CL21X475MAQNNNE

SPECIFICATION  Supplier : Samsung electro-mechanics  Samsung P/N : CL21X475MAQNNNE  Product : Multi-layer Ceramic Capacitor  Description : CAP, 4.7㎌, 25V, ±20%, X6S, 0805 A. Samsung Part Number ① Series ② Size CL 21 X 475 M A Q N N N E ① ② ③ ④ ⑤ ⑥ ⑦ ⑧ ⑨ ⑩ ⑪ Samsung Multi-layer Ceramic Capacitor 0805 (inch code) ③ Dielectric X6S ④ Capacitance 4.7 ㎌ ±20 % ⑤ Capacitance L: 2.0 ± 0.15 tolerance 25 V ⑥ Rated Voltage ⑦ Thickness 1.25 ± 0.15 mm mm 1.25 ± 0.15 mm W: ⑧ Inner electrode Ni Termination Cu Plating Sn 100% (Pb Free) ⑨ Product Normal ⑩ Special Reserved for future use ⑪ Packaging Embossed Type, 7"reel(2,000ea) B. Samsung Reliability Test and Judgement condition Performance 1.0±0.2Vrms More than 100Mohm㎌ Rated Voltage 60~120 sec. Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Visual inspection 250% of the rated voltage Voltage mechanical breakdown Temperature X6S Characteristics Adhesive Strength (From -55℃ to 105℃, Capacitance change should be within ±22%) No peeling shall be occur on the 500gF, for 10±1 sec. of Termination terminal electrode Bending Strength Capacitance change : Tan δ (DF) Insulation Within specified tolerance Test condition 1㎑±10% Capacitance 0.1 max. Resistance within ±12.5% Bending to the limit (1mm) with 1.0mm/sec. Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 245±5℃, 3±0.3sec. (preheating : 80~120℃ for 10~30sec.) Resistance to Capacitance change : Soldering heat Tan δ, IR : initial spec. within ±7.5% Solder pot : 270±5℃, 10±1sec. Performance Vibration Test Capacitance change : within ±10% Test condition Amplitude : 1.5mm Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.) Moisture Capacitance change : 2hours  3 direction (x, y, z) With rated voltage Resistance Tan δ : 0.2 max IR 40±2℃, 90~95%RH, 500 +12/-0 hour : More than 12.5㏁·㎌ High Temperature Capacitance change : Resistance Tan δ : 0.2 max IR within ±12.5% within ±12.5% With 100% of the rated voltage Max. operating temperature : More than 25㏁·㎌ 1000+48/-0 hour Temperature Capacitance change : Cycling Tan δ, IR : initial spec. within ±15% 1 cycle condition Min. operating temperature 25℃ → 25℃ → Max. operating temperature → 5 cycles test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue.