SPECIFICATION
Supplier : Samsung electro-mechanics
Samsung P/N : CL31X106MOCLNNC
Product : Multi-layer Ceramic Capacitor
Description :
CAP, 10㎌, 16V, ±20%, X6S, 1206
A. Samsung Part Number
① Series
② Size
③ Dielectric
④ Capacitance
⑤ Capacitance
CL
31
X
106
M
O
C
L
N
N
C
①
②
③
④
⑤
⑥
⑦
⑧
⑨
⑩
⑪
Samsung Multi-layer Ceramic Capacitor
1206 (inch code)
L: 3.2 ± 0.2
10 ㎌
±20 %
tolerance
⑦ Thickness
16 V
0.85 ± 0.1
1.6 ± 0.2
W:
mm
mm
Low profile
Ni
⑧ Thickness division
Inner electrode
X6S
⑥ Rated Voltage
mm
Termination
Cu
Plating
Sn 100%
(Pb Free)
⑨ Product
Normal
⑩ Special
Reserved for future use
⑪ Packaging
Cardboard Type, 7" reel(4,000ea)
B. Samsung Reliability Test and Judgement condition
Performance
1.0±0.2Vrms
More than 100Mohm㎌
Rated Voltage
60~120 sec.
Appearance
No abnormal exterior appearance
Withstanding
No dielectric breakdown or
Visual inspection
250% of the rated voltage
Voltage
mechanical breakdown
Temperature
X6S
Characteristics
Adhesive Strength
(From -55℃ to 105℃, Capacitance change should be within ±22%)
No peeling shall be occur on the
500gF, for 10±1 sec.
of Termination
terminal electrode
Bending Strength
Capacitance change :
Tan δ (DF)
Insulation
Within specified tolerance
Test condition
1㎑±10%
Capacitance
0.1 max.
Resistance
within ±12.5%
Bending to the limit (1mm)
with 1.0mm/sec.
Solderability
More than 75% of terminal surface
SnAg3.0Cu0.5 solder
is to be soldered newly
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to
Capacitance change :
Soldering heat
Tan δ, IR : initial spec.
within ±7.5%
Solder pot : 270±5℃, 10±1sec.
Performance
Vibration Test
Capacitance change :
within ±10%
Test condition
Amplitude : 1.5mm
Tan δ, IR : initial spec.
From 10㎐ to 55㎐ (return : 1min.)
Moisture
Capacitance change :
2hours 3 direction (x, y, z)
With rated voltage
Resistance
Tan δ : 0.125 max
IR
40±2℃, 90~95%RH, 500+12/-0 hours
: More than 12.5㏁·㎌
High Temperature
Capacitance change :
Resistance
Tan δ : 0.125 max
IR
within ±12.5%
within ±12.5%
With 100%
of the rated voltage
Max. operating temperature
: More than 25㏁·㎌
1000+48/-0 hours
Temperature
Capacitance change :
Cycling
Tan δ, IR : initial spec.
within ±15%
1 cycle condition
Min. operating temperature
25℃
→
25℃
→
Max. operating temperature →
5 cycles test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.