VDR-14D101KJ

VDR Varistor 14D SERIES 嵩隆力上 SONGLONG LISHANG METAL OXIDE VARISTOR – 14D SERIES FEATURES * Wide operating voltage (V1mA) range from 18V to 1800V. * Fast responding to transient over-voltage. * Large absorbing transient energy capability. * Low clamping ratio and no follow-on current. * Meets MSL level 1, per J-STD-020 * Safety number : CUL- E317616 VDE- 40028836 CQC-12001078540 ISO9001-2018 APPLICATION *Transistor, Diode, IC, Thyristor or Triac semiconductor protection. * Surge protection in consumer electronics. * Surge protection in industrial electronics. * Surge protection in electronic home appliances, gas and petroleum appliances. * Relay and electromagnetic valve surge absorption. General Characteristics Definition *Operating Temperature: (-40 ℃ ~ +85 ℃ ) o & ( -40 ℃ ~ +125 ℃) o *Storage Temperature: (-40 C ~ +125 C) *Working Surface Temperature: +115 C > 100M Ω Flame-Retardant to UL 94 V-0 o *Insulation Resistance: *Coating (Epoxy Resin): Material *Coating: Epoxy Resin *Lead Wire: The Copper Wire *Electrode: *Disk: Silver Solder Zinc Oxide PART NUMBER CODE VDR Brand Mark □□ D □□□ K Element Diameter Type: D: Disk , S: Square Varistor Voltage Tolerance : K±10%, L±15% □ □□ Sapce:Straight 85℃ H:125℃ C:Crimped , Y:Y kink I:Inner,Tor G :Plaster Lead Form : Short leg : NO : □.□ E: 4KV2KA S:6KV/3KA Y:10KV/5KA =ABCDEF Times □ J:High Surge & High Energy PH=Ultra Surge Taping : TA : Ammo, TR : Reel Page-1 VDR Varistor 14D SERIES 嵩隆力上 SONGLONG LISHANG Part No. Part No. T Max. D Max. VDR-14D180L VDR-14D220K VDR-14D270K VDR-14D330K VDR-14D390K VDR-14D470K VDR-14D560K VDR-14D680K VDR-14D820K VDR-14D101K VDR-14D121K VDR-14D151K VDR-14D181K VDR-14D201K VDR-14D221K VDR-14D241K VDR-14D271K VDR-14D301K VDR-14D331K VDR-14D361K VDR-14D391K VDR-14D431K VDR-14D471K VDR-14D511K VDR-14D561K VDR-14D621K VDR-14D681K VDR-14D751K VDR-14D781K VDR-14D821K VDR-14D911K VDR-14D102K VDR-14D112K VDR-14D122K VDR-14D142K VDR-14D162K VDR-14D182K VDR-14D180LJ VDR-14D220KJ VDR-14D270KJ VDR-14D330KJ VDR-14D390KJ VDR-14D470KJ VDR-14D560KJ VDR-14D680KJ VDR-14D820KJ VDR-14D101KJ VDR-14D121KJ VDR-14D151KJ VDR-14D181KJ VDR-14D201KJ VDR-14D221KJ VDR-14D241KJ VDR-14D271KJ VDR-14D301KJ VDR-14D331KJ VDR-14D361KJ VDR-14D391KJ VDR-14D431KJ VDR-14D471KJ VDR-14D511KJ VDR-14D561KJ VDR-14D621KJ VDR-14D681KJ VDR-14D751KJ VDR-14D781KJ VDR-14D821KJ VDR-14D911KJ VDR-14D102KJ VDR-14D112KJ VDR-14D122KJ VDR-14D142KJ VDR-14D162KJ VDR-14D182KJ 4.5 4.6 4.7 4.9 4.8 4.9 5.0 5.2 4.1 4.3 4.4 4.2 4.3 4.4 4.5 4.6 4.7 4.8 5.0 5.2 5.2 5.4 5.9 6.1 6.4 6.8 7.1 7.2 7.3 7.5 7.6 8.0 8.5 9.0 10.5 11.0 12.0 16.5 S H Max. I/C/Y 21.0 23.0 L min. 20.0 F ±0.8 d + 0.05 7.5 0.8 Page-2 VDR Varistor 14D SERIES 嵩隆力上 SONGLONG LISHANG ELECTRICAL CHARACTERISTIC Part Number Maximum Varistor Withstanding Energy Allowable Voltage Maximum Clamping Voltage Voltage Surge Current 10/1000μS AC (V) DC (V) V1mA(V) IP(A) VC(V) I(A) I(A) I(A) I(A) 36 1000 2000 4.0 10 43 1000 2000 10 53 1000 2000 33(29.5~36.5) 10 65 1000 31 39(35 ~43) 10 77 30 38 47(42~52) 10 35 45 56(50~62) 10 14D680KJ 40 56 68(61~75) 10 14D820K 14D820KJ 50 65 82(74~90) 14D101K 14D101KJ 60 85 14D121K 14D121KJ 75 14D151K 14D151KJ 14D181K Typical Rated Capacitance Powe (Reference) (W) @1KHzPF 7.0 0.1 1100 5.0 8.0 0.1 9100 6.0 10.0 0.1 7400 2000 7.5 12.0 0.1 6100 1000 2000 8.6 13.0 0.1 5100 93 1000 2000 10.0 17.0 0.1 4300 110 1000 2000 11.0 20.0 0.1 3600 135 1000 2000 14.0 24.0 0.1 2900 50 135 4500 6000 22.0 27.0 0.6 2400 100(90~110) 50 165 4500 6000 28.0 33.0 0.6 2000 100 120(108~132) 50 200 4500 6000 32.0 40.0 0.6 1700 95 125 150(135~165) 50 250 4500 6000 40.0 53.0 0.6 1300 14D181KJ 115 150 180(162~198) 50 300 4500 6000 50.0 60.0 0.6 1100 14D201K 14D201KJ 130 170 200(185~225) 50 330 4500 6000 57.0 70.0 0.6 1000 14D221K 14D221KJ 140 180 220(198~242) 50 360 4500 6000 60.0 78.0 0.6 830 14D241K 14D241KJ 150 200 240(216~264) 50 395 4500 6000 63.0 84.0 0.6 740 14D271K 14D271KJ 175 225 270(243~297) 50 455 4500 6000 70.0 99.0 0.6 670 14D301K 14D301KJ 190 250 300(270~330) 50 505 4500 6000 77.0 108 0.6 610 14D331K 14D331KJ 210 275 330(297~363) 50 550 4500 6000 85.0 115 0.6 560 14D361K 14D361KJ 230 300 360(324~396) 50 595 4500 6000 93.0 130 0.6 510 14D391K 14D391KJ 250 320 390(351~429) 50 650 4500 6000 100 140 0.6 460 14D431K 14D431KJ 275 350 430(387~473) 50 710 4500 6000 115 155 0.6 230 14D471K 14D471KJ 300 385 470(423~517) 50 775 4500 6000 125 175 0.6 430 14D511K 14D511KJ 320 415 510(459~561) 50 845 4500 6000 126 180 0.6 390 14D561K 14D561KJ 350 460 560(504~616) 50 920 4500 6000 127 185 0.6 360 14D621K 14D621KJ 385 505 620(558~682) 50 1025 4500 6000 128 190 0.6 320 14D681K 14D681KJ 420 560 680(612~748) 50 1120 4500 6000 130 200 0.6 290 14D751K 14D751KJ 460 615 750(675~825) 50 1240 4500 6000 143 210 0.6 270 14D781K 14D781KJ 485 640 780(702~858) 50 1290 4500 6000 148 220 0.6 260 14D821K 14D821KJ 510 670 820(738~902) 50 1355 4500 6000 157 235 0.6 240 14D911K 14D911KJ 550 745 910(819~1001) 50 1500 4500 6000 175 255 0.6 220 14D102K 14D102KJ 625 825 1000(900~1100) 50 1650 4500 6000 190 280 0.6 200 14D112K 14D112KJ 680 895 1100(990~1210) 50 1815 4500 6000 213 310 0.6 180 14D122K 14D122KJ 750 990 1200(1080~1320) 50 1980 4500 6000 232 324 0.6 160 14D142K 14D142KJ 880 1140 1400(1260~1540) 50 2310 4500 6000 238 327 0.6 150 14D162K 14D162KJ 1000 1280 1600(1400~1760) 50 2640 4500 6000 243 331 0.6 140 14D182K 14D182KJ 1100 1465 1800(1620~1980) 50 2970 4500 6000 250 335 0.6 130 Standard High Surge 14D180L 14D180LJ 11 14 18(15.0~21.6) 10 14D220K 14D220KJ 14 18 22(19.5~26.0) 14D270K 14D270KJ 17 22 27(24-31) 14D330K 14D330KJ 20 26 14D390K 14D390KJ 25 14D470K 14D470KJ 14D560K 14D560KJ 14D680K Standard High Surge Standard High Surge The tolerance of varistor voltage between 18V and 68V is more than 10%. Page-3 嵩隆力上 SONGLONG LISHANG Mechanical Ratings VDR Varistor 14D SERIES Reliability Test Performance Requirements Test Parameter Test Condition / Description Terminal Pull Strength After gradually applying the load specified below and keeping the unit fixed for ten seconds, the terminal shall be visually examined for any damage. The unit shall be secured with its terminal kept vertical and the weight specified below be applied in the axial direction. The Terminal Bending terminal shall gradually be bent by 90° in one direction, then 90° Strength in the opposite direction, and again back to the original position. The damage of the terminal shall be visually examined. Vibration Solderingsolderability SolderingResistance to Solder Heat Diameter Loading 0.6mm 1.0 Kg 0.8mm 1.0 Kg 1.0mm 2.0 Kg Diameter Loading 0.6mm 0.5 Kg 0.8mm 0.5 Kg 1.0mm 1.0 Kg The Specimen shall be vibrated by its lead wires with a total amplitude of 1.5㎜ and a varying frequency of 10~55~10HZ(each minutes) for a period of 2 hours respectively in each X,Yand Z directions. No visible damage No visible damage No visible damage △VB/VB%≦±5% After dipping the terminal to depth of approximately 3㎜ from the specimen in a soldering Terminations shall bath of 260℃ for 10±1(D5: 5±1) seconds. Thereafter the terminal shall be visually be uniformly tinned examined. After preheating the specimen, the specimen shall be completely immersed into a soldering bath having a temperature of 260±5℃ for 10±1 (D5: 5±1) seconds or iron of 400±5℃ for 3±0.5 seconds. There after the change of Vb and mechanical damage shall be examined. No visible damage △VB/VB%≦±5% ENVIRONMENTAL RATINGS The specimen shall be applied continuously the maximum allowable voltage at the specified conditions for specified period and then stored at room temperature and normal Dry Heat Loading humidity over 2 hours. Thereafter, the change of Vb and mechanical damage shall be △VB/VB%≦±10% examined. Ambient temp：125±2℃ ; Period：1000±24hours. High Temperature In a drying oven without load. Storage Ambient temp：125±2℃ ; period：1000±24hours Damp Heat Loading △VB/VB%≦±5% The specimen shall be applied continuously the maximum allowable voltage at the specified conditions for specified period and then stored at room temperature and normal humidity over 2 hours. Thereafter, the change of Vb and mechanical damage shall be △VB/VB%≦±10% examined. Ambient condition：40±2℃ , 90 to 95%R.H. ; period：1000±24 hours Step Temperature Cycle Condition the specimen to each temperature form step 1 to step 4 in this order for the period shown in the table of specifications. The change of Vb and mechanical damage shall be examined after 2 hours. o Period o Temp C 1 -40+3 C 30 min. 2 Room Temp 15 min. 3 85+2 C 30 min. 4 Room Temp 15 min. o Surge Lifetime Rating The change of Vb shall be measured after the impulse listed below is applied 10,000 times continuously with the interval of ten seconds at room temperature. Voltage Proof Voltage：2500VAC Leakage Current≦0.5mA Time：60 Seconds No visible damage △VB/VB%≦±10% No visible damage △VB/VB%≦±10% No Breakdown Page-4 VDR Varistor 14D SERIES 嵩隆力上 SONGLONG LISHANG MARKING CODE 1 SongLong Lishang Logo 2 Disk Size 3 CUL Accreditation Logo 4 “Y” &“M” Product Line Code 5 Varistor Voltage 6 VDE Accreditation Logo 7 Energy and frequency of combined wave “J” is High Surge Code,not “J” is Standard Surge “H” is High temperature range ,not “H” is Standard Packaging specification / bulk packaging quantity Unit:Pcs Dimension Part No. Bag Small Carton Carton 14D 180L to 112K 500 3,000 6,000 14D (Short leg) 180L to 112K 500 4,000 8,000 Page-5