0.047 0.068 0.082 0.10 0.12 0.15 0.18 0.22 0.27 Minimum Q L.Q. Test Frequency (MHz) 50 Self Resonant Frequency Typical (MHz) 260 250 245 240 205 180 165 150 136 DC Resistance Maximum (Ω) 0.30 -55°C to +125°C Allowable DC Current Maximum (mA) Operating Temperature Range 10 0.50 0.60 0.80 50 15 25 * Add tolerance character (K, M) - Other tolerances available upon request PAGE 1 OF 6 814-362-5536 ■ Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ Fax 814-362-8883 ■ www.koaspeer.com S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e . SS-223 R9 12/6/06 11:26 AM Page 2 SS-223 R9 4. Standard Applications (continued) Part Designation MCL1JHTTDR33* MCL1JHTTDR39* MCL1JHTTDR47* MCL1JHTTDR56* MCL1JHTTDR68* MCL1JHTTDR82* MCL1JJTTD1R0* MCL1JJTTD1R2* MCL1JJTTD1R5* MCL1JJTTD1R8* MCL1JJTTD2R2* MCL1JJTTD2R7* MCL1JJTTD3R3* MCL1JJTTD3R9* MCL1JJTTD4R7* MCL1JJTTD5R6* MCL1JJTTD6R8* MCL1JJTTD8R2* MCL1JJTTD100* MCL1JJTTD120* MCL2AHTTD047M MCL2AHTTD068M MCL2AHTTD082M MCL2AHTTDR10* MCL2AHTTDR12* MCL2AHTTDR15* MCL2AHTTDR18* MCL2AHTTDR22* MCL2AHTTDR27* MCL2AHTTDR33* MCL2AHTTDR39* MCL2AHTTDR47* MCL2AHTTDR56* MCL2AHTTDR68* MCL2AHTTDR82* MCL2AJTTD1R0* MCL2AJTTD1R2* MCL2AJTTD1R5* MCL2AJTTD1R8* MCL2AJTTD2R2* MCL2AJTTE2R7* MCL2AJTTE3R3* MCL2AJTTE3R9* MCL2AJTTE4R7* Inductance L (µH) 0.33 0.39 0.47 0.56 0.68 0.82 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 0.047 0.068 0.082 0.10 0.12 0.15 0.18 0.22 0.27 0.33 0.39 0.47 0.56 0.68 0.82 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 Minimum Q L.Q. Test Frequency (MHz) Self Resonant Frequency Typical (MHz) 125 110 105 95 90 85 75 65 60 55 50 45 40 35 33 22 20 18 17 15 320 280 255 235 220 200 185 170 150 145 135 125 115 105 100 75 65 60 55 50 45 41 38 35 DC Resistance Maximum (Ω) 0.85 1.00 1.35 1.55 1.70 2.10 0.60 0.80 0.95 1.15 1.35 1.55 1.70 2.10 1.55 1.70 2.10 1.85 2.10 0.20 Allowable DC Current Maximum (mA) Operating Temperature Range 15 25 35 25 -55°C to +125°C 15 10 35 4 5 30 2 3 15 50 300 0.30 0.40 0.50 0.55 0.65 0.75 0.80 1.00 0.40 0.50 0.60 0.65 0.75 0.80 0.90 1.00 200 -55°C to +125°C 20 250 25 25 150 50 45 10 30 * Add tolerance character (K, M) - Other tolerances available upon request PAGE 2 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e . SS-223 R9 12/6/06 11:26 AM Page 3 SS-223 R9 4. Standard Applications (continued) Part Designation MCL2AJTTE5R6* MCL2AJTTE6R8* MCL2AJTTE8R2* MCL2AJTTE100* MCL2BHTTE047M MCL2BHTTE068M MCL2BHTTER10* MCL2BHTTER12* MCL2BHTTER15* MCL2BHTTER18* MCL2BHTTER22* MCL2BHTTER27* MCL2BHTTER33* MCL2BHTTER39* MCL2BHTTER47* MCL2BHTTER56* MCL2BHTTER68* MCL2BHTTER82* MCL2BJTTE1R0* MCL2BJTTE1R2* MCL2BJTTE1R5* MCL2BJTTE1R8* MCL2BJTTE2R2* MCL2BJTTE2R7* MCL2BJTTE3R3* MCL2BJTTE3R9* MCL2BJTTE4R7* MCL2BJTTE5R6* MCL2BJTTE6R8* MCL2BJTTE8R2* MCL2BJTTE100* MCL2BJTTE120* MCL2BJTTE150* MCL2BJTTE180* MCL2BJTTE220* MCL2BJTTE270* MCL2BJTTE330* Inductance L (µH) 5.6 6.8 8.2 10 0.047 0.068 0.10 0.12 0.15 0.18 0.22 0.27 0.33 0.39 0.47 0.56 0.68 0.82 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 Minimum Q L.Q. Test Frequency (MHz) 4 2 50 Self Resonant Frequency Typical (MHz) 32 29 26 24 320 280 235 220 200 185 170 150 145 135 125 115 105 100 75 65 60 55 50 45 41 38 35 32 29 26 24 22 19 18 16 14 13 DC Resistance Maximum (Ω) 0.90 1.00 1.10 1.15 0.15 0.25 0.30 0.40 0.50 0.60 0.50 0.60 0.70 0.80 0.90 0.40 0.50 250 Allowable DC Current Maximum (mA) Operating Temperature Range -55°C to +125°C 50 15 300 20 25 200 25 150 100 -55°C to +125°C 45 10 0.60 50 0.70 0.80 0.85 0.90 1.00 1.05 0.70 0.90 1.05 5 4 50 2 25 15 30 1 0.4 * Add tolerance character (K, M) - Other tolerances available upon request PAGE 3 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com S p e ci fi c a t io n s g ive n h e r e i n m a y b e ch a n g e d a t a n y ti m e w i th o u t p r i o r n o t i ce . P l e a s e c o n f ir m t e ch n ic a l s p e c i fi ca ti o n s b e fo r e yo u o r d e r a n d /o r u se . SS-223 R9 12/6/06 11:26 AM Page 4 SS-223 R9 5. Characteristics Item Operating Temperature Storage Temperature Requirement -25°C ~ +85°C 40°C @ 70% Humidity Sealed plastic bags with desiccant shall be used to reduce the potential of oxidation on the ter minations during storage. Flux: 5-10 sec dip After Flux: Air dry for 15 sec Preheat: 150°C ±10°C Preheat Time: 60 sec Solder Temp: 260°C ±5°C Dip Time: 10 ±1 sec Flux: 5-10 sec dip After Flux: Air dry for 15 sec Solder Temp: 245°C ±5°C Dip Time: 5 ±0.5 sec The bead shall be subjected to the following 5 steps for the period of time shown below. The 5 steps constitute one (1) rotation. 4 rotations shall be carried out. 1) Flux: 5-10 sec 2) After Flux: Air dry for 15 sec 3) Solder Temp: 230°C ±5°C 4) Dip Time: 5 ±0.5 sec 5) Cool: Air cool for 60 seconds Conditions Resistance to Solder Heat Change in Inductance: Relative to value before test ±20%. Appearance: There shall be no cracking Solder Coverage: More than 75% of the terminal electrode shall be covered with solder. Solder Coverage: More than 95% of the termination shall be covered with solder. Solderability Leach Resistance Appearance: There shall be no visible signs of physical or mechanical damage (i.e. no cracks) Terminations: Ter mination must not be leached away for more than 5%. Insulation Resistance Solvent Resistance Insulation Resistance: Min 1G ohms Change in Inductance: Relative to value before test ±10%. Cleaning by: Washer: Ultrasonic washer (100W) Solvent: Isopropyl alcohol Time: 3 minutes Type 1J (0603) 2A (0805) 2B (1206) Type 1J (0603) 2A (0805) 2B (1206) W(kgf) 0.5 1.0 1.5 W(kgf) 1.4 1.8 2.3 Time 30 sec ±2 sec 30 sec ±2 sec 30 sec ±2 sec Time 60 sec 60 sec 60 sec Terminal Strength (hanging test) Appearance: The terminal electrode shall not break off, nor shall there be damage to the body. Terminal Strength (push test) Appearance: There shall be no evidence of mechanical degradations to terminals or body. Bending Strength Appearance: There shall be no physical or mechanical damage Inductance: Relative to initial value before test ±10% Board: 90x40x1.6mm Bend: 1mm Time: 5 sec PAGE 4 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e . SS-223 R9 12/6/06 11:26 AM Page 5 SS-223 R9 5. Characteristics (continued) Item Mechanical Shock Requirement Appearance: There shall be no physical or mechanical damage Inductance: Relative to initial value before test ±10% Inductance: Relative to initial value ±10% Conditions Force: 50G Time: 11 msec There shall be 3 shocks in each of 6 directions (18 shocks total). Only endurance conditioning by sweeping shall be made. The entire frequency range from 10-2,000 Hz and retur n to 10 Hz in 20 minutes (this shall constitute one cycle). Amplitude: 1.5mm The test shall have a 15G peak and shall be applied for a period of 4 hours (12 cycles) in each of 3 mutually per pendicular directions (a total of 36 cycles within a total of 12 hours). Step 1-start 2-hold 3-transfer 4-hold 5-transfer Temperature -40°C ±2°C -40°C ±2°C — +105°C ±2°C — Time — 30 min ±5 min 0.5 min max. 30 min ±5 min 0.5 min max. Vibration Thermal Shock Appearance: There shall be no physical or mechanical damage. Inductance: Relative to initial value ±20%. DCR: The DCR shall not exceed initial specified value. Testing of the par ts will be made at 0 hours, 250 hours and 500 hours. Before testing the par ts shall be allowed to cool to room temperature for 24 hours. Steps 1 thru 5 constitute one complete cycle and the test shall consist of a total of 500 cycles. Temperature: 85°C ±2°C Relative Humidity: 85% Time: 1,000 hours total Apply: 100% rated current Load Humidity Appearance: There shall be no physical or mechanical damage Inductance: Relative to initial value ±15% Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above. Life Test Appearance: There shall be no physical or mechanical damage Inductance: Relative to initial value ±15% Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above. Temperature: 85°C ±2°C Time: 1,000 hours total Apply: 100% rated current 6. Packaging Specifications KOA’s multi layer components are provided on tape-and-reel for use in pick-and-place machines. The reel size is 7 inch. PAGE 5 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e . SS-223 R9 12/6/06 11:26 AM Page 6 SS-223 R9 7. Dimensions - inches (mm) Tape 1J 2A 2B Ao Bo Ko E F Do Po P2 t 0.043±0.002 0.075±0.002 0.043±0.002 (1.1±0.1) (1.9±0.1) (1.1±0.1) 0.063±0.002 0.093±0.002 0.046±0.002 (1.6±0.1) (2.4±0.1) (1.2±0.1) 0.071±0.002 0.138±0.002 0.048±0.002 (1.8±0.1) (3.5±0.1) (1.2±0.1) W Bo D1 P1 Ao Ko Tape 1J 2A 2B E F W P1 Po P2 Do D1 t 0.009±0.001 (0.23±0.02) 0.069±0.004 0.138±0.002 0.318±0.002 0.157±0.004 0.157±0.004 0.079±0.002 0.059±0.004 0.039 min. (1.75±0.10) (3.50±.005) (8.1±0.1) (4.0±0.1) (4.0±0.1) (2.00±0.05) (1.5+0.1/-0.0) (1.0 min.) 8. Chip Quantities Per Reel Chip Size 1J 2A 2B Par ts on 7 inch (178mm) Reel 4,000 * 2,000/4,000 3,000 9. Recommended PC Board Land Patterns - inches (mm) Chip Size 1J 2A 2B L 0.102 (2.6) 0.118 (3.0) 0.173 (4.4) G 0.022 (0.55) 0.026 (0.66) 0.059 (1.5) H 0.037 (0.94) 0.057 (1.45) 0.071 (1.8) * MCL0805: 2.7µH ~ 12µH = 2K 0.047µH ~ 2.2µH = 4K G L H 10. Recommended Temperature Profiles for Soldering Recommended Temperature Profile Recommended Temperature Profile forforave Soldering W Wave Soldering Preheat 100 Preheat 100 Seconds Max. Seconds Max. 250°C 250°C Soldering Soldering 10 Seconds Max. 10 Seconds Max. Natural Natural Cooling Cooling 230°C 230°C 200°C 200°C 150°C 150°C 60 Seconds Max. 60 Seconds Max. 150°C 150°C Recommended Temperature Profile Recommended Temperature Profile forfor Reflow Soldering Reflow Soldering Preheat 100 Preheat 100 Seconds Max. Seconds Max. Soldering Soldering 10 Seconds Max. 10 Seconds Max. Natural Natural Cooling Cooling 20 Seconds Max. 20 Seconds Max. 60 Seconds Max. 60 Seconds Max. PAGE 6 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com S p e c i f i c a t i o n s g iv e n h e r e i n m ay b e c h a n g e d a t a n y t i m e w i t h o u t p r i o r n o t i c e . P l e a s e c o n f ir m t e c h n i c a l s p e c if i c a t i o n s b e f o r e y o u o r d e r a n d / o r u s e .