CL32C182JGHNNNF

SPECIFICATION  Supplier : Samsung electro-mechanics  Product : Multi-layer Ceramic Capacitor  Samsung P/N : CL32C182JGHNNNF CAP, 1.8㎋, 500V, ±5%, C0G, 1210  Description : A. Samsung Part Number ① Series ② Size ③ Dielectric ④ Capacitance ⑤ Capacitance tolerance ⑥ Rated Voltage ⑦ Thickness CL 32 C 182 J G H N N N F ① ② ③ ④ ⑤ ⑥ ⑦ ⑧ ⑨ ⑩ ⑪ Samsung Multi-layer Ceramic Capacitor 1210 (inch code) L: 3.2 ± 0.3 C0G 1.8 ㎋ ±5 % W: ⑧ Inner electrode Termination 500 V 1.6 ± 0.2 mm mm 2.5 ± 0.2 mm Ni Cu Sn 100% (Pb Free) Plating ⑨ Product ⑩ Special Normal Reserved for future use ⑪ Packaging Embossed Type,13"reel(8,000ea) B Samsung Reliability Test and Judgement condition B. Performance Capacitance Q Insulation Resistance Appearance Withstanding Voltage Temperature Characteristics Adhesive Strength of Termination Bending Strength Solderability Test condition Within specified tolerance 1000 min 1㎑±10% 0.5~5Vrms More than 500Mohm㎌ Rated Voltage 60~120 sec. No abnormal exterior appearance No dielectric breakdown or mechanical breakdown C0G Visual inspection 150% of the rated voltage (From -55℃ to 125℃, Capacitance change should be within ±30PPM/℃) No peeling shall be occur on the 500gF, for 10±1 sec. terminal electrode Capacitance change : within ±5% Bending to the limit (1mm) with 1.0mm/sec. More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 245±5℃, 3±0.3sec. (preheating : 80~120℃ for 10~30sec.) Resistance to Soldering heat Capacitance change : within ±2.5% Tan δ, IR : initial spec. Solder pot : 270±5℃, 10±1sec. Performance Vibration Test Moisture Resistance Capacitance change : within ±2.5% Tan δ, IR : initial spec. Capacitance change : within ±7.5% Q: 200 min IR : Amplitude : 1.5mm From 10㎐ to 55㎐ (return : 1min.) 2hours  3 direction (x, y, z) With rated voltage 40±2℃, 90~95%RH, 500 +12/-0 hour More than 25㏁·㎌ High Temperature Capacitance change : within ±3% Resistance Q: IR : Temperature Cycling Test condition 350 min More than 50㏁·㎌ Capacitance change : within ±2.5% Tan δ, IR : initial spec. With 150% of the rated voltage Max. operating temperature 1000+48/-0 hour 1 cycle condition Min. operating temperature → → Max. operating temperature → 5 cycles test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue. 25℃ 25℃