SPECIFICATION
Supplier : Samsung electro-mechanics
Samsung P/N : CL10A226MR8NQDC
Product : Multi-layer Ceramic Capacitor
Description :
CAP, 22㎌, 4V, ±20%, X5R, 0603
A. Samsung Part Number
① Series
② Size
CL
10
A
226
M
R
8
N
Q
D
C
①
②
③
④
⑤
⑥
⑦
⑧
⑨
⑩
⑪
Samsung Multi-layer Ceramic Capacitor
0603 (inch code)
③ Dielectric
X5R
④ Capacitance
22 ㎌
±20 %
⑤ Capacitance
L: 1.6 ± 0.15
tolerance
4V
⑥ Rated Voltage
⑦ Thickness
0.8 ± 0.15 mm
mm
0.8 ± 0.15 mm
W:
⑧ Inner electrode
Ni
Termination
Cu
Plating
Sn 100%
(Pb Free)
⑨ Product
0603 Size dimension spec
⑩ Special
Dc-bias aging
⑪ Packaging
Cardboard Type,7"reel(4,000ea)
B. Samsung Reliability Test and Judgement condition
Performance
0.5±0.1Vrms
More than 50Mohm㎌
Rated Voltage
60~120 sec.
Appearance
No abnormal exterior appearance
Withstanding
No dielectric breakdown or
Visual inspection
250% of the rated voltage
Voltage
mechanical breakdown
Temperature
X5R
Characteristics
Adhesive Strength
(From -55℃ to 85℃, Capacitance change should be within ±15%)
No peeling shall be occur on the
500gF, for 10±1 sec.
of Termination
terminal electrode
Bending Strength
Capacitance change :
Tan δ (DF)
Insulation
Within specified tolerance
Test condition
120㎐±20%
Capacitance
0.1 max.
Resistance
within ±12.5%
Bending to the limit (1mm)
with 1.0mm/sec.
Solderability
More than 75% of terminal surface
SnAg3.0Cu0.5 solder
is to be soldered newly
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to
Capacitance change :
Soldering heat
Tan δ, IR : initial spec.
within ±7.5%
Solder pot : 270±5℃, 10±1sec.
Performance
Vibration Test
Capacitance change :
within ±5%
Test condition
Amplitude : 1.5mm
Tan δ, IR : initial spec.
From 10㎐ to 55㎐ (return : 1min.)
Moisture
Capacitance change :
2hours 3 direction (x, y, z)
With rated voltage
Resistance
Tan δ : 0.25 max
IR
40±2℃, 90~95%RH, 500 +12/-0 hours
: More than 8.8㏁·㎌
High Temperature
Capacitance change :
Resistance
Tan δ : 0.25 max
IR
within ±12.5%
within ±12.5%
With 100%
of the rated voltage
Max. operating temperature
: More than 17.7㏁·㎌
1000+48/-0 hours
Temperature
Capacitance change :
Cycling
Tan δ, IR : initial spec.
within ±10%
1 cycle condition
Min. operating temperature
25℃
→
25℃
→
Max. operating temperature →
5 cycles test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.