OD-880W

HIGH-POWER GaAlAs IR EMITTERS GLASS .006 HIGH MAX .015 1.00 MIN. OD-880W FEATURES • High reliability liquid-phase epitaxially grown GaAlAs • 880nm peak emission for optimum matching with ODD-45W photodiode • Wide range of linear power output • Hermetically sealed TO-46 package • Wide emission angle to cover a large area ANODE (CASE) .209 .220 .183 .152 .187 .156 .100 .017 .098 .112 All surfaces are gold plated. Dimensions are nominal values in inches unless otherwise specified. Window caps are welded to the case. 13 .041 20 .036 CATHODE PARAMETERS MB E ELECTRO-OPTICAL CHARACTERISTICS AT 25°C R 45° .143 .150 TEST CONDITIONS Total Power Output, Po IF = 100mA Radiant Intensity, Ie TYP 18 20 mW 16 mW/sr 880 nm 80 nm CE Peak Emission Wavelength, λP MIN Spectral Bandwidth at 50%, Δλ IF = 50mA Half Intensity Beam Angle, θ 70 IF = 100mA Reverse Breakdown Voltage, VR IR = 10μA DE Forward Voltage, VF 5 Rise Time FE Fall Time UNITS Deg 80 1.55 VR = 0V Capacitance, C MAX 1.9 Volts 30 Volts 17 pF 0.5 μsec 0.5 μsec ABSOLUTE MAXIMUM RATINGS AT 25°C CASE 190mW LI Power Dissipation1 Continuous Forward Current 100mA Peak Forward Current (10μs, 400Hz)2 OF 3A Reverse Voltage 5V Lead Soldering Temperature (1/16" from case for 10sec) 260°C D 1Derate per Thermal Derating Curve above 25°C 2Derate linearly above 25°C EN THERMAL PARAMETERS Storage and Operating Temperature Range -55°C TO 100°C Maximum Junction Temperature 100°C Thermal Resistance, RTHJA1 400°C/W Typical Thermal Resistance, RTHJA2 135°C/W Typical 1Heat transfer minimized by measuring in still air with minimum heat conducting through leads 2Air circulating at a rapid rate to keep case temperature at 25°C 1260 Calle Suerte, Camarillo, California 93012 Phone: (805) 499-0335, Fax: (805) 499-8108 Email: sales@optodiode.com, Website: www.optodiode.com Revision February 26, 2013 HIGH-POWER GaAlAs IR EMITTERS 10 PEAK FORWARD CURRENT, Ip (amps) POWER DISSIPATION (mW) INFINITE HEAT SINK 160 140 NO HEAT SINK 120 100 80 60 40 20 50 75 AMBIENT TEMPERATURE (°C) t = 500μs 100 T IF = 50mA 80 70 TCASE = 25°C NO PRE BURN-IN PERFORMED RELATIVE POWER OUTPUT FE 2 1 100 40 20 0 –100 105 DE 104 LI FORWARD CURRENT, IF (amps) 3 10 60 –80 –60 –40 –20 0 20 40 BEAM ANGLE, θ(deg) 60 80 100 POWER OUTPUT vs TEMPERATURE FORWARD I-V CHARACTERISTICS 4 1 DUTY CYCLE, D (%) 80 CE IF = 100mA 50 103 STRESS TIME, (hrs) 0.1 RADIATION PATTERN 90 102 t T Ip 100 IF = 20mA 101 D= t 0.1 DEGRADATION CURVE 60 t = 100μs 1 MB ER 100 25 t = 10μs 0.01 0.01 RELATIVE POWER OUTPUT (%) 0 RELATIVE POWER OUTPUT (%) TYPICAL CHARACTERISTICS MAXIMUM RATINGS 180 MAXIMUM PEAK PULSE CURRENT 13 THERMAL DERATING CURVE 20 200 OD-880W 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0.7 OF 0.6 0.5 –50 0 0 1 2 3 4 FORWARD VOLTAGE, VF (volts) 5 6 75 100 1,000 D 80 POWER OUTPUT, Po (mW) RELATIVE POWER OUTPUT (%) 0 25 50 AMBIENT TEMPERATURE (°C) POWER OUTPUT vs FORWARD CURRENT SPECTRAL OUTPUT 100 EN –25 60 40 100 10 20 0 750 800 850 900 WAVELENGTH, λ(nm) 950 1,000 1 10 DC PULSE 10μs, 100Hz 100 1,000 FORWARD CURRENT, IF (mA) 10,000 1260 Calle Suerte, Camarillo, California 93012 Phone: (805) 499-0335, Fax: (805) 499-8108 Email: sales@optodiode.com, Website: www.optodiode.com Revision February 26, 2013