SAFC1808X7R502-102KNE

SAFC SERIES SAFETY CERTIFIED CAPACITORS FEATURES: • Multi-layer Ceramic Capacitors are safety standard approved by IEC60384-14 and UL 60950-1 and UL60384-14 • UL Certified: E511154 & E511217 • TUV Certified: R50450826 PART NUMBER STRUCTURE SAFC 1808 X7R 502 Series Safety Approved MLCC Size 1808 1812 2211 2208 2220 Temperature Characteristic (Dielectric) C0G X7R Class 202 = X2 502 = X1/Y2 — 102 K N E Capacitance (picofarads) 1st two digits are significant, followed by number of zeroes. R denotes decimal e.g: 101 = 100pF 333 = 0.033uF, etc Tolerance J = 5% K = 10% M = 20% Termination/Special N = standard termination X = Soft/Flex Termination S = Arc Prevention Coating Z=A  rc Prevention Coating + Soft/Flex Termination Packaging E = Embossed Tape (7” reels) Example P/N: SAFC1808X7R502-102KNE APPLICATIONS The X2 and X1/Y2 (250Vac) are specially designed for use in modems, telephone and telecommunication equipment, electronic equipment for lighting and surge protection, EMI filtering and Isolation. PERFORMANCE SPECIFICATIONS Rated Voltage (Ur) 250Vac Temperature Coefficient C0G: < 30ppm/˚C , -55˚C ~ +125˚C (EIA Class I) X7R: < ±15% , -55˚C ~ +125˚C (EIA Class II) Capacitance Range X1/Y2, 250Vac: 2pF ~ 4700pF X2, 250Vac: 2pF ~ 56nF Quality and Dissipation Factor C0G: Q ≥ 1000 , X7R : D.F. ≤ 2.5% Environmental Testing -55˚C (cold); +125˚C (hot); 21 days under damp heat (steady state) Insulation Resistance ≥ 10GΩ Voltage Rating DC X1/Y2: 2KV Vdc X2: 1.5KV Vdc Voltage Proof (Dielectric Withstanding Voltage) X2 Capacitor: 1075Vdc (4.3Ur) X1/Y2 Capacitor: 1500Vac min. Peak Impulse Voltage X2: 2.5KV , X1/Y2: 5KV, each per IEC60384-14:2013 Operating Temperature -55˚C to +125˚C Dielectric Aging C0G: 0 % , X7R: 1.0 % per decade hr., typical Test Conditions per IEC60384-14 Voltage: 1.0 Vrms C < 100pF at 1MHz C ≥ 100pF at 1KHz SAFETY DETAILS OF SPECIFICATIONS IEC 660384-14: 2013, 4th Edition EN 60384-1 4: 2013, 4th Edition Meets the electrical requirements and certification for equipment requiring Class X1/Y2 and X2 devices. UL 60384-14 : 2014, 2nd Edition Component certified for equipment requiring UL-60384-14 compliance UL 60950-1 : 2007, 2nd Edition TNV/SELV isolation capacitors certified To UL 60950-1 Email: sales@venkel.com | Phone: 512.794.0081 | Toll Free: 800.950.8365 | Web: www.venkel.com Rev: 09/2020-A 1 SAFC SERIES SAFETY CERTIFIED CAPACITORS DIMENSIONS Unit: inches (mm) SIZE L W T (MAX) EB (MIN) 1808 0.18 ± 0.011 (4.60 ± 0.30) 0.08 ± 0.008 (2.00 ± 0.20) 0.088 (2.20) 0.008 (0.20) 1812 0.18 ± 0.011 (4.60 ± 0.30) 0.12 ± 0.012 (3.20 ± 0.30) 0.104 (2.60) 0.008 (0.20) 2208 0.22 ± 0.016 (5.70 ± 0.40) 0.08 ± 0.008 (2.00 ± 0.20) 0.088 (2.20) 0.012 (0.30) 2211 0.22 ± 0.016 (5.70 ± 0.40) 0.11 ± 0.012 (2.80 ± 0.30) 0.120 (3.00) 0.012 (0.30) 2220 0.22 ± 0.016 (5.70 ± 0.40) 0.20 ± 0.016 (5.00 ± 0.40) 0.120 (3.00) 0.012 (0.30) VOLTAGE AND CAPACITANCE RANGE X2 CLASS - C0G DIELECTRIC Values that are typically available. SIZE Code 1808 Value Rated Max Voltage (Vac) Certificate TUV/UL 2R0 2pF 250 5R0 5pF 250 TUV/UL 6R8 6.8pF 250 TUV/UL 8R2 8.2pF 250 TUV/UL 100 10pF 250 TUV/UL 120 12pF 250 TUV/UL 150 15pF 250 TUV/UL 180 18pF 250 TUV/UL 220 22pF 250 TUV/UL 270 27pF 250 TUV/UL 330 33pF 250 TUV/UL 360 36pF 250 TUV/UL 390 39pF 250 TUV/UL 470 47pF 250 TUV/UL 560 56pF 250 TUV/UL 680 68pF 250 TUV/UL 820 82pF 250 TUV/UL 101 100pF 250 TUV/UL 121 120pF 250 TUV/UL 131 130pF 250 TUV/UL 151 150pF 250 TUV/UL 181 180pF 250 TUV/UL 221 220pF 250 TUV/UL 271 270pF 250 TUV/UL 331 330pF 250 TUV/UL 391 390pF 250 TUV/UL 471 470pF 250 TUV/UL 561 560pF 250 TUV/UL 681 680pF 250 TUV/UL 821 820pF 250 TUV/UL 102 1000pF 250 TUV/UL 122 1200pF 250 152 1500pF 250 182 1800pF 250 222 2200pF 250 272 2700pF 250 332 3300pF 250 472 4700pF 250 1812 2208 2211 2220 Note: Additional values may be available. Please contact us for more information. Due to demand and raw material fluctuations, specific values may not be available. Email: sales@venkel.com | Phone: 512.794.0081 | Toll Free: 800.950.8365 | Web: www.venkel.com Rev: 09/2020-A 2 SAFC SERIES SAFETY CERTIFIED CAPACITORS VOLTAGE AND CAPACITANCE RANGE X2 CLASS - X7R DIELECTRIC Values that are typically available. SIZE Code 1808 Value Rated Max Voltage (Vac) Certificate 151 150pF 250 TUV/UL 181 180pF 250 TUV/UL 221 220pF 250 TUV/UL 271 270pF 250 TUV/UL 331 220pF 250 TUV/UL 391 390pF 250 TUV/UL 471 470pF 250 TUV/UL 561 560pF 250 TUV/UL 681 680pF 250 TUV/UL 821 820pF 250 TUV/UL 102 1000pF 250 TUV/UL 122 1200pF 250 TUV/UL 152 1500pF 250 TUV/UL 182 1800pF 250 TUV/UL 222 2200pF 250 TUV/UL 272 2700pF 250 TUV/UL 332 3300pF 250 TUV/UL 472 4700pF 250 TUV/UL 103 0.01uF 250 TUV/UL TUV/UL 153 0.015uF 250 223 0.022uF 250 TUV/UL 333 0.033uF 250 TUV/UL 473 0.047uF 250 563 0.056uF 250 1812 2208 2211 2220 Note: Additional values may be available. Please contact us for more information. Due to demand and raw material fluctuations, specific values may not be available. Email: sales@venkel.com | Phone: 512.794.0081 | Toll Free: 800.950.8365 | Web: www.venkel.com Rev: 09/2020-A 3 SAFC SERIES SAFETY CERTIFIED CAPACITORS VOLTAGE AND CAPACITANCE RANGE X1/Y2 CLASS - C0G DIELECTRIC Values that are typically available. SIZE Code 1808 Value Rated Max Voltage (Vac) Certificate 2R0 2pF 250 TUV/UL 5R0 5pF 250 TUV/UL 6R8 6.8pF 250 TUV/UL 8R2 8.2pF 250 TUV/UL 100 10pF 250 TUV/UL 120 12pF 250 TUV/UL 150 15pF 250 TUV/UL TUV/UL 180 18pF 250 220 22pF 250 TUV/UL 270 27pF 250 TUV/UL 330 33pF 250 TUV/UL 360 36pF 250 TUV/UL 390 39pF 250 TUV/UL 470 47pF 250 TUV/UL 560 56pF 250 TUV/UL 680 68pF 250 TUV/UL 820 82pF 250 TUV/UL 101 100pF 250 TUV/UL 121 120pF 250 TUV/UL 131 130pF 250 TUV/UL 151 150pF 250 TUV/UL 181 180pF 250 TUV/UL 221 220pF 250 TUV/UL 271 270pF 250 TUV/UL 331 330pF 250 TUV/UL 391 390pF 250 TUV/UL 471 470pF 250 TUV/UL 561 560pF 250 TUV/UL 681 680pF 250 TUV/UL 821 820pF 250 TUV/UL 102 1000pF 250 TUV/UL 122 1200pF 250 TUV/UL 1812 2208 2211 2220 Note: Additional values may be available. Please contact us for more information. Due to demand and raw material fluctuations, specific values may not be available. Email: sales@venkel.com | Phone: 512.794.0081 | Toll Free: 800.950.8365 | Web: www.venkel.com Rev: 09/2020-A 4 SAFC SERIES SAFETY CERTIFIED CAPACITORS VOLTAGE AND CAPACITANCE RANGE X1/Y2 CLASS - X7R DIELECTRIC Values that are typically available. SIZE 1808 Code Value Rated Max Voltage (Vac) 2R0 2pF 250 5R0 5pF 250 6R8 6.8pF 250 8R2 8.2pF 250 100 10pF 250 120 12pF 250 1812 2208 2211 2220 Certificate 150 15pF 250 180 18pF 250 220 22pF 250 270 27pF 250 330 33pF 250 360 36pF 250 TUV/UL 390 39pF 250 TUV/UL 470 47pF 250 TUV/UL 560 56pF 250 TUV/UL 680 68pF 250 TUV/UL 820 82pF 250 TUV/UL 101 100pF 250 TUV/UL 121 120pF 250 TUV/UL 131 130pF 250 TUV/UL 151 150pF 250 TUV/UL 181 180pF 250 TUV/UL 221 220pF 250 TUV/UL 271 270pF 250 TUV/UL 331 330pF 250 TUV/UL 391 390pF 250 TUV/UL 471 470pF 250 TUV/UL 561 560pF 250 TUV/UL 681 680pF 250 TUV/UL 821 820pF 250 TUV/UL 102 1000pF 250 TUV/UL 122 1200pF 250 TUV/UL 152 1500pF 250 TUV/UL 182 1800pF 250 TUV/UL 222 2200pF 250 TUV/UL 272 2700pF 250 TUV/UL 332 3300pF 250 TUV/UL 472 4700pF 250 TUV/UL Note: Additional values may be available. Please contact us for more information. Due to demand and raw material fluctuations, specific values may not be available. Email: sales@venkel.com | Phone: 512.794.0081 | Toll Free: 800.950.8365 | Web: www.venkel.com Rev: 09/2020-A 5 SAFC SERIES SAFETY CERTIFIED CAPACITORS APPLICATION - EXAMPLE CIRCUIT Y Y Tip & Ring TNV SELV X 1st X : Across The Line Y : Line By Pass 2nd TEST SPECIFICATIONS NO. ITEM SPECIFICATION Appearance No mechanical damage shall occur Capacitance 1 Resistance to soldering heat ≤ ± 10% of initial value Class II (X7R) ≤ ± 20% of initial value More than 1,000MΩ (Dielectric Withstanding Voltage) To satisfy the specified initial value Appearance No mechanical damage shall occur Characteristic Cap. Change Class I (C0G) ≤ ± 15% of initial value Class II (X7R) ≤ ± 20% of initial value Q Class I More Than 30pF : Q ≥ 350 30pF and below: Q ≥ 275 + 2.5 x C (C:pF) Tan 0 Class II Maximum 5.0% Insulation Resistance More than 1,000MΩ (Dielectric Withstanding Voltage) To satisfy the specified initial value Appearance No mechanical damage shall occur Capacitance Endurance Class I (C0G) Insulation Resistance Voltage Proof 3 Cap. Change To satisfy the specified initial value Capacitance Damp Heat / Steady State Characteristic Q/Tanδ Voltage Proof 2 TEST CONDITION Characteristic Cap. Change Class I (C0G) ≤ ± 20% of initial value Class II (X7R) ≤ ± 25% of initial value Q Class I More Than 30pF : Q≥350 30pF and below: Q ≥ 275 + 2.5 x C (C:pF) Tan 0 Class II Maximum 5.0% Insulation Resistance More than 1,000MΩ Class II capacitor shall be set for 48 ± 4 hours at room temperature after one hour heat treatment at 150 + 0/-10°C before initial measure. Preheat : At 150 ± 10°C For 60 ~120sec. Dip : Solder Temperature of 260 ± 5°C Dip Time: 10 ± 1sec. Solder : H63A Flux : Rosin Measure at room temp. after cooling for: Class I : 24 ± 2 Hours Class II : 48 + 4 Hours Temperature : 40°C Humidity: 95 %RH Test Time : 500hr (21days) The capacitors with rated voltage (250Vac) applied. Measure at room temp. after cooling for: Class I : 24 ± 2 Hrs Class II : 48 ± 4 Hrs Solder the Capacitor on P.C. Board shown before testing. Impulse Voltage Each individual capacitor shall be subjected to a 2.5KV(X2) and 5KV(X1/Y2) impulse for three times. Then the capacitors are applied to life test. T1 = 1.2us is between 10% to 90% T2 = 50us is between 50% to 50% 100% 90 50 10 T1 T2 Voltage Proof (Dielectric Withstanding Voltage) Email: sales@venkel.com | To satisfy the specified initial value Phone: 512.794.0081 | Toll Free: 800.950.8365 | Temperature : 125°C Test Time : 1 000hrs Applied Voltage : Class X Capacitors :1.25Ur (312.5Vac) Class Y Capacitors :1.70Ur (425Vac) Except that once every hour the voltage shall be increased to 1 000Vrms for 0.1 s. Web: www.venkel.com Rev: 09/2020-A 6 SAFC SERIES SAFETY CERTIFIED CAPACITORS TEST SPECIFICATIONS FIG.1 P.C.Board for Bending Strength Test (referring to IEC384-14 and EN132400) Solder Resist Copper C 40mm A B 100mm 1.6mm Material : Glass Epoxy Substrate Copper (Thickness : 0.035mm) Solder Resist FIG.2 Test Substrate C 10mm A Material : Glass Epoxy Substrate Copper (Thickness : 0.035mm) Solder Resist Thickness : 1.6 mm 3mm B Unit: mm Email: sales@venkel.com | TYPE A B C 1808 3.5 7.0 2.5 1812 3.5 7.0 3.7 2208 4.5 8.0 2.5 2211 4.5 8.0 3.0 2220 4.5 8.0 5.6 Phone: 512.794.0081 | Toll Free: 800.950.8365 | Web: www.venkel.com Rev: 09/2020-A 7 SAFC SERIES SAFETY CERTIFIED CAPACITORS PERFORMANCE SPECIFICATIONS NO. ITEM SPECIFICATION TEST CONDITION 1 Visual No abnormal exterior appearance Visual Inspection 2 Dimension See Page2 Visual Inspection 3 Capacitance Within the specified tolerance Char. Class I (C0G) C0G 4 Q and Dissipation Factor Frequency Voltage 1.0 ± 0.2Vrms More than 30pF : Q ≥ 1000 C≤100pF 1MHz ±10% 30pF & below: Q ≥ 400 + 20C (C:pF) C≤100pF 1KHz ±10% Class II (X7R) Maximum : 2.5% (0.025) X7R 1KHz ±10% 1.0 ± 0.2Vrms After performing deage at 150 ± 5% for 30min. and placement room temperature for 24± 2hr. 5 6 7 Insulation Resistance Minimum 10,000MΩ Applied Voltage: Applied Voltage: 500V Charge Time : 60sec. Voltage Proof No dielectric breakdown or mechanical breakdown Applied Voltage: X Capacitor: Applied Voltage 1075Vdc(4.3Ur) Y Capacitor: Applied Voltage 1500Vac For 1min. Is Applied Less Than 50mA Current (Dielectric Withstanding Voltage) More than 90% of the terminal surface is to be soldered newly, so metal part does not come out Solder Temperature: 245 ± 5˚C Dip Time: 5 ± 0.5 sec. or dissolve Immersing Speed: 25 ± 10% mm/s Solderability Solder: H63A Flux: Rosin Preheat : At 80 ~120˚C For 10 ~30sec. Appearance No mechanical damage shall occur Capacitance 8 Resistance to Flexure of Substrate Class II (X7R) ≤ ± 12.5% of initial value To satisfy the specified initial value To satisfy the specified initial value No indication of peeling shall occur on the terminal electrode. Capacitance Characteristic Cap. Change Class I (C0G) ≤ ± 5% of initial value Class II (X7R) ≤ ± 12.5% of initial value Q Class I More Than 30pF : Q ≥ 350 30pF and below: Q ≥ 275 + 2.5 x C (C:pF) Q / Tanδ To satisfy the specified initial value Insulation Resistance To satisfy the specified initial value Voltage Proof (Dielectric Withstanding Voltage) To satisfy the specified initial value Appearance No mechanical damage shall occur Capacitance Resistance to Soldering Heat ≤ ± 5.0% of initial value Insulation Resistance Appearance 10 Class I (C0G) To satisfy the specified initial value (Dielectric Withstanding Voltage) Robustness of Shear Cap. Change Q / Tanδ Voltage Proof 9 Characteristic Characteristic Cap. Change Class I (C0G) ≤ ± 10% of initial value Class II (X7R) ≤ ± 20% of initial value Q / Tanδ To satisfy the specified initial value Insulation Resistance More than 1,000MΩ Voltage Proof (Dielectric Withstanding Voltage) Email: sales@venkel.com | To satisfy the specified initial value Phone: 512.794.0081 | Toll Free: 800.950.8365 | Bending shall be applied to the 1.0 mm with 1.0 mm/sec. R340 Bending Limit C Meter 45±1mm 45±1mm Solder the capacitor on P.C. board shown in Fig 1. before testing. A 5N·f ( 0.5Kg·f) pull force shall be applied for 10 ± 1 second. Solder the capacitor on P.C. board shown in Fig 1. before testing. Class II capacitor shall be set for 48 ± 4 hours at room temperature after one hour heat treatment at 150 + 0/-10˚C before initial measure. Preheat: At 150± 10˚C For 60 ~120sec. Dip: Solder Temperature of 260 ± 5˚C Dip Time: 10 ± 1sec. Solder: H63A Flux: Rosin Measure at room temp. after cooling for: Class I: 24 ± 2 Hours Class II: 48 ± 4 Hours Web: www.venkel.com Rev: 09/2020-A 8 SAFC SERIES SAFETY CERTIFIED CAPACITORS PERFORMANCE SPECIFICATIONS NO. ITEM Appearance Capacitance 11 Damp Heat/Steady State No mechanical damage shall occur Test Condition : Temperature : 40˚C Humidity : 95 %RH Test Time : 500hr (21days) The capacitors with rated voltage(250Vac) applied. Measure at room temp. after cooling for: Class I: 24 ± 2 Hrs Class II: 48 ± 4 Hrs Solder The Capacitor On P.C. Board Shown In Fig 2. Before Testing. Characteristic Cap. Change Class I (C0G) ≤ ± 15% of initial value Class II (X7R) ≤ ± 20% of initial value Q Class I Tan δ Class II Maximum 5.0% Insulation Resistance More than 1,000MΩ (Dielectric Withstanding Voltage) To satisfy the specified initial value Appearance No mechanical damage shall occur Capacitance Endurance TEST CONDITION More Than 30pF: Q ≥ 350 30pF & Below:Q ≥ 275 + 2.5× C (C:pF) Voltage Proof 12 SPECIFICATION Characteristic Cap. Change Class I (C0G) ≤ ± 20% of initial value Class II (X7R) ≤ ± 25% of initial value Q Class I More Than 30pF : Q≥350 30pF and below: Q ≥ 275 + 2.5 x C (C:pF) Tan δ Class II Maximum 5.0% Insulation Resistance More than 1,000MΩ Impulse Voltage Each individual capacitor shall be subjected to a 2.5KV(X2) and 5KV(X1/Y2) impulse for three times. Then the capacitors are applied to life test. 100 (%) 90 T1=1.2us is between 10% to 90% T2=50us is between 50% to 50% 50 10 t T1 T12 Voltage Proof (Dielectric Withstanding Voltage) 13 14 Capacitor didn’t burnt at all Passive Flammability The cheese cloth shall not burn with a flame Active Flammability Email: sales@venkel.com To satisfy the specified initial value | Phone: 512.794.0081 | Toll Free: 800.950.8365 | Temperature : 125˚C Test Time : 1000hrs Applied Voltage : Class X Capacitors :1.25Ur (312.5Vac) Class Y Capacitors :1.70Ur (425Vac) Except that once every hour the voltage shall be increased to 1000Vrms for 0.1s. Volume Sample : 21.56mm3 Flame exposure time : 5 sec.Max. The capacitors of class X2 each test capacitors applied Ur(250Vac). Then each sample shall be subjected to 20 discharges from a tank capacitor, charge to a voltage that, when discharged, places Ui(2500V) across the capacitor under test. The interval between successive discharges shall be 5s. Web: www.venkel.com Rev: 09/2020-A 9 SAFC SERIES SAFETY CERTIFIED CAPACITORS TAPE & REEL SPECIFICATIONS PLASTIC TAPE Pitch Hold I Chip Inserting Hole F A G H B t O C D E J Unit: mm TYPE A B 1808 2.5±0.2 4.9±0.2 1812 3.6±0.2 4.9±0.2 2208 2.5±0.2 6.1±0.2 2211 3.2±0.2 6.1±0.2 2220 5.4±0.2 6.1±0.2 TYPE G 5.5±0.05 C D E F 4.0±01 8.0±01 4.0±0.05 8.0±01 1.75±0.1 H I J T O 12.0±0.3 1.5±0.1/-0 3.7 max. 0.3 max. 0.5 min. 1808 1812 2208 2211 2220 REEL DIMENSIONS Reel Material: Polystyrene E C B D W A TYPE Unit: mm A B C D E W 178±2.0 Ø50 min. Ø13±0.5 Ø21±0.8 2.0±0.5 14±0.15 1808 1812 2208 2211 2220 TAPE & REEL QUANTITIES (EMBOSSED PLASTIC TAPE) SIZE 1808, 1812, 2208, 2211, 2220 Email: sales@venkel.com | Phone: 512.794.0081 | THICKNESS (T) QTY PER REEL 0.9mm < T ≤ 1.25mm 3000 1.25mm < T ≤ 2.0mm 2000 1.25mm < T ≤ 2.2mm 1000 T > 2.2mm 700 Toll Free: 800.950.8365 | Web: www.venkel.com Rev: 09/2020-A 10