L4-R12-10

FERRITE CHIP INDUCTORS 1. PART NO. EXPRESSION : L4 SERIES L4-47NK-10 (a) (b) (c) (d) (a) Series code (b) Inductance code : 47N = 0.047uH (c) Tolerance code : K = ±10%, M = ±20% (d) 10 : Lead Free 2. CONFIGURATION & DIMENSIONS : A D L G B C PCB Pattern Unit:m/m A B C D G 2.20 Ref. H 1.40 Ref. L 4.40 Ref. 3.20±0.20 1.60±0.20 1.10±0.30 0.50±0.30 3. SCHEMATIC : 4. MATERIALS : b a Ag(100%) Ni(100%)-1.5um(min.) Sn(100%)-3.0um(min.) (a) Body : Ferrite (b) Termination : Ag/Ni/Sn 5. GENERAL SPECIFICATION : a) Temp. rise : 30°C Max. b) Rated current : Base on temp. rise c) Storage temp. : -40°C to +85°C d) Operating temp. : -40°C to +85°C e) Resistance to solder heat : 260°C.10secs NOTE : Specifications subject to change without notice. Please check our website for latest information. H 15.01.2008 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 1 FERRITE CHIP INDUCTORS 6. ELECTRICAL CHARACTERISTICS : Part Number L4-47N -10 L4-68N -10 L4-R10 -10 L4-R12 -10 L4-R15 -10 L4-R18 -10 L4-R22 -10 L4-R27 -10 L4-R33 -10 L4-R39 -10 L4-R47 -10 L4-R56 -10 L4-R68 -10 L4-R82 -10 L4-1R0 -10 L4-1R2 -10 L4-1R5 -10 L4-1R8 -10 L4-2R2 -10 L4-2R7 -10 L4-3R3 -10 L4-3R9 -10 L4-4R7 -10 L4-5R6 -10 L4-6R8 -10 L4-8R2 -10 L4-100 -10 L4-120 -10 L4-150 -10 L4-180 -10 L4-220 -10 L4-270 -10 L4-330 -10 Inductance tolerance : : K : ±10% M : ±20% NOTE : Specifications subject to change without notice. Please check our website for latest information. L4 SERIES EIA Size 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 1206 Inductance ( µH ) 0.047 0.068 0.100 0.120 0.150 0.180 0.220 0.270 0.330 0.390 0.470 0.560 0.680 0.820 1.000 1.200 1.500 1.800 2.200 2.700 3.300 3.900 4.700 5.600 6.800 8.200 10.000 12.000 15.000 18.000 22.000 27.000 33.000 Q Min 20 20 20 20 20 20 20 20 20 25 25 25 25 25 45 45 45 45 45 45 45 45 45 50 50 50 50 50 35 35 35 35 35 Test Frequency ( MHz ) 50 50 25 25 25 25 25 25 25 25 25 25 25 25 10 10 10 10 10 10 10 10 10 4 4 4 2 2 1 1 1 1 0.4 SRF ( MHz ) Min. 320 280 235 220 200 185 170 150 145 135 125 115 105 100 75 65 60 55 50 45 41 38 35 32 29 26 24 22 19 18 16 14 13 DC Resistance () Max. 0.15 0.25 0.25 0.30 0.30 0.40 0.40 0.50 0.50 0.60 0.60 0.70 0.80 0.90 0.40 0.50 0.50 0.50 0.60 0.60 0.70 0.80 0.90 0.70 0.80 0.90 1.00 1.05 0.70 070 0.90 0.90 1.05 Rated Current ( mA ) 300 300 250 250 250 250 250 250 250 250 200 200 150 150 100 100 50 50 50 50 50 50 50 25 25 25 25 15 5 5 5 5 5 15.01.2008 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 2 FERRITE CHIP INDUCTORS 7. IMPEDANCE VS. FREQUENCY CURVES : L4 SERIES Q vs. Q vs F req FCI3 2 16 -Se rie s Frequency . 12 0 10 0 80 10 0 4 R7 1 R0 33 0 Q 60 40 20 0 1 10 R1 2 100 F REQ UENCY(M Hz) L vs. IDC FCI3216-Series L vs IDC. 100 330 100 4R7 1 In ctance ) du (uH 10 1R0 0.1 1 10 1 00 1 000 DC Curren t(mA) NOTE : Specifications subject to change without notice. Please check our website for latest information. 15.01.2008 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 3 FERRITE CHIP INDUCTORS 8. RELIABILITY & TEST CONDITION : L4 SERIES ITEM Electrical Characteristics Test Impedance DC Resistance Rated Current Temperature Rise Test PERFORMANCE TEST CONDITION HP4291A, HP4287A+16092A Refer to standard electrical characteristics list HP4338B 30°C max. ( t) 1. Applied the allowed DC current. 2. Temperature measured by digital surface thermometer. Preheat : 150°C, 60sec. Solder : Sn-Ag3.0-Cu0.5 Solder Temperature : 260±5°C Flux for lead free : rosin Dip Time : 10±0.5sec. Solder Heat Resistance No mechanical damage Remaining terminal electrode : 70% min. Preheating Dipping 260°C Natural cooling 150°C 60 seconds 10±0.5 seconds Solderability More than 90% of the terminal electrode should be covered with solder. Preheating Dipping 245°C Natural cooling Preheat : 150°C, 60sec. Solder : Sn-Ag3.0-Cu0.5 Solder Temperature : 245±5°C Flux for lead free : rosin Dip Time : 4±1sec. 150°C 60 seconds 4±1.0 seconds Terminal Strength The terminal electrode & the dielectric must not be damaged by the forces applied on the right conditions. For Z / L Series : Size 1 2 3 4 5 6 Force (Kfg) 0.2 0.5 0.6 1.0 1.0 1.0 1.5 2.0 > 25 Time (sec) W W 7 8 Flexture Strength The terminal electrode & the dielectric must not be damaged by the forces applied on the right conditions. 20(.787) Bending 45(1.772) 45(1.772) 40(1.575) Solder a chip on a test substrate, bend the substrate by 2mm (0.079in) and return. 100(3.937) NOTE : Specifications subject to change without notice. Please check our website for latest information. 15.01.2008 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 4 FERRITE CHIP INDUCTORS 8. RELIABILITY & TEST CONDITION : L4 SERIES ITEM Bending Strength PERFORMANCE The ferrite should not be damaged by forces applied on the right condition. R0.5(0.02) 1.0(0.039) TEST CONDITION For Z / L Series : Series name 2 3 4 mm (inches) 0.80 (0.033) 1.40 (0.055) 2.00 (0.079) 2.70 (0.106) P-Kgf 0.3 1.0 2.5 2.5 Chip A 5 6 7 8 Random Vibration Test Appearance : Cracking, shipping & any other defects harmful to the characteristics should not be allowed. Frequency : 10-55-10Hz for 1 min. Amplitude : 1.52mm Directions & times : X, Y, Z directions for 2 hours. A period of 2 hours in each of 3 mutually perpendicular directions (Total 6 hours). No mechanical damage Temperature : 85±5°C Applied Current : rated current Duration : 1008±12hrs Measured at room temperature after placing for 2 to 3hrs. Humidity : 90~95% RH. Temperature : 40±2°C Duration : 1008±12hrs Measured at room temperature after placing for 2 to 3hrs. Drop Loading at High Temperature Drop 10 times on a concrete floor from a height of 75cm. Appearance : No damage. Inductance : Within ±10% of initial value. Q : Within ±30% of initial value. Humidity Thermal Shock Appearance : No damage. Inductance : Within ±10% of initial value. Q : Within ±30% of initial value. Phase 1 2 Temperature (°C) -40±2°C +85±5°C Times (min.) 30±3 30±3 For L Series : Condition for 1 cycle Step1 : -40±2°C 30±3 min. Step2 : +85±5°C 30±3 min. Number of cycles : 100 Measured at room temperature after placing for 2 to 3hrs. Temperature : -55±2°C Duration : 1008±12hrs Measured at room temperature after placing for 2 to 3hrs. No mechanical damage Low temperature storage test Measured : 100 times Drop Drop 10 times on a concrete floor from a height of 75cm. Derating Curve Derated Current(A) Derating 6 5 4 3 2 1 0 6A 5A 4A 3A 2A 1.5A 1A For the ferrite chip bead which withstanding current over 1.5A, as the operating temperature over 85°C, the derating current information is necessary to consider with. For the detail derating of current, please refer to the Derated Current vs. Operating Temperature curve. 85 125 Operating Tem perature(°C) Operating Temperature(¢X ) C NOTE : Specifications subject to change without notice. Please check our website for latest information. 15.01.2008 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 5 FERRITE CHIP INDUCTORS 9. SOLDERIND AND MOUNTING : 9-1. Recommended PC Board Pattern 2.60 0.60 L4 SERIES 9-2. Soldering Mildly activated rosin fluxes are preferred. The minimum amount of solder can lead to damage from the stresses caused by the difference in coefficients of expansion between solder, chip and substrate. The terminations are suitable for all wave and re-flow soldering systems. If hand soldering cannot be avoided, the preferred technique is the utilization of hot air soldering tools. 9-2.1 Lead Free Solder Re-flow : Recommended temperature profiles for re-flow soldering in Figure 1. 9-2.2 Solder Wave : Wave soldering is perhaps the most rigorous of surface mount soldering processes due to the steep rise in temperature seen by the circuit when immersed in the molten solder wave, typical at 230°C. Due to the risk of thermal damage to products, wave soldering of large size products is discouraged. Recommended temperature profile for wave soldering is shown in Fig. 2 9-2.3 Soldering Iron (Figure 3) : Products attachment with soldering iron is discouraged due to the inherent process control limitations. In the event that a soldering iron must be employed the following precautions are recommended. Note : d) 1.0mm tip diameter (max) a) Preheat circuit and products to 150°C. e) Use a 20 watt soldering iron with tip diameter of 1.0mm b) 350°C tip temperature (max) f) Limit soldering time to 3 secs. c) Never contact the ceramic with the iron tip Preheating Soldering 10s max. 250 ~ 260 230 180 150 TEMPERATURE °C TEMPERATURE °C Natural cooling 0.80 PC board should be designed so that products are not sufficient under mechanical stress as warping the board. Products shall be positioned in the sideway direction against the mechanical stress to prevent failure. Preheating 260 245 150 Soldering Natural cooling 60~120s 30~60s Time(sec.) Figure 1. Re-flow Soldering Over 2min. Gradual Cooling Within 3s Preheating Soldering 3s (max.) 10s (max.) TEMPERATURE °C Natural cooling Figure 2. Wave Soldering 350 330 150 Over 1min. Gradual Cooling Figure 3. Hand Soldering NOTE : Specifications subject to change without notice. Please check our website for latest information. 15.01.2008 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 6 FERRITE CHIP INDUCTORS L4 SERIES 9-3. Solder Volume Accordingly increasing the solder volume, the mechanical stress to product is also increased. Exceeding solder volume may cause the failure of mechanical or electrical performance. Solder shall be used not to be exceed as shown in Fig. 4. Upper limit Recommendable t Figure 4 NOTE : Specifications subject to change without notice. Please check our website for latest information. 15.01.2008 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 7 FERRITE CHIP INDUCTORS 10. PACKAGING INFORMATION : 10-1. Reel Dimension A L4 SERIES Type 7" x 8mm D B C A(mm) 9.0±0.5 B(mm) 60.0±2.0 60.0±2.0 C(mm) D(mm) 13.5±0.5 178.0±2.0 13.5±0.5 178.0±2.0 7" x 12mm 13.5±0.5 2±0.5 13.5±0.5 R10.5 7" x 8mm 7" x 12mm R1.9 R0.5 120° 10-2 Tape Dimension / 8mm P2:2±0.05 Po:4 ±0.1 D:1.5+0.1 A W:8.0±0.1 t Series Size 1 Bo(mm) Ao(mm) Ko(mm) P(mm) 2.0±0.1 4.0±0.1 4.0±0.1 4.0±0.1 4.0±0.1 4.0±0.1 t(mm) 0.23±0.05 0.22±0.05 0.22±0.05 0.22±0.05 0.22±0.05 0.22±0.05 D1(mm) none none 1.0±0.1 1.0±0.1 1.0±0.1 1.0±0.1 E:1.75±0.1 F:3.5 ±0.05 1.12±0.05 0.67±0.05 0.54±0.05 1.80±0.10 1.01±0.10 1.02±0.10 2.25±0.10 1.42±0.10 1.04±0.10 2.35±0.10 1.50±0.10 1.45±0.10 3.50±0.10 1.88±0.10 1.27±0.10 3.42±0.10 2.77±0.10 1.55±0.10 Bo 2 Z/L 3 (09) 3 (12) 4 5 P A D1:1±0.1 Ao Ko Section A-A 10-2.1 Tape Dimension / 12mm D:1.5+0.1 A Po:4±0.1 P2:2±0.05 t Series Size 6 Bo(mm) 4.95±0.1 4.95±0.1 6.10±0.1 Ao(mm) 1.93±0.1 3.66±0.1 5.40±0.1 Ko(mm) 1.93±0.1 1.85±0.1 2.00±0.1 P(mm) 4.0±0.1 8.0±0.1 8.0±0.1 t(mm) 0.24±0.05 0.24±0.05 0.30±0.05 D1(mm) 1.5±0.1 1.5±0.1 1.5±0.1 E:1.75±0.1 W:12.0±0.1 F:5.5 ±0.05 Bo Z/L 7 8 A D1:1.5±0.1 P Ao Ko Section A-A 10-3. Packaging Quantity Chip Size Chip / Reel Inner Box Middle Box Carton Bulk (Bags) 8 1000 4000 20000 40000 7000 7 1000 4000 20000 40000 12000 6 2000 8000 40000 80000 20000 5 2500 12500 62500 125000 30000 4 3000 15000 75000 150000 50000 3 (12) 2000 10000 50000 100000 100000 3 (09) 4000 20000 100000 200000 150000 2 4000 20000 100000 200000 200000 1 10000 50000 250000 500000 300000 NOTE : Specifications subject to change without notice. Please check our website for latest information. 15.01.2008 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 8 FERRITE CHIP INDUCTORS L4 SERIES 10-4. Tearing Off Force F 165° to 180° Top cover tape Room Temp. (°C) 5~35 Room Humidity (%) 45~85 Room atm (hPa) 860~1060 Tearing Speed (mm/min) 300 The force for tearing off cover tape is 15 to 60 grams in the arrow direction under the following conditions. Base tape Application Notice 1. Storage Conditions : To maintain the solderabililty of terminal electrodes : a) Temperature and humidity conditions : 10 ~ 40°C and 30 ~ 70% RH. b) Recommended products should be used within 6 months from the time of delivery. c) The packaging material should be kept where no chlorine or sulfur exists in the air. 2. Transportation : a) Products should be handled with care to avoid damage or contamination from perspiration and skin oils. b) The use of tweezers or vacuum pick up is strongly recommended for individual components. c) Bulk handling should ensure that abrasion and mechanical shock are minimized. NOTE : Specifications subject to change without notice. Please check our website for latest information. 15.01.2008 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 9