MC0603B104K500CT

General Purpose Multilayer Ceramic Capacitors 4 to 100V (NP0, X5R, X7R & Y5V Dielectrics) Description: MLCC consists of a conducting material and electrodes. To manufacture a chip-type SMT and achieve miniaturization, high density and high efficiency, ceramic condensers are used. The MLCC is made by NP0, X7R, X6S, X5R and Y5V dielectric material and which provides product with high electrical precision, stability and reliability. Features: Applications: •  A wide selection of sizes is available (0201 to 1812). •  High capacitance in given case size. •  Capacitor with lead-free termination (pure Tin). •  •  •  •   or general digital circuit. F For power supply bypass capacitors. For consumer electronics. For telecommunication. How To Order: MC Multicomp 1206 B 104 K 500 C T Size Dielectric Capacitance Tolerance Rated Voltage Termination Packaging style Two significant digits followed by no. of zeros. And R is in place of decimal point. A=±0.05pF B=±0.1pF C=±0.25pF D=±0.5pF F=±1% G=±2% J=±5% K=±10% M=±20% Z=-20/+80% Two significant digits followed by no. of zeros. And R is in place of decimal point. C=Cu/Ni/Sn T=7” reeled R=7” reeled (2mm pitch for 0603 size; paper tape) G=13” reeled Inch (mm) 0201 (0603) 0402 (1005) 0603 (1608) 0805 (2012) 1206 (3216) 1210 (3225) 1812 (4532) N=NP0 (C0G) B=X7R F=Y5V X=X5R S=X6S Eg.: 0R5=0.5pF 1R0=1.0pF 104 = 10×104 = 10μF 4R0=4V DC 6R3=6.3V DC 100=10V DC 160=16V DC 250=25V DC 500=50V DC 101=100V DC External Dimensions: The outline of MLCC Size Inch (mm) L (mm) W (mm) 01R5 (0402) 0.4 ±0.02 0.2 ±0.02 0.2 ±0.02 0.6±0.03 0.3 ±0.03 0.3 ±0.03 Soldering Method * MB (mm) V R 0.1 ±0.03 L R T (mm)/Symbol 0201 (0603) 0.6±0.05#2 0.3 ±0.05#2 0.3 ±0.05#2 0.6±0.09#3 0.3 ±0.09#3 0.3 ±0.09#3 0402 (1005) 1 ±0.05 0.5 ±0.05 1 ±0.2 0.5 ±0.2 0.15 ±0.05 0.15 +0.1/-0.05 0.5 ±0.05 N 0.5 +0.02/-0.05 Q 0.5 ±0.2 E R 0.25 +0.05/-0.1 www.element14.com www.farnell.com www.newark.com Page 18/12/14 V1.0 General Purpose Multilayer Ceramic Capacitors 4 to 100V (NP0, X5R, X7R & Y5V Dielectrics) Size Inch (mm) 0603 (1608) 0805 (2012) L (mm) W (mm) 1.6 ±0.1 0.8 ±0.1 1.6 +0.15/0.1 0.8 +0.15/-0.1 1.6 ±0.2*1 0.8 ±0.2*1 2 ±0.15 2 ±0.2 3.2 ±0.15 1206 (3216) 3.2 ±0.2 3.2 +0.3/-0.1 3.2 ±0.3 1.25 ±0.1 1.25 ±0.2 1.6 ±0.15 1.6 ±0.2 1.6 +0.30/-0.1 2.5±0.2 1210 (3225) 3.2±0.4 1808 (4520) 1812 (4532) 4.5 ±0.4 (4.5+0.5/0.3)** 4.5 ±0.4 4.5+0.5/0.3)** 2.5±0.3 2.03 ±0.25 3.2 ±0.3 3.2 ±0.4 Soldering Method * T (mm)/Symbol 0.8 ±0.07 S R/W 0.5 ±0.1 H R/W X R/W 0.8 +0.15/-0.1 0.8 ±0.2*1 0.5 ±0.1 H R/W 0.6 ±0.1 A R/W 0.8 ±0.1 B R/W 1.25 ±0.1 D R 0.85 ±0.1 T R/W 1.25 ±0.2 I R 0.8 ±0.1 B R/W 0.95 ±0.1 C R 1.25 ±0.1 D R 1.15 ±0.15 J R 1.6 ±0.2 G R 0.85 ±0.1 T R/W 1.6 +0.3/-0.1 P R 0.95 ±0.1 C R 0.85 ±0.1 T R 1.25 ±0.1 D R 1.6 ±0.2 G R 2 ±0.2 K R 2.5 ±0.3 M R 1.25 ±0.1 D R 1.4 ±0.15 F R 1.6 ±0.2 G R 2 ±0.2 K R 1.25 ±0.1 D R 1.6 ±0.2 G R 2 ±0.2 K R 2.5 ±0.3 M R 2.8 ±0.3 U R MB (mm) 0.4 ±0.15 0.5 ±0.2 0.6 ±0.2 (0.5±0.25)*** 0.75 ±0.25 0.75 ±0.25 (0.5±0.25)*** 0.75 ±0.25 0.5±0.25)*** * R = Reflow soldering process; W = Wave soldering process. ** For 1808_200V ~3kV, 1812_200V~3kV and safety certificated products. *** For 1206_1000V ~3kV, 1808_200V ~3kV, 1812_200V~3kV and safety certificated products. #1: For 0603/Cap^10μF or 0603(>10V)/Cap>1μF products. #2: For 0201/Cap^0.68μF products. #3: For 0201/Cap >1μF products. www.element14.com www.farnell.com www.newark.com Page 18/12/14 V1.0 General Purpose Multilayer Ceramic Capacitors 4 to 100V (NP0, X5R, X7R & Y5V Dielectrics) General Electrical Data: Dielectric NP0 X7R Size Capacitance range* 0.1pF to 0.1μF Capacitance tolerance** Cap≤5pF#1: A (±0.05pF), B (±0.1pF), C (±0.25pF) 5pF0.1μF, 0603^0.068μF, 1206>1μF; TT series %3% 0201(50V); 0603^0.047μF; 0805^0.18μF;1206^0.47μF %5% 1210^4.7μF %10% 0402^0.1μF; 0603^1μF; 0805^1μF; 1206^4.7μF; 1210^10μF TT series %10% 0603^1μF; 0805≥2.2μF; 1210^10μF %5% 0201^0.01μF;0805^1μF; 1210^10μF %7% 0603^0.33μF; 1206^4.7μF %10% 0402^0.10μF;0603^0.47μF;0805^2.2 μF; 1206^6.8μF ; 1210^22μF; TT series %12.5% 16V ** Test condition: 0.5±0.2Vrms, 1KHz±10% X7R: 0603^225(10V), 0805=106(6.3V&10V) X5R: 01R5^103, 0201^224 (6.3V,10V), 0402^475 (6.3V), 0402^225(10V), 0603=106 (6.3V,10V), TT18X ^475(10V) , TT15X series X6S:0201^224 (6.3V),0402^225 (6.3V), Exception of D.F. % 6.3V 4V %5% 0201^0.01μF; 0402^0.033μF; 0805^0.68μF;1206^2.2μF;1210^4.7μF %10% 0201^0.1μF; 0402^0.47µF; 0603^0.68μF;0805^2.2μF; 1206^4.7μF; 1210^22μF; TT series %10% 0201^0.012μF;0402^0.33μF(0402/ X7R^0.22μF); TT series 0603^0.33μF; 0805^2.2μF;1206^2.2μF;1210^22μF %15% 0201^0.1μF; 0402^1μF %15% 0201^0.1μF;0402^1μF;0603^10μF; 0805^4.7μF; 1206^47μF :1210^100μF; TT series %20% 0402^2.2μF %3.5% 10V %5% %10% %15% 0402^1μF - - Y5V: Rated vol. D.F.% ^50V 5% 7% 35V 7% - 25V 16V (C0.1μF; 0603≥10μF; 0805≥47μF 6.3V: 0201≥0.1μF; 1206≥10μF 4V:0603≥22μF; 0805≥47μF With no electrical load. 6 7 8 Temperature Coefficient T.C. Operating Temp T.C. Capacitance Change NPO -55~125°C at 25°C NPO Within ±30ppm/°C X7R -55~125°C at 25°C X7R Within ±15% X5R -55~ 85°C at 25°C X5R Within ±15% X6S -55~105°C at 25°C X6S Within ±22% Y5V -25~ 85°C at 20°C Y5V Within +30%/-80% Adhesive Strength of Termination Pressurizing force: 1N (0201) and 5N (≤0603) and 10N (>0603) * Test time: 10±1 sec. No remarkable damage or removal of the terminations. Vibration Resistance Vibration frequency: 10~55 Hz/min. Total amplitude: 1.5mm Test time: 6 hrs. (Two hrs each in three mutually perpendicular directions.) Measurement to be made after keeping at room temp. for 24±2 hrs. No remarkable damage. Cap change and Q/D.F.: To meet initial spec. www.element14.com www.farnell.com www.newark.com Page 18/12/14 V1.0 General Purpose Multilayer Ceramic Capacitors 4 to 100V (NP0, X5R, X7R & Y5V Dielectrics) No Item 9 Solderability Solder temperature: 235±5°C Dipping time: 2±0.5 sec. 95% min. coverage of all metalized area. Bending Test The middle part of substrate shall be pressurized by means of the pressurizing rod at a rate of about 1 mm per second until the deflection becomes 1 mm and then the pressure shall be maintained for 5±1 sec. Measurement to be made after keeping at room temp. for 24±2 hrs. No remarkable damage. Cap change: NP0: within ±5% or 0.5pF whichever is larger X7R, X5R, X6S: within ±12.5% Y5V: within ±30% (This capacitance change means the change of capacitance under specified flexure of substrate from the capacitance measured before the test.) Resistance to Soldering Heat Solder temperature: 260±5°C Dipping time: 10±1 sec Preheating: 120 to 150°C for 1 minute before immerse the capacitor in a eutectic solder. Before initial measurement (Class II only): Perform 150+0/-10°C for 1 hr and then set for 24±2 hrs at room temp. Measurement to be made after keeping at room temp. for 24±2 hrs. No remarkable damage. Cap change: NP0: within ±2.5% or 0.25pF whichever is larger X7R, X5R, X6S: within ±7.5% Y5V: within ±20% Q/D.F., I.R. and dielectric strength: To meet initial requirements. 25% max. leaching on each edge. 10. 11 Test Condition Requirements Conduct the five cycles according to the temperatures and time. 12 Step Temp. (°C) Time (min.) 1 Min. operating temp. +0/-3 30±3 2 Room temp. 2~3 3 Max. operating temp. +3/-0 30±3 4 Room temp. 2~3 Temperature Cycle Before initial measurement (Class II only): Perform 150+0/-10°C for 1 hr and then set for 24±2 hrs at room temp. Measurement to be made after keeping at room temp. for 24±2 hrs. No remarkable damage. Cap change: NP0: within ±2.5% or 0.25pF whichever is larger X7R, X5R, X6S: within ±7.5% Y5V: within ±20% Q/D.F., I.R. and dielectric strength: To meet initial requirements. www.element14.com www.farnell.com www.newark.com Page 18/12/14 V1.0 General Purpose Multilayer Ceramic Capacitors 4 to 100V (NP0, X5R, X7R & Y5V Dielectrics) No Item Test Condition Requirements No remarkable damage. Cap change: NP0: within ±5% or 0.5pF whichever is larger X7R, X5R, X6S: ≥10V**,within ±12.5%; %6.3V within ±25%; TT series & C≥ 1uF,within ±25% **10V: 0603^4.7μF;0402^1μF;0201^0.1μF, within ±25%; Y5V: ≥10V, within ±30%; %6.3V, within +30/-40% Q/D.F. value: NP0: More than 30pF Q≥350, 10pF≤C≤30pF, Q≥275+2.5C Less than 10pF Q≥200+10C X7R, X5R, X6S: Rated vol. D.F.% ^100V %3% Exception of D.F. % %6% 13 Humidity (Damp Heat) Steady State Test temp.: 40±2°C Humidity: 90~95% RH Test time: 500+24/-0hrs. Before initial measurement (Class II only): Perform 150+0/-10°C for 1 hr and then set for 24±2 hrs at room temp. Measurement to be made after keeping at room temp. for 24±2 hrs. ^50V 35V 25V 16V 10V %3% %5% %5% %7.5% 0805>0.1μF, 0603^0.068μF %6% 0201(50V); 0603^0.047μF; 0805^0.18μF;1206^0.47μF %10% 1210^4.7μF %20% 0402^0.1μF; 0603^1μF; 0805^1μF;1206^4.7μF; 1210^10μF TT series %20% 0603^1μF; 0805≥2.2μF; 1210^10μF %10% 0201^0.01μF;0805^1μF; 1210^10μF %14% 0603^0.33μF; 1206^4.7μF %15% 0402^0.10μF;0603^0.47μF;0805^2.2 μF; 1206^6.8μF ; 1210^22μF; TT series %20% 0402^1μF %10% 0201^0.01μF; 0402^0.033μF; 0805^0.68μF;1206^2.2μF;1210^4.7μF %15% 0201^0.1μF; 0402^0.47µF; 0603^0.68μF;0805^2.2μF; 1206^4.7μF; 1210^22μF; TT series %15% 0201^0.012μF 0402^0.33μF; 0603^0.33μF; 0805^2.2μF; 1206^2.2μF; 1210^22μF %20% 0201^0.1μF; 0402^1μF TT series 0201^0.1μF;0402^1μF;0603^10μF; 0805^4.7μF; 1206^47μF :1210^100μF; TT series %5% %7.5% 1206^0.47μF 6.3V %15% %30% 4V %20% - - www.element14.com www.farnell.com www.newark.com Page 18/12/14 V1.0 General Purpose Multilayer Ceramic Capacitors 4 to 100V (NP0, X5R, X7R & Y5V Dielectrics) No Item Test Condition Requirements Y5V: Rated vol. D.F.% ^50V 7.5% 10% 35V 10% - 25V 16V (C