VDR Varistor
20D SERIES
嵩隆力上
SONGLONG LISHANG
METAL OXIDE VARISTOR – 20D SERIES
FEATURES
* Wide operating voltage (V1mA) range from 18V to 1800V.
* Fast responding to transient over-voltage.
* Large absorbing transient energy capability.
* Low clamping ratio and no follow-on current.
* Meets MSL level 1, per J-STD-020
* Safety number : CUL- E317616
VDE- 40028836
CQC-12001076476
ISO9001-2018
APPLICATION
*Transistor, Diode, IC, Thyristor or Triac semiconductor protection.
* Surge protection in consumer electronics.
* Surge protection in industrial electronics.
* Surge protection in electronic home appliances, gas and petroleum appliances.
* Relay and electromagnetic valve surge absorption.
General Characteristics Definition
*Operating Temperature:
(-40 ℃ ~ +85 ℃ )
*Storage Temperature:
(-40 oC ~ +125 oC)
*Working Surface Temperature:
*Insulation Resistance:
+115 oC
> 100M Ω
*Coating (Epoxy Resin):
Flame-Retardant to UL 94 V-0
Material
*Coating:
Epoxy Resin
*Lead Wire:
The Copper Wire
*Electrode:
Silver
*Disk:
Zinc Oxide
&
( -40 ℃ ~ +125 ℃)
Solder
PART NUMBER CODE
VDR
Brand Mark
□□
D
□□□
K
□
□□
Sapce:Straight 85℃
H:125℃
Element Diameter
C:Crimped , Y:Y kink
Type: D: Disk , S: Square
I:Inner,Tor G :Plaster
Varistor Voltage
Tolerance : K±10%, L±15%
Lead Form :
Short leg : NO :
□.□
E: 4KV2KA S:6KV/3KA Y:10KV/5KA
□=ABCDEF Times
J:High Surge & High Energy
PH=Ultra Surge
Taping : TA : Ammo, TR : Reel
Page-1
VDR Varistor
20D SERIES
嵩隆力上
SONGLONG LISHANG
Part No.
Part No.
VDR-20D180L VDR-20D180LJ
VDR-20D220K VDR-20D220KJ
VDR-20D270K VDR-20D270KJ
VDR-20D330K VDR-20D330KJ
VDR-20D390K VDR-20D390KJ
VDR-20D470K VDR-20D470KJ
VDR-20D560K VDR-20D560KJ
VDR-20D680K VDR-20D680KJ
VDR-20D820K VDR-20D820KJ
VDR-20D101K VDR-20D101KJ
VDR-20D121K VDR-20D121KJ
VDR-20D151K VDR-20D151KJ
VDR-20D181K VDR-20D181KJ
VDR-20D201K VDR-20D201KJ
VDR-20D221K VDR-20D221KJ
VDR-20D241K VDR-20D241KJ
VDR-20D271K VDR-20D271KJ
VDR-20D301K VDR-20D301KJ
VDR-20D331K VDR-20D331KJ
VDR-20D361K VDR-20D361KJ
VDR-20D391K VDR-20D391KJ
VDR-20D431K VDR-20D431KJ
VDR-20D471K VDR-20D471KJ
VDR-20D511K VDR-20D511KJ
VDR-20D561K VDR-20D561KJ
VDR-20D621K VDR-20D621KJ
VDR-20D681K VDR-20D681KJ
VDR-20D751K VDR-20D751KJ
VDR-20D781K VDR-20D781KJ
VDR-20D821K VDR-20D821KJ
VDR-20D911K VDR-20D911KJ
VDR-20D102K VDR-20D102KJ
VDR-20D112K VDR-20D112KJ
VDR-20D122K VDR-20D122KJ
VDR-20D142K VDR-20D142KJ
VDR-20D162K VDR-20D162KJ
VDR-20D182K VDR-20D182KJ
T Max.
D Max.
4.5
4.6
4.7
4.9
4.8
4.9
5.0
5.2
4.1
4.3
4.4
4.2
4.3
4.4
4.5
4.6
4.7
4.8
5.0
5.2
5.2
5.4
5.9
6.1
6.4
6.8
7.1
7.2
7.3
7.5
7.6
8.0
8.5
9.0
10.5
11.0
12.0
23.0
S
H Max.
I/C/Y
26.5
28.0
L min.
F
d + 0.05
20.0
7.5±0.8
10±1.0
0.8
1.0
Page-2
VDR Varistor
20D SERIES
嵩隆力上
SONGLONG LISHANG
ELECTRICAL CHARACTERISTIC
Part Number
Maximum
Varistor
Withstanding
Energy
Allowable
Voltage
Maximum
Clamping
Voltage
Voltage
Surge Current
10/1000μS
IP(A) VC(V)
I(A)
I(A)
I(A)
I(A)
36
2000
3000
11
20
43
2000
3000
20
53
2000
3000
33(29.5~36.5)
20
65
2000
31
39(35 ~43)
20
77
30
38
47(42~52)
20
35
45
56(50~62)
20
20D680KJ
40
56
68(61~75)
20
20D820K
20D820KJ
50
65
82(74~90)
20D101K
20D101KJ
60
85
20D121K
20D121KJ
75
20D151K
20D151KJ
20D181K
Standard
High Surge
AC (V)
DC (V)
V1mA(V)
20D180L
20D180LJ
11
14
18(15.0~21.6)
20
20D220K
20D220KJ
14
18
22(19.5~26.0)
20D270K
20D270KJ
17
22
27(24-31)
20D330K
20D330KJ
20
26
20D390K
20D390KJ
25
20D470K
20D470KJ
20D560K
20D560KJ
20D680K
Typical
Rated Capacitance
Powe (Reference)
(W)
@1KHzPF
13
0.2
28500
14
16
0.2
18500
16
19
0.2
13000
3000
23
24
0.2
11500
2000
3000
26
28
0.2
8500
93
2000
3000
30
34
0.2
7400
110
2000
3000
41
46
0.2
6500
135
2000
3000
46
49
0.2
5800
100
135
6500
10000
38
56
1.0
4900
100(90~110)
100
165
6500
10000
45
70
1.0
4000
100
120(108~132)
100
200
6500
10000
55
85
1.0
3300
95
125
150(135~165)
100
250
6500
10000
70
106
1.0
2700
20D181KJ
115
150
180(162~198)
100
300
6500
10000
85
130
1.0
2200
20D201K
20D201KJ
130
170
200(185~225)
100
330
6500
10000
95
140
1.0
2000
20D221K
20D221KJ
140
180
220(198~242)
100
360
6500
10000
100
155
1.0
1800
20D241K
20D241KJ
150
200
240(216~264)
100
395
6500
10000
108
168
1.0
1650
20D271K
20D271KJ
175
225
270(243~297)
100
455
6500
10000
127
190
1.0
1500
20D301K
20D301KJ
190
250
300(270~330)
100
505
6500
10000
136
210
1.0
1300
20D331K
20D331KJ
210
275
330(297~363)
100
550
6500
10000
150
228
1.0
1200
20D361K
20D361KJ
230
300
360(324~396)
100
595
6500
10000
163
255
1.0
1100
20D391K
20D391KJ
250
320
390(351~429)
100
650
6500
10000
180
275
1.0
1000
20D431K
20D431KJ
275
350
430(387~473)
100
710
6500
10000
190
305
1.0
930
20D471K
20D471KJ
300
385
470(423~517)
100
775
6500
10000
220
350
1.0
850
20D511K
20D511KJ
320
415
510(459~561)
100
845
6500
10000
225
360
1.0
780
20D561K
20D561KJ
350
460
560(504~616)
100
920
6500
10000
230
380
1.0
710
20D621K
20D621KJ
385
505
620(558~682)
100
1025
6500
10000
235
390
1.0
650
20D681K
20D681KJ
420
560
680(612~748)
100
1120
6500
10000
240
400
1.0
600
20D751K
20D751KJ
460
615
750(675~825)
100
1240
6500
10000
255
420
1.0
530
20D781K
20D781KJ
485
640
780(702~858)
100
1290
6500
10000
265
440
1.0
510
20D821K
20D821KJ
510
670
820(738~902)
100
1355
6500
10000
282
460
1.0
500
20D911K
20D911KJ
550
745
910(819~1001)
100
1500
6500
10000
310
510
1.0
440
20D102K
20D102KJ
625
825
1000(900~1100)
100
1650
6500
10000
342
565
1.0
400
20D112K
20D112KJ
680
895
1100(990~1210)
100
1815
6500
10000
383
620
1.0
360
20D122K
20D122KJ
750
990 1200(1080~1320)
100
1980
6500
10000
408
660
1.0
350
20D142K
20D142KJ
880
1140 1400(1260~1540)
100
2310
6500
10000
532
784
1.0
340
20D162K
20D162KJ
1000 1280 1600(1400~1760)
100
2640
6500
10000
606
896
1.0
330
20D182K
20D182KJ
1100 1465 1800(1620~1980)
100
2970
6500
10000
625
990
1.0
320
Standard High Surge Standard High Surge
The tolerance of varistor voltage between 18V and 68V is more than 10%.
20D180L & 20D220K does not have VDE certification
Page-3
嵩隆力上
SONGLONG LISHANG
VDR Varistor
20D SERIES
Reliability Test
Mechanical Ratings
Performance
Requirements
Test Parameter Test Condition / Description
Terminal Pull
Strength
After gradually applying the load specified below and keeping
the unit fixed for ten seconds, the terminal shall be visually
examined for any damage.
The unit shall be secured with its terminal kept vertical and the
weight specified below be applied in the axial direction. The
Terminal Bending terminal shall gradually be bent by 90° in one direction, then
Strength
90° in the opposite direction, and again back to the original
position. The damage of the terminal shall be visually
examined.
Vibration
Solderingsolderability
SolderingResistance to
Solder Heat
Diameter
Loading
0.6mm
1.0 Kg
0.8mm
1.0 Kg
1.0mm
2.0 Kg
Diameter
Loading
0.6mm
0.5 Kg
0.8mm
0.5 Kg
1.0mm
1.0 Kg
No visible damage
No visible damage
The Specimen shall be vibrated by its lead wires with a total amplitude of 1.5㎜ and a
varying frequency of 10~55~10HZ(each minutes) for a period of 2 hours respectively in
each X,Yand Z directions.
No visible damage
△VB/VB%≦±5%
After dipping the terminal to depth of approximately 3㎜ from the specimen in a
soldering bath of 260℃ for 10±1(D5: 5±1) seconds. Thereafter the terminal shall be
visually examined.
Terminations shall
be uniformly tinned
After preheating the specimen, the specimen shall be completely immersed into a
soldering bath having a temperature of 260±5℃ for 10±1 (D5: 5±1) seconds or iron of
400±5℃ for 3±0.5 seconds. There after the change of Vb and mechanical damage shall
be examined.
No visible damage
△VB/VB%≦±5%
ENVIRONMENTAL RATINGS
The specimen shall be applied continuously the maximum allowable voltage at the
specified conditions for specified period and then stored at room temperature and
Dry Heat Loading normal humidity over 2 hours. Thereafter, the change of Vb and mechanical damage
shall be examined.
Ambient temp:125±2℃ ;
Period:1000±24hours.
△VB/VB%≦±10%
High Temperature In a drying oven without load.
Storage
Ambient temp:125±2℃ ; period:1000±24hours
△VB/VB%≦±5%
Damp Heat
Loading
The specimen shall be applied continuously the maximum allowable voltage at the
specified conditions for specified period and then stored at room temperature and
normal humidity over 2 hours. Thereafter, the change of Vb and mechanical damage
shall be examined.
Ambient condition:40±2℃ , 90 to 95%R.H. ; period:1000±24 hours
Step
Temperature
Cycle
Condition the specimen to each temperature form step 1
to step 4 in this order for the period shown in the table
of specifications. The change of Vb and mechanical
damage shall be examined after 2 hours.
TempoC
Period
1
-40+3 C
30 min.
2
Room Temp
15 min.
3
85+2 C
30 min.
4
Room Temp
15 min.
o
o
Surge Lifetime
Rating
The change of Vb shall be measured after the impulse listed below is applied 10,000
times continuously with the interval of ten seconds at room temperature.
Voltage Proof
Voltage:2500VAC
Leakage Current≦0.5mA
Time:60 Seconds
△VB/VB%≦±10%
No visible damage
△VB/VB%≦±10%
No visible damage
△VB/VB%≦±10%
No Breakdown
Page-4
VDR Varistor
20D SERIES
嵩隆力上
SONGLONG LISHANG
MARKING CODE
1 SongLong Lishang Logo
2 Disk Size
3 CUL Accreditation Logo
4 “Y” &“M” Product Line Code
5 Varistor Voltage
6 VDE Accreditation Logo
7 Energy and frequency of combined wave
“J” is High Surge Code,not “J” is Standard Surge
“H” is High temperature range ,not “H” is Standard
Packaging specification / bulk packaging quantity
Unit:Pcs
Dimension
Part No.
Bag
Small Carton
Carton
20D
180L to 112K
250
1,500
3,000
20D (Short leg)
180L to 112K
250
2,000
4,000
Page-5
很抱歉,暂时无法提供与“VDR-20D471K”相匹配的价格&库存,您可以联系我们找货
免费人工找货- 国内价格
- 5+1.49624
- 50+1.22408
- 250+0.98432
- 500+0.83884
- 2500+0.77404