#SH721 Viton® Heat Shrink Tubing (AMS-DTL-23053/13 (MIL-DTL23053/13) 2:1 Shrink Ratio, Fluoroelastomer Tubing Flexible High Temperature Chemical an d Abrasion Resistant Applications Daburn SH721 is a heat shrinkable, flexible, fluoroelastomer sleeving that is used in high temperature applications or where exposure to high temperature and aggressive solvents is expected. It is widely used in hydraulic equipment, aircraft manufacture and ship building applications. Features Shrink ratio: 50% or more in the radial direction, 20% or less in the axial direction Shrink temperature 175⁰ C Continuous operating temperature range: - 40°C (-40°F) to 200°C (392°F) Excellent abrasion protection while maintaining flexibility at high temperatures High resistance to chemicals and oils AMS-DTL-23053/13 (Formerly MIL-DTL-23053/13) RoHS Compliant Specification/Test Values Property Physical Electrical Chemical Test Method Tensile strength gElongation Unaged Tensile stress @ 200% elongation Tensile strength Aged Elongation Tensile strength Fluid Resistance Elongation Heat shock g Cold bend Voltage withstand Dielectric strength Volume resistivity Copper corrosion Fungus resistance Water absorption Flammability ASTM-D412 Value Min. 1,200 psi Min. 250% Max. 2,000 psi ASTM-D412 250°C/168 hrs ASTM-D412 250°C/168 hrs 300°C/4 hrs - 40°C/4 hrs 2kV/1min ASTM-D2671 ASTM-D876 175°C/16 hrs ASTM G21 ASTM-D570 ASTM-D2671 Rev. May 2011 Min. 1,200 psi Min. 200% Min. 1,200 psi Min. 250% No cracking, flowing or dripping No cracking Pass Min. V 200 olts/mil Min. 109 - cm No pitting or corrosion No growth % 0.5 Max Pass Recovered Expanded Daburn Part # SH721-1/8 SH721-3/16 SH721-1/4 SH721-3/8 SH721-1/2 SH721-5/8 SH721-3/4 SH721-7/8 SH721-1” SH721-1 1/4” SH721-1 1/2” Internal Diameter (Minimum) m (D) Internal Diameter (Maximum) (d) Minimum Total Wall Thickness (t) In. mm In. mm In. mm 0.125 0.187 0.250 0.375 0.500 0.625 0.750 0.875 1.000 1.125 1.500 3.4 4.7 6.4 9.5 12.7 15.9 19.1 22.2 25.4 31.8 38.1 0.063 0.094 0.125 0.187 0.250 0.312 0.375 0.437 0.500 0.625 0.750 1.6 2.4 3.2 4.7 6.4 7.9 9.5 11.1 12.7 15.9 19.1 0.048 0.028 0.028 0.028 0.028 0.034 0.034 0.038 0.038 0.040 0.040 0.65 0.72 0.72 0.72 0.72 0.90 0.90 0.92 0.92 1.02 1.02 AMS-DTLMIL-DTL- 23053/13-012 23053/13-001 23053/13-002 23053/13-003 23053/13-004 23053/13-005 23053/13-006 23053/13-007 23053/13-008 23053/13-009 23053/13-010 Standard Color: Black Standard Put-Ups (Spool Sizes): 25', 50', & 100', also 250' on 1/8", 3/16", & 1/4", & 500' on 1/8". Larger spool sizes have a discounted price per foot. Please call for other put-ups. Storage Condition: Keep cool. Don’t keep package over 8 hours at temperature exceeding 40°C (104°F). * Test Fluids: Hydraulic Fluid petroleum base JP-8 Lubricating Oil Lubricating Oil 5 percent NaCI Deicing Fluid MIL-H-5606 Mil-T-5624 Mil-L-7808 MIL-L-23699 A-A-694 Mil-A-8243

下载 PDF

SH721-7/8-100

物料型号为DABURN #SH721，是一种Viton®热收缩套管，符合AMS-DTL-23053/13（原MIL-DTL-23053/13）标准。

器件简介显示，SH721适用于高温应用或预期暴露于高温和腐蚀性溶剂的环境中，广泛应用于液压设备、飞机制造和船舶建造等领域。

引脚分配未在文档中明确说明，但该热收缩套管的主要特性包括：2:1的径向收缩比，轴向收缩不超过20%，收缩温度为175°C。

它的连续工作温度范围为-40°C至200°C，并具有良好的耐磨损性、耐化学和耐油性能。

参数特性包括：未老化状态下的拉伸强度至少为1,200 psi，延伸率至少为250%；在250°C下老化168小时后的拉伸强度至少为1,200 psi，延伸率至少为200%；耐化学试剂和耐油性能良好，热冲击试验、冷弯试验和耐电压测试均通过。

功能详解指出，SH721在高温下保持柔韧性的同时提供优异的耐磨保护，符合RoHS标准。

应用信息强调了其在液压设备、飞机制造和船舶建造等领域的广泛应用。

封装信息包括：标准颜色为黑色，标准包装尺寸为25英尺、50英尺和100英尺，对于1/8英寸、3/16英寸、1/4英寸和1/8英寸的尺寸，还有500英尺的包装。

大卷包装尺寸有价格优惠，具体请咨询。

存储条件为：保持冷却，不要将包装在超过40°C（104°F）的温度下存放超过8小时。