CC1206MRY5V9BB224

DATA SHEET SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS 6.3 V TO 50 V 10 nF to 47 µF RoHS compliant & Halogen Free Product Specification – October 05, 2021 V.11 S General purpose & High capacitance Class 2, Y5V Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V 6.3 V to 50 V SCOPE ORDERING INFORMATION - GLOBAL PART NUMBER, PHYCOMP This specification describes Y5V series chip capacitors with leadfree terminations. CTC & 12NC APPLICATIONS Consumer electronics, for example: - Tuners - Television receivers - Video recorders - All types of cameras - Mobile telephones 2 13 All part numbers are identified by the series, size, tolerance, TC material, packing style, voltage, process code, termination and capacitance value. YAGEO BRAND ordering code GLOBAL PART NUMBER (PREFERRED ) CC XXXX X X (1) Y5V (2) (3) X BB XXX (4) (5) (1) SIZE – INCH BASED (METRIC) 0201 (0603) 0402 (1005) 0603 (1608) FEATURES Supplied in tape on reel Nickel-barrier end termination RoHS compliant Halogen Free compliant 0805 (2012) 1206 (3216) 1210 (3225) (2) TOLERANCE M = ± 20% Z = –20% to +80% (3) PACKING STYLE R = Paper/PE taping reel; Reel 7 inch K = Blister taping reel; Reel 7 inch P = Paper/PE taping reel; Reel 13 inch F = Blister taping reel; Reel 13 inch (4) RATED VOLTAGE 5 = 6.3 V 6 = 10 V 7 = 16 V 8 = 25 V 9 = 50 V (5) CAPACITANCE VALUE 2 significant digits+number of zeros The 3rd digit signifies the multiplying factor, and letter R is decimal point Example: 103 = 10 x 103 = 10,000 pF = 10 nF www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V 6.3 V to 50 V 3 13 CONSTRUCTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. The inner electrodes are connected to the two end terminations and finally covered with a layer of plated tin (NiSn). The terminations are lead-free. A cross section of the structure is shown in Fig.1. terminations electrodes MLB457 ceramic material Fig. 1 Surface mounted multilayer ceramic capacitor construction DIMENSION OUTLINES Table 1 For outlines see fig. 2 TYPE L1 (mm) W (mm) 0201 0402 0603 0.6 ± 0.03 1.0 ± 0.05 0805 1206 1210 1812 T (MM) L2 / L3 (mm) L4 (mm) min. max. min. 0.3 ± 0.03 0.5 ± 0.05 0.10 0.15 0.20 0.35 0.20 0.30 1.6 ± 0.10 0.8 ± 0.10 0.20 0.60 0.40 2.0 ± 0.10 (1) 1.25 ± 0.10 (1) 2.0 ± 0.20 (2) 1.25 ± 0.20 (2) 0.25 0.75 0.70 3.2 ± 0.15 (1) 1.6 ± 0.15 (1) 3.2 ± 0.30 (2) 1.6 ± 0.20 (2) 0.25 0.75 1.40 (1) ± 0.20 (1) 3.2 ± 0.20 2.5 3.2 ± 0.40 (2) 2.5 ± 0.30 (2) 4.5 ± 0.20 (1) 3.2 ± 0.20 (1) 4.5 ± 0.40 (2) 3.2 ± 0.40 (2) Refer to table 2 to 4 For dimension see Table 1 W T L2 L4 L3 MBB211 L1 Fig. 2 Surface mounted multilayer ceramic capacitor dimension 0.25 0.75 1.40 0.25 0.75 2.20 NOTE 1. Dimension for size 0805 to 1812, C ≤ 100 nF 2. Dimension for size 0805 to 1812, C > 100 nF www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V 6.3 V to 50 V 4 13 CAPACITANCE RANGE & THICKNESS FOR Y5V Table 2 Sizes from 0201 to 0402 0201 0402 CAP. 6.3 V 10 V 16 V 25 V 50 V 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 22 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 47 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 220 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 470 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 1.0 µF 0.5± 0.05 0.5± 0.05 10 nF 25 V 6.3 V 0.3± 0.03 100 nF 0.3± 0.03 2.2 µF 4.7 µF 10 µF 22 µF 47 µF Table 3 Sizes from 0603 to 0805 0603 CAP. 6.3 V 10 V 0805 16 V 25 V 50 V 10 nF 0.8± 0.1 22 nF 47 nF 6.3 V 10 V 16 V 25 V 50 V 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 100 nF 0.8± 0.1 0.8± 0.1 220 nF 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.85± 0.1 0.85± 0.1 470 nF 0.8± 0.1 0.8± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.8± 0.1 0.85± 0.1 0.85± 0.1 1.25± 0.2 1.25± 0.2 1.0 µF 0.8± 0.1 0.8± 0.1 0.8± 0.1 2.2 µF 0.8± 0.1 0.8± 0.1 0.8± 0.1 4.7 µF 0.8± 0.1 0.8± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.25± 0.2 10 µF 1.25± 0.2 1.25± 0.2 22 µF 1.25± 0.2 1.25± 0.2 47 µF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-3 series is on request www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V 6.3 V to 50 V 5 13 CAPACITANCE RANGE & THICKNESS FOR Y5V Table 4 Sizes from 1206 to 1210 1206 CAP. 6.3 V 1210 10 V 16 V 25 V 50 V 10 nF 0.6± 0.1 0.6± 0.1 22 nF 0.6± 0.1 0.6± 0.1 47 nF 0.6± 0.1 0.6± 0.1 100 nF 0.6± 0.1 0.6± 0.1 220 nF 0.6± 0.1 0.6± 0.1 470 nF 0.85± 0.1 0.85± 0.1 1.0 µF 0.85± 0.1 2.2 µF 0.85± 0.1 0.85± 0.1 4.7 µF 0.85± 0.1 0.85± 0.1 10 µF 0.85± 0.1 0.85± 0.1 1.15± 0.1 22 µF 1.6± 0.2 1.6± 0.2 1.6± 0.2 6.3 V 10 V 16 V 25 V 50V 1.5± 0.1 1.5± 0.1 1.5± 0.1 1.5± 0.1 1.5± 0.1 1.6± 0.2 1.6± 0.2 1.6± 0.2 0.85± 0.1 1.6± 0.2 47 µF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-3 series is on request www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V 6.3 V to 50 V 6 13 THICKNESS CLASSES AND PACKING QUANTITY Table 5 SIZE CODE THICKNESS CLASSIFICATION TAPE WIDTH QUANTITY PER REEL 0201 0.3 ± 0.03 mm 0402 0603 0805 1206 Ø 180 MM / 7 INCH Ø 330 MM / 13 INCH Paper Blister Paper Blister QUANTITY PER BULK CASE 8 mm 15,000 --- 50,000 --- --- 0.5 ± 0.05 mm 8 mm 10,000 --- 50,000 --- 50,000 0.8 ± 0.1 mm 8 mm 4,000 --- 15,000 --- 15,000 0.6 ± 0.1 mm 8 mm 4,000 --- 20,000 --- 10,000 0.85 ± 0.1 mm 8 mm 4,000 --- 15,000 --- 8,000 1.25 ± 0.2 mm 8 mm --- 3,000 --- 10,000 5,000 0.6 ± 0.1 mm 8 mm 4,000 --- 20,000 --- --- 0.85 ± 0.1 mm 8 mm 4,000 --- 15,000 --- --- 1.00 / 1.15 ± 0.1 mm 8 mm --- 3,000 --- 10,000 --- 1.25 ± 0.2 mm 8 mm --- 3,000 --- 10,000 --- 1.6 ± 0.15 mm 8 mm --- 2,500 --- 10,000 --- 1.6 ± 0.2 mm 8 mm --- 2,000 --- 10,000 --- 0.6 / 0.7 ± 0.1 mm 8 mm --- 4,000 --- 15,000 --- 0.85 ± 0.1 mm 8 mm --- 4,000 --- 10,000 --- 1.15 ± 0.1 mm 8 mm --- 3,000 --- 10,000 --- 1.15 ± 0.15 mm 8 mm --- 3,000 --- 10,000 --- 1.25 ± 0.2 mm 8 mm --- 3,000 --- --- --- 1210 1.5 ± 0.1 mm 8 mm --- 2,000 --- --- --- 1.6 / 1.9 ± 0.2 mm 8 mm --- 2,000 --- --- --- 2.0 ± 0.2 mm 8 mm --- 2,000 1,000 --- --- --- 2.5 ± 0.2 mm 8 mm --- 1,000 500 --- --- --- www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V 7 13 6.3 V to 50 V ELECTRICAL CHARACTERISTICS Y5V DIELECTRIC CAPACITORS; NISN TERMINATIONS Unless otherwise specified, all test and measurements shall be made under standard atmospheric conditions for testing as given in 5.3 of IEC 60068-1: - Temperature: 15 °C to 35 °C - Relative humidity: 25% to 75% - Air pressure: 86 kPa to 106 kPa Before the measurements are made, the capacitor shall be stored at the measuring temperature for a time sufficient to allow the entire capacitor to reach this temperature. The period as prescribed for recovery at the end of a test is norma lly sufficient for this purpose. Table 6 VALUE DESCRIPTION Capacitance range 10 nF to 22 µF ± 20% Capacitance tolerance Dissipation factor (D.F.) –20% to +80% ≤ 6.3 V ≤ 15% Exception: 0805 ≥ 22 µF ≤ 20% 10 V ≤ 12.5% Exception: 0402 ≥ 680 nF; 0603 ≥ 2.2 µF; 0805 ≥ 10 µF; 16 V 1206 ≥ 10 µF ≤ 15% ≤ 20% ≤ 12.5% Exception: 0603 ≥ 4.7 µF ≤ 15% 1206 ≥ 10 µF ≤ 20% ≥ 25 V ≤ 9% Exception: 0201 ≥ 10 nF ≤ 12.5% Rins ≥ 10 GΩ or Rins × Cr ≥ 500 Ω.F whichever is less Insulation resistance after 1 minute at Ur (DC) Rins × Cr ≥ 100 Ω.F : 0603 , 4.7uF, 6.3V and 10V; 0805, 22uF, 10V; Rins × Cr ≥ 50Ω.F: 0805, 22uF, 6.3V; Maximum capacitance change as a function of temperature (temperature characteristic/coefficient): Operating temperature range: +22% to –82% –30 °C to +85 °C www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors YNM0019 25 C C (%) General Purpose & High Cap. C C (%) Y5V YNM0020 15 0 10 25 35 50 60 75 85 50 V 10 V 25 V 16 V 110 100 30 -5 20 45 70 0 95 10 20 30 T ( oC) Fig. 3 6.3 V to 50 V 8 13 Fig. 4 Typical capacitance change as a function of temperature 40 50 V DC (V) Typical capacitance change with respect to the capacitance at 1 V as a function of DC voltage at 20 °C MBD078 2000 tan (x 10 4 ) 1500 1000 500 0 25 0 25 50 75 100 T ( oC) Fig. 5 Typical tan δ as a function of temperature SOLDERING RECOMMENDATION Table 7 SIZE SOLDERING 0201 METHOD Reflow Reflow/Wave Reflow only 0402 0603 0805 1206 ≥ 1210 > 100 nF > 1.0 µF > 2.2 µF > 2.2 µF Reflow only ≤ 100 nF ≤ 1.0 µF ≤ 2.2 µF ≤ 2.2 µF --- www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V 6.3 V to 50 V 9 13 TESTS AND REQUIREMENTS Table 8 TEST Test procedures and requirements TEST METHOD PROCEDURE Mounting IEC 60384- 4.3 21/22 REQUIREMENTS The capacitors may be mounted on printed-circuit boards or ceramic substrates No visible damage Visual inspection and dimension check 4.4 Any applicable method using × 10 magnification In accordance with specification Capacitance (1) 4.5.1 Class 2: At 20 °C, 24 hrs after annealing Within specified tolerance f = 1 KHz for C ≤ 10 µF, rated voltage > 6.3 V, measuring at voltage 1 Vrms at 20 °C f = 1 KHz, for C ≤ 10 µF, rated voltage ≤ 6.3 V, measuring at voltage 0.5 Vrms at 20 °C f = 120 Hz for C > 10 µF, measuring at voltage 0.5 Vrms at 20 °C Dissipation factor (D.F.) (1) 4.5.2 Class 2: At 20 °C, 24 hrs after annealing In accordance with specification f = 1 KHz for C ≤ 10 µF, rated voltage > 6.3 V, measuring at voltage 1 Vrms at 20 °C f = 1 KHz, for C ≤ 10 µF, rated voltage ≤ 6.3 V, measuring at voltage 0.5 Vrms at 20 °C f = 120 Hz for C > 10 µF, measuring at voltage 0.5 Vrms at 20 °C Insulation resistance 4.5.3 At Ur (DC) for 1 minute In accordance with specification Temperature characteristic 4.6 Class 2: Between minimum and maximum temperature Y5V: -30 °C to +85 °C Normal Temperature: 20 °C ∆C/C Class 2: Y5V: 22% to -82% ∆C/C Class 2: Y5V: 22% to -82% Adhesion 4.7 A force applied for 10 seconds to the line joining the terminations Force and in a plane parallel to the substrate size ≥ 0603: 5N size = 0402: 2.5N size = 0201: 1N NOTE: 1. For individual product specification, please contact local sales. www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V TEST TEST METHOD PROCEDURE REQUIREMENTS Bending strength IEC 6038421/22 Mounting in accordance with IEC 60384-22 paragraph 4.3 No visible damage Conditions: bending 1 mm at a rate of 1 mm/s, radius jig 5 mm ∆C/C 4.8 6.3 V to 50 V 10 13 Class2: Y5V: ± 10% ∆C/C Class2: Y5V: ± 10% Resistance to soldering heat 4.9 Precondition: 150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature Preheating: for size ≤ 1206: 120 °C to 150 °C for 1 minute Preheating: for size >1206: 100 °C to 120 °C for 1 minute and 170 °C to 200 °C for 1 minute Solder bath temperature: 260 ± 5 °C Dipping time: 10 ± 0.5 seconds Recovery time: 24 ± 2 hours Dissolution of the end face plating shall not exceed 25% of the length of the edge concerned ∆C/C Class2: Y5V: ± 20% ∆C/C Class2: Y5V: ± 20% D.F. within initial specified value Rins within initial specified value Solderability 4.10 Preheated the temperature of 80 °C to 140 °C and maintained for 30 seconds to 60 seconds. The solder should cover over 95% of the critical area of each termination 1. Temperature: 235± 5°C / Dipping time: 2 ± 0.5 s 2. Temperature: 245± 5°C / Dipping time: 3 ± 0.5 s (lead free) Depth of immersion: 10mm www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. TEST TEST METHOD PROCEDURE REQUIREMENTS Rapid change of temperature IEC 6038421/22 Preconditioning; 150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature No visual damage 4.11 Y5V 6.3 V to 50 V 11 13 ∆C/C 5 cycles with following detail: 30 minutes at lower category temperature 30 minutes at upper category temperature Class2: Y5V: ± 20% Recovery time 24 ± 2 hours ∆C/C Class2: Y5V: ± 20% D.F. meet initial specified value Rins meet initial specified value Damp heat with Ur load 4.13 1. Preconditioning, class 2 only: 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp 2. Initial measure: Spec: refer initial spec C, D, IR 3. Damp heat test: 500 ± 12 hours at 40 ± 2 °C; 90 to 95% R.H. 1.0 Ur applied 4. Recovery: Class 2: 24 ± 2 hours 5. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be precondition according to “IEC 60384 4.1” and then the requirement shall be met. No visual damage after recovery ∆C/C Class2: Y5V: ± 30% D.F. Class2: Y5V: ≤ 15% Rins Class2: Y5V: ≥ 500 MΩ or Rins x Cr ≥ 25s whichever is less ∆C/C Class2: Y5V: ± 30% D.F. Class2: Y5V: 2 x initial value max Rins Class2: Y5V: 500 MΩ or Rins x Cr ≥ 5s whichever is less www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V TEST TEST METHOD PROCEDURE REQUIREMENTS Endurance IEC 6038421/22 1. Preconditioning, class 2 only: No visual damage 4.14 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp 2. Initial measure: Spec: refer initial spec C, D, IR 3. Endurance test: Temperature: Y5V: 85 °C Specified stress voltage applied for 1,000 hours: Applied 2.0 x Ur for general product. Applied 1.5 x Ur for high cap. product. 4. Recovery time: 24 ± 2 hours 5. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be precondition according to “IEC 60384 4.1” and then the requirement shall be met. 6.3 V to 50 V 12 13 ∆C/C Class2: Y5V: ± 30% D.F. Class2: Y5V: ≤ 15% Rins Class2: Y5V: ≥ 1,000 MΩ or Rins x Cr ≥ 50s whichever is less ∆C/C Class 2: Y5V: ± 30% D.F. Class 2: Y5V: 2 x initial value max Rins Class 2: Y5V: 1,000 MΩ or Rins x Cr ≥ 10s whichever is less Voltage proof IEC 60384-1 4.6 Specified stress voltage applied for 1~5 seconds Ur ≤ 100 V: series applied 2.5 Ur No breakdown or flashover Charge/Discharge current is less than 50 mA www.yageo.com Oct 05, 2021 V.11 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. Y5V 6.3 V to 50 V 13 13 REVISION HISTORY REVISION DATE CHANGE NOTIFICATION DESCRIPTION Version 11 Oct. 05, 2021 - - Update 0805, 1210 I.R. spec, modify 0402 L4 spec Version 10 Apr. 29, 2021 - - Update 1206 ≥ 10 µF, 16V Df value Version 9 Nov. 11, 2019 - - Add 0603, 4.7uF, 10V Version 8 Mar. 7, 2017 - - 0805 L4 spec updated Version 7 Dec. 9, 2016 - - Soldering recommendation update Version 6 Jan. 12, 2016 - - Update capacitance range & thickness Version 5 Jul. 29, 2010 - - Modify the last 2-digit of 12NC Version 4 Jun. 24, 2010 - - Dimension on 1206 case size updated Version 3 Apr. 22, 2010 - - Dimension updated Version 2 Feb. 04, 2010 - - The statement of "Halogen Free" on the cover added Version 1 Nov. 04, 2009 - - Ordering code updated - Dimension updated Version 0 Apr. 15, 2009 - - New datasheet for general purpose and high capacitance Y5V series with RoHS compliant - Replace the "6.3V to 50V" part of pdf files: Y5V_6.3V_10V_9_Preliminary, Y5V_10V-to-50V_10_Preliminary, Y5V_16V_25V_50V_11 - Combine 0201 from pdf files: UP-NP0X5RX7RY5V_0201_6.3-to-50V_2 and UY-NPOX5RX7RY5V_0201_6.3-to-50V_2 - Define global part number - Description of "Halogen Free compliant" added - Test method and procedure updated www.yageo.com Oct 05, 2021 V.11