HR-SCUF9

High-Rate Discharge Model HR-SCU Size : SC Data sheet Dimensions Capacity Nominal1) 3000 mAh Minimum1) 2700 mAh 1)Single cell capacity under the following condition. Charge : 270 mA × 16 hours, Discharge : 540 mA(E.V.=1.00 V) at 20 °C +0 mm 23.0−1.0 General Specifications +0 mm 43.5−1.5 Nominal Voltage 1.2 V End Voltage 1.00 V Charging Current x Time Ambient Temp. 3000 mA x about 1.1 hours Fast Charge 2) Charge Fast Charge 2) Condition3) 0 °C ～ ＋40 °C Discharge Recommended Condition3) 0 °C ～ ＋50 °C 45 % ～ 85 % Relative Humidity 4) 2)Use recommended charging system. 3)Charge or discharge on outside the recommended temperature range may generate the battery degradation. 4)No water condensation. Storage Conditions Dimensions (including tube) Diameter 23.0 ＋0/ －1.0 mm Height 43.5 ＋0/ －1.5 mm Approx. Weight (including tube) 59 g Approx. Internal Impedance at 1kHz 20ﾟC 5) 7 mΩ 5) After 3 cycles of charge and discharge under the conditions of 1), followed by the measurement 1~4 hours later. Nominal Charge Characteristics 1.7 －20 °C ～ ＋50 °C Less than 90 days －20 °C ～ ＋40 °C Less than 1 year －20 °C ～ ＋30 °C 45 % ～ 85 % Relative Humidity 6) 6)No water condensation. Nominal Discharge Characteristics 1.6 1.8 Char Ambient Temp. Less than 30 days Charge : 3000mA (-ΔV=10mV) Char 0.6A Ambient Temp. : 0, 25, 40ﾟC 3A 10A 20A 30A Cell Voltage (V) 1.6 1.5 1.4 1.3 1.2 0ﾟC 25ﾟC 40ﾟC Cell Voltage (V) 1.4 1.2 1.0 0.8 1.1 1.0 Charge : 3000mA (-ΔV=10mV) Rest : 3hours Discharge : 0.6A, 3A, 10A 20A, 30A (E.V.=0.80V) Ambient Temp. : 25ﾟC 0.6 and0.6 lifespan are affected by conditions. 0 500 1000 0.0・Battery 0.2performance 0.4 0.8 greatly1.0 1.2usage and temperature 1500 2000 ・Test results vary depending on individual batteries. Discharge Capacity Charge Time (hours) ・Specific values included in this material are intended to describe performance. They are not guaranteed. ・Single cell performance and lifespan are greatly affected by usage and temperature conditions. ・Test results vary depending on individual cells. ・Each values included in this material are intended to describe performance. They are not guaranteed. 2500 3000 (mAh) ZKH