SCCU1B150F2E

Surface Mount Disc Capacitors Surface Mount Disc Capacitors Introduction Samwha's high voltage ceramic capacitors offer superior performance and reliability. SMDC is the resin molded SMD type that surface mounting is available. SMDC exhibits high reliability through use of disc capacitor element. Competitive lower maintenance cost is guaranteed. Wide rated voltage ranges from 1kV to 6kV, through a disc element which withstand high voltage and outcurve terminals. Design flexibility ensures down sizing and higher resistance to outer impact. How to Order(Product Identification) SCC O 3H 150 J 2 E 00 Style Mark SCC SCK SCG Product Name Temperature Compensating Type High Dielectric Type Semiconductor Type Mark SSD SSC Product Name AC250/400V(Testing Voltage:AC4000V) AC250(Testing Voltage:AC2500V) Surface Mount Disc Capacitors www.samwha.com Capacitance temperature characteristic Shape & Dimensions C L P R NPO(0) N80(-80) N150(-150) N220(-220) N330(-330) SCC Type (PPM/℃) T U O N470(-470) N750(-750) SL(+350~-1000) B R E F SCK, SCG, SSC, SSD Type Y5P(+10~-10%) Y5R(+15~-15%) Y5U(+22~-56%) Y5V(+22~-82%) Inside Terminal (Style 1) (Development Product) Outside Terminal (Style 2) (Mass Product) S Rating Voltage 1A 2A 3A 4A 10V 100V 1kV 10kV 1B 2B 3B 4B 12.5V 125V 1.25kV 3D 4C 2kV 16kV 1C 16V 1E 2E 25V 250V 3F 3.15kV 2G 3G 400V 4kV 1H 2H 3H 50V 500V 5kV 3J 6.3kV Capacitance (in picofarads) The first two digits indicate significant digits. The 3rd digit indicate the number of zero following. R denotes decimal. (Unit : mm) Ex.) 0.5pF : 0R5, 10pF : 100, 100pF : 101 Rated Capacitance Voltage (pF) 3kV 5 ~ 33 5 ~ 33 4kV 39 ~ 47 18 ~ 27 39 ~ 47 5kV 6kV 5 ~ 15 18 ~ 27 5 ~ 15 L ±0.5 5.7 5.7 7.1 5.5 7.1 5.5 7.1 7.1 W ±0.3 4.5 4.5 6.3 4.5 6.3 4.5 6.3 6.3 H ±0.2 2.3 2.3 2.4 2.3 2.4 2.3 2.4 2.4 E ±0.2 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 A 1.7 1.7 2.0 1.7 2.0 1.7 2.0 2.0 B 3.1 3.1 3.7 3.1 3.7 3.1 3.7 3.7 K ±0.1 0.5 0.5 0.5 0.5 0.5 L1 ±0.3 9.4 10.8 9.4 10.8 10.8 L2 Min. 6.7 7.9 6.7 7.9 7.9 Terminal Developm Form ent/Mass Style 1 Style 1 Style 1 Style 2 Style 2 Style 2 Style 2 Style 2 Development Development Development Mass Development Mass Development Development Cap. Tolerance Mark C D F Cap. Tolerance ±0.25pF ±0.5pF ±1.0pF Mark J K M Cap. Tolerance ±5% ±10% ±20% Mark P Z Cap. Tolerance +100%, -0% +80%, -20% Style Mark 1 2 Packing Style Terminal Form Inside Terminal Outside Terminal Spare Code Mark B E Bulk Packaging Style Embossed Carrier Taping 134 SAMWHA CAPACITOR Co., Ltd. Surface Mount Disc Capacitors 135 Surface Mount Disc Capacitors Electrical Performance Requirement No. Item SCC Type 1 Operating Temperature Range Capacitance -25℃ ~ 110℃ SCK, SCG, SSC, SSD Type B.E : -25℃ ~ +85℃ F : +10℃ ~ +65℃ 1 High Temperature Test Appearance Capacitance Change Test Conditions No. Item SCC Type SCK, SCG, SSC, SSD Type - Temperature : 85±2℃ - Test voltage : 1.2 times of the rated voltage - Operating time of test : 1000 +48,/ -0 hours After testing, The capacitor shall be subjected to the standard test condition for a period 4~24 hours and shall be measured. Charge and discharge current shall be 50 mA or less. ※Standard test condition : -Temperature : 20±2℃ - Frequency : 1± 0.1MHz(SCC Type) 1± 0.1KHz (SCK, SCG, SSC, SSD Type) - Relative Humidity : 60 ~ 70% - Measure voltage : 1± 0.1Vrms - Temperature : 40±2℃ - Relative Humidity : 90~95% R.H - Operating time of test : 500 +24, -0 hours After testing, The capacitor shall be subjected to the standard test condition for a period 4~24 hours and shall be measured. Charge and discharge current shall be 50 mA or less. ※Standard test condition : -Temperature : 20±2℃ - Frequency : 1± 0.1MHz(SCC Type) 1± 0.1KHz (SCK, SCG, SSC, SSD Type) - Relative Humidity : 60 ~ 70% - Measure voltage : 1± 0.1Vrms - The capacitors shall be subjected to 5cycles of the temperature cycle under Table. B : With ± 10% E : With ± 20% F : With ± 30% B,E : 5% Max. F : 7.5% Max. Step. 1 2 3 4 Temperature(℃) -25, +0/-3 Standard test condition +85, +0/-3 Standard test condition Period(minutes) 30 10~15 30 10~15 Temperature and Humity Test Characteristics Requirement Test Conditions No. visible damage ±5% or ±0.5 pF Whichever is larger from initial measurement Q ≥ 200 B : With ± 10% E : With ± 20% F : With ± 30% B,E : 5% Max. F : 7.5% Max. 2 Within the specified range 3 Dissipation Factor , (tan δ Q) Q ≥ 400+20C (C : capacitance, pF) B,E : 2.5% Max. F : 5.0% Max. - Temperature : 20±2℃ - Frequency : 1±0.1MHz(SCC Type) 1±0.1KHz (SCK,SCG,SSC,SSD Type) - Relative Humidity : 60~70% - Measure voltage : 1±0.1Vrms - Applied Voltage : To be below 500V - Rating Voltage Above 500V - 500V - Charge Time : 60±5sec 2 - Testing Voltage R.V W.V 3kV R.V × 1.75 4kV~ R.V × 1.5 Dissipation Factor , (tan δ Q) I.R Surface Mount Disc Capacitors www.samwha.com More than 2000MΩ 4 Insulation resistance More than 10000MΩ 5 Dielectric Withstanding Voltage No remarkable abnormality is recognized Humidity Resistance Test Appearance No. visible damage Capacitance Change ±5% or ±0.5 pF Whichever is larger from initial measurement Dissipation Factor , (tan δ Q) I.R Q ≥ 200 B : With ± 10% E : With ± 20% F : With ± 30% B,E : 5% Max. F : 7.5% Max. For 1 to 5 sec.(Between terminals) The discharge current, however was 50 mA or less 6 Capacitance temperature Characteristics Based on Items 2.2. 12 of EIA RS-198-C More than 500MΩ 3 Temperature Cycle Test Appearance No. visible damage Capacitance Change ±5% or ±0.5 pF Whichever is larger from initial measurement Q ≥ 200 Dissipation Factor , (tan δ Q) I.R More than 1000MΩ After testing, The capacitor shall be subjected to the standard test condition for a period 4~24 hours and shall be measured. Charge and discharge current shall be 50 mA or less. ※Standard test condition : -Temperature : 20±2℃ - Frequency : 1± 0.1MHz(SCC Type) 1± 0.1KHz (SCK, SCG, SSC, SSD Type) - Relative Humidity : 60 ~ 70% - Measure voltage : 1± 0.1Vrms 136 SAMWHA CAPACITOR Co., Ltd. Surface Mount Disc Capacitors 137 Ceramic Type Mechanical test and Environmental Substance Requirement No. Item SCC Type 1 Adhesive Strength of Terminal SCK, SCG, SSC, SSD Type Test Conditions No removal of the termination or other defect should occur. Solder the capacitor to the testing jig (glass epoxy board) shown in Fig. 2 using a eutectic solder. Then apply 5 N force in the direction of the arrow. The soldering should be used the reflow method and should be conducted with care so that the soldering is uniform and free of defects such as heat shock. Appendix SMD Type Packing CHIP B/I Packing SMDC Packing Surface Mount Disc Capacitors www.samwha.com Fig.2 2 Vibration Resistance Appearance Capacitance Change No. visible damage ±5% or ±0.5 pF Whichever is larger from initial measurement B : With ± 10% E : With ± 20% F : With ± 30% B,E : 5% Max. F : 7.5% Max. Dissipation Q ≥ 200 , Factor (tan δ Q) I.R 3 Bending Strength Appearance Capacitance Change More than 1000MΩ No. visible damage ±5% or ±0.5 pF Whichever is larger from initial measurement The capacitor should be subjected to a simple harmonic motion having a total amplitude of 1.5mm, the frequency being varied uniformly between the approximate limits of 10 and 55Hz. The frequency range, from 10 to 55Hz and return to 10Hz, should be traversed in approximately 1 min. This motion should be applied for a period of 2hrs. in each 3mutually perpendicular directions (total of 6hrs.) Solder the capacitor to the testing jig (glass epoxy board) shown in Fig. 3 using a eutectic solder. Then apply a force in the direction shown in Fig. 4. The soldering should be done either with an iron or using the reflow method and should be conducted with care so that the soldering is uniform and free of defects such as heat shock. 140 142 144 B : With ± 10% E : With ± 20% F : With ± 30% Fig.3 Fig.4 4 Solderability Test Visual examination terminals area shall be at least 90% covered with a new solder coating No. visible damage ±5% or ±0.5 pF Whichever is larger from initial measurement No. Failure B : With ± 5% E : With ± 15% F : With ± 20% Soldering Method : Reflow Soldering - Maximum Temperature : 250℃ max. (245± 5℃, 5± 0.5 sec.) - Preheating Temperature : 150~180℃, 60~180 sec. Soldering Method : Reflow Soldering - Maximum Temperature : 250℃ max. (245± 5℃, 5± 0.5 sec.) - Preheating Temperature : 150~180℃, 60~180 sec. - After testing, The capacitors shall be subjected to the standard test condition for a period 24 hours and shall be measured. 5 Solder Heat Resistance Appearance Capacitance Change Dielectric Strength 6 The regulation of environmental pollution materials. ※ Never use materials mentioned below in high voltage products regulated this document. ※ Pb, Hg, Cr+6, PBB, PBDE : 100ppm, Cd : 5ppm ※ Exception : - Pb of solder :