DATA SHEET
SURFACE MOUNT MULTILAYER
CERAMIC CAPACITORS
Automotive grade
NP0/X7R
6.3 V TO 2000 V
Product Specification – January 14, 2022 V.17
0.2 pF to 680nF
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
SCOPE
ORDERING INFORMATION - GLOBAL PART NUMBER
This specification describes
Automotive grade chip capacitors
with lead-free terminations and
used for automotive equipments.
All part numbers are identified by the series, size, tolerance, TC material,
packing style, voltage, process code, termination and capacitance value.
GLOBAL PART NUMBER
AC
APPLICATIONS
All general purpose applications
under normal operation and
usage conditions for automotive
equipments.
XXXX X X XXX X
(1)
(2) (3) (4)
B
(5)
X XXX
(6) (7)
(1) SIZE – INCH BASED (METRIC)
0201 (0603) / 0402 (1005) / 0603 (1608) / 0805 (2012) / 1206 (3216)/ 1210 (3225) /
1812 (4532)
(2) TOLERANCE
FEATURES
NPO(< 10 pF)
NPO(≥ 10 pF)
X7R
AEC-Q200 qualified
MSL class: MSL 1
AC series soldering is
compliant with J-STD-020D
High component and
equipment reliability
The capacitors are 100%
performed by automatic optical
inspection prior to taping.
B = ± 0.1 pF
F = ± 1%
J = ± 5%
C = ± 0.25 pF
G = ± 2%
K = ± 10%
D = ± 0.5 pF
J = ± 5%
M = ± 20%
Note: Capacitance tolerance ±5% doesn’t available for full X7R range,
please contact local sale before order.
(3) PACKING STYLE (SEE TABLE. 9 FOR DETAIL)
R = Paper/PE taping reel; Reel 7 inch
K = Blister taping reel; Reel 7 inch
P = Paper/PE taping reel; Reel 13 inch
F = Blister taping reel; Reel 13 inch
(4) TC MATERIAL
NPO
X7R
(5) RATED VOLTAGE
5 = 6.3 V
6 = 10 V
B = 500 V
7 = 16 V
C = 1000 V
D = 2000 V
8 = 25 V
Z = 630 V
9 = 50 V
0 = 100 V
A = 200 V
Y = 250 V
6) PROCESS
N = NP0
B = X7R
(7) CAPACITANCE VALUE
2 significant digits+number of zeros
The 3rd digit signifies the multiplying factor, and letter R is decimal point
Example: 121 = 12 x 101 = 120 pF
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
CONSTRUCTION
The capacitor consists of a
rectangular block of ceramic
dielectric in which a number of
interleaved metal electrodes are
contained. This structure gives rise
to a high capacitance per unit
volume.
The inner electrodes are
connected to the two end
terminations and finally covered
with a layer of plated tin (Matte
Sn). The terminations are leadfree. A cross section of the
structure is shown in Fig.1.
terminations
electrodes
MLB457
ceramic material
Fig. 1 Surface mounted multilayer ceramic capacitor construction
OUTLINES
DIMENSION
Table 1 For outlines see fig. 2
For dimension see Table 1
TYPE
L1 (mm)
W (mm)
T (MM)
0201
0.6± 0.03
0.3± 0.03
0402
1.0± 0.05
0603
0805
L2 / L3 (mm)
L4 (mm)
min.
max.
min.
0.3± 0.03
0.10
0.20
0.20
0.5 ± 0.05
0.5± 0.05
0.15
0.35
0.30
1.6± 0.10
0.8± 0.10
0.8± 0.10
0.20
0.60
0.40
2.0± 0.10
1.25± 0.10
0.25
0.75
0.70
2.0± 0.20
1.25± 0.20
3.2± 0.15
1.6± 0.15
0.25
0.75
1.40
0.25
0.75
1.40
0.25
0.75
2.20
0.25
0.75
2.20
0.25
0.75
3.40
0.6± 0.10
0.85± 0.10
1.25± 0.20
Fig. 2 Surface mounted multilayer
ceramic capacitor dimension
0.6± 0.10
0.85± 0.10
1.00± 0.10
1206
3.2± 0.30
1.6± 0.20
1.15± 0.10
1.25± 0.20
1.6± 0.20
1210
1808
3.2± 0.30
1.6± 0.30
1.6± 0.30
3.2± 0.20
2.5± 0.20
3.2± 0.30
2.5± 0.20
3.2± 0.40
2.5± 0.30
2.5± 0.20
4.5± 0.40
2.0± 0.30
1.25± 0.20
0.85± 0.10
1.25± 0.20
1.6± 0.20
2.0± 0.20
0.85± 0.10
1812
4.5± 0.40
3.2± 0.30
1.25± 0.20
1.60± 0.20
2020
5.7± 0.40
5.0± 0.30
0.85 ± 0.10
2.0± 0.20
1.25
1.25 ±
± 0.20
0.20
1.6
±
0.20
1.6 ± 0.20
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
CAPACITANCE RANGE & THICKNESS FOR NP0
Table 2 Sizes from 0201 to 0805
0201
0402
CAP.
0603
0805
0.2 pF
0.3± 0.03
0.47 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.56 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.68 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.82 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.0 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.2 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.5 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.8 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
2.2 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
2.7 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
3.3 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
3.9 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
4.7 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
5.6 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
6.8 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
8.2 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
10 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
12 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
15 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
18 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
22 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
27 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
33 pF
0.3± 0.03
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
39 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
47 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
56 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
68 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
82 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
100 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-12 series is on request
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
CAPACITANCE RANGE & THICKNESS FOR NP0
Table 3 Sizes from 0402 to 0805 (continued)
CAP.
0402
0603
0805
120 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
150 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
180 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
220 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.85± 0.1
270 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.85± 0.1
330 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.85± 0.1
390 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.85± 0.1
470 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.6± 0.1
0.85± 0.1
560 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.85± 0.1
0.85± 0.1
680 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.85± 0.1
0.85± 0.1
820 pF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.85± 0.1
0.85± 0.1
1.0 nF
0.5± 0.05
0.8± 0.1
0.8± 0.1
0.6± 0.1
0.85± 0.1
0.85± 0.1
1.2 nF
0.8± 0.1
0.8± 0.1
0.85± 0.1
0.85± 0.1
1.5 nF
0.8± 0.1
0.8± 0.1
0.85± 0.1
0.85± 0.1
1.8 nF
0.8± 0.1
0.8± 0.1
0.85± 0.1
0.85± 0.1
2.2 nF
0.8± 0.1
0.8± 0.1
1.25± 0.2
1.25± 0.2
2.7 nF
0.8± 0.1
1.25± 0.2
1.25± 0.2
3.3 nF
0.8± 0.1
1.25± 0.2
1.25± 0.2
3.9 nF
0.8± 0.1
1.25± 0.2
1.25± 0.2
4.7 nF
0.8± 0.1
1.25± 0.2
1.25± 0.2
5.6 nF
0.8± 0.1
1.25± 0.2
1.25± 0.2
6.8 nF
0.8± 0.1
1.25± 0.2
1.25± 0.2
8.2 nF
0.8± 0.1
1.25± 0.2
1.25± 0.2
10 nF
0.8± 0.1
1.25± 0.2
1.25± 0.2
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-12 series is on request
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
CAPACITANCE RANGE & THICKNESS FOR NP0
Table 4 Sizes from 1206 to 1210
CAP.
1210
1206
50 V
100 V 200 V / 250 V
500 V
630 V
1000 V
2000 V
10 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
12 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
15 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
18 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
22 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
27 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
33 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
39 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
47 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
56 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
68 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
82 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
100 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
120 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
150 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
180 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
220 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
270 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
330 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
390 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
470 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
560 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
680 pF
0.6± 0.1
0.6± 0.1
0.6± 0.1
0.6± 0.1
1.25± 0.2
820 pF
0.6± 0.1
0.6± 0.1
0.85± 0.1 0.85± 0.1
1.25± 0.2
1.0 nF
0.6± 0.1
0.6± 0.1
0.85± 0.1 0.85± 0.1
1.25± 0.2
1.2 nF
0.6± 0.1
0.6± 0.1
1.5 nF
0.6± 0.1
0.6± 0.1
1.8 nF
0.6± 0.1
2.2 nF
2.7 nF
50 V
100 V 200 V / 250 V
500 V
1.25± 0.2
1.25± 0.2
1.25± 0.2 1.25± 0.2
0.85± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2 1.25± 0.2
0.85± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2 1.25± 0.2
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2 1.25± 0.2
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
0.6± 0.1
0.6± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-12 series is on request
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
CAPACITANCE RANGE & THICKNESS FOR X7R
Table 5
CAP.
Sizes from 0201 to 0603
0201
25V
0603
0402
50 V
10V
16 V
25 V
50 V
100 V
10V
16 V
25 V
50 V
100 V
1.0 nF 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
1.5 nF 0.3± 0.03
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
2.2 nF 0.3± 0.03
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
3.3 nF 0.3± 0.03
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
4.7 nF 0.3± 0.03
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
6.8 nF 0.3± 0.03
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
10 nF 0.3± 0.03
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
15 nF
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
22 nF
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
33 nF
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
47 nF
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
68 nF
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
100 nF
0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
150 nF
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
220 nF
0.8± 0.1
0.8± 0.1
0.8± 0.1
0.8± 0.1
330 nF
0.8± 0.1
0.8± 0.1
0.8± 0.1
470 nF
0.8± 0.1
0.8± 0.1
0.8± 0.1
680 nF
0.8± 0.1
0.8± 0.1
0.8± 0.1
100 pF 0.3± 0.03 0.3± 0.03
150 pF 0.3± 0.03 0.3± 0.03
220 pF 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
330 pF 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
470 pF 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
680 pF 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-6 series is on request
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
CAPACITANCE RANGE & THICKNESS FOR X7R
Table 6
Size 0805
0805
CAP.
10 V
16 V
25 V
50 V
100 V
200 V / 250 V
500 V
1.0 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.5 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
2.2 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
3.3 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
4.7 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
6.8 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
10 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
15 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
22 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
33 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
47 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
68 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
100 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
150 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
220 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
330 nF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
470 nF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
680 nF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
0.85± 0.1
1.25± 0.2
0.85± 0.1
1.25± 0.2
1.25± 0.2
1.25± 0.2
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-6 series is on request
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
CAPACITANCE RANGE & THICKNESS FOR X7R
Table 7
CAP.
Size 1206
1206
6.3 V
10V
16V
25V
50 V
100 V
200 V / 250 V
500 V
630 V
1000 V
220 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
330 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
470 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
680 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1 nF
1.25± 0.2
1.25± 0.2
1.25± 0.2
2.2 nF
1.25± 0.2
1.25± 0.2
4.7 nF
1.25± 0.2
1.25± 0.2
10 nF
1.25± 0.2
1.25± 0.2
22 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
33 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.60± 0.2
47 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.60± 0.2
68 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
1.60± 0.2
100 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
1.60± 0.2
150 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
1.25± 0.2
220 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
1.25± 0.2
330 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.60± 0.2
1.60± 0.2
470 nF
1.00± 0.1
1.00± 0.1
1.00± 0.1
1.00± 0.1
1.60± 0.2
1.60± 0.2
680 nF
1.15± 0.1
1.15± 0.1
1.15± 0.1
1.60± 0.2
1.60± 0.2
1.60± 0.2
Table 8
Size 1210
1812
1210
CAP.
6.3V
10 V
16 V
25 V
50V
100 V
200 V / 250 V
50V
100V
100 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
150 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
1.25± 0.2
220 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
1.25± 0.2
330 nF
0.85± 0.1
0.85± 0.1
0.85± 0.1
0.85± 0.1
1.25± 0.2
2.0± 0.2
470 nF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
2.0± 0.2
1.60± 0.2
1.60± 0.2
680 nF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
2.0± 0.2
1.60± 0.2
1.60± 0.2
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-6 series is on request
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
THICKNESS CLASSES AND PACKING QUANTITY
Table 9
THICKNESS
SIZE CODE
CLASSIFICATION
PACKING CODE
7 INCH
13 INCH
QUANTITY PER REEL
TAPE WIDTH
Ø 180 MM / 7 INCH
Paper
Blister
Ø 330 MM / 13 INCH
Paper
Blister
0201
0.3 ± 0.03 mm
R
P
8 mm
15,000
---
50,000
---
0402
0.5 ± 0.05 mm
R
P
8 mm
10,000
---
50,000
---
0603
0.8 ± 0.1 mm
R
P
8 mm
4,000
---
15,000
---
0.6 ± 0.1 mm
R
P
8 mm
4,000
---
20,000
---
0.85 ± 0.1 mm
R
P
8 mm
4,000
---
15,000
---
1.25 ± 0.2 mm
K
F
8 mm
---
3,000
---
10,000
0.6 ± 0.1 mm
R
P
8 mm
4,000
---
20,000
---
0.85 ± 0.1 mm
R
P
8 mm
4,000
---
15,000
---
1.0/1.15 ± 0.1 mm
K
F
8 mm
---
3,000
---
10,000
1.25 ± 0.2 mm
K
F
8 mm
---
3,000
---
10,000
1.60 ± 0.2 mm
K
F
8 mm
---
2,000
---
8,000
0.85 ± 0.1 mm
K
F
8 mm
---
4,000
---
10,000
1.15 ± 0.1 mm
K
F
8 mm
---
3,000
---
10,000
1.25 ± 0.2 mm
K
F
8 mm
---
3,000
---
10,000
2.0 ± 0.2 mm
K
8 mm
---
2,000
---
---
2.5 ± 0.2 mm
K
8 mm
---
1,000
---
---
0.6 / 0.85± 0.1 mm
K
12 mm
---
2,000
---
---
1.15± 0.1 mm
K
12 mm
---
1,000
---
---
1.25± 0.2 mm
K
12 mm
---
1,000
---
---
1.6 ± 0.2 mm
K
12 mm
---
2,000
---
---
0805
1206
1210
1812
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
PAPER/PE TAPE SPECIFICATION
Fig. 3 Paper/PE tape
Table 10 Dimensions of paper/PE tape for relevant chip size; see Fig.3
SIZE
Unit: mm
SYMBOL
CODE A0
B0
W
E
F
P0
(1)
P1
P2
Ø D0
K0
T
0.38 ± 0.05
(0.47 / 0.55)±0.10
0201
0.39 ± 0.06 0.70 ± 0.06
8.0 ± 0.20
1.75 ± 0.1
3.50 ± 0.05 4.0 ± 0.05
2.0 ± 0.05
2.0 ± 0.05
1.55 ± 0.03
0402
0.70 ± 0.15 1.21 ± 0.12
8.0 ± 0.20
1.75 ± 0.1
3.50 ± 0.05 4.0 ± 0.05
2.0 ± 0.05
2.0 ± 0.05
1.50 +0.1 /-0 (0.75 / 0.60)±0.10
(0.85 / 0.70)±0.10
0603
1.05 ± 0.14 1.86 ± 0.13
8.0 ± 0.20
1.75 ± 0.1
3.50 ± 0.05 4.0 ± 0.10
4.0 ± 0.10
2.0 ± 0.05
1.50 +0.1 /-0 (1.05 / 0.95 / 0.75)±0.10
(1.15 / 1.05 / 0.85)±0.10
0805
1.50 ± 0.15 2.26 ± 0.20
8.0 ± 0.20
1.75 ± 0.1
3.50 ± 0.05 4.0 ± 0.10
4.0 ± 0.10
2.0 ± 0.05
1.50 +0.1 /-0 (1.05 / 0.95 / 0.75)±0.10
(1.15 / 1.05 / 0.85)±0.10
1206
1.90 ± 0.15 3.50 ± 0.20
8.0 ± 0.20
1.75 ± 0.1
3.50 ± 0.05 4.0 ± 0.10
4.0 ± 0.10
2.0 ± 0.05
1.50 +0.1 /-0 (0.95 / 0.75)±0.10
(1.05 / 0.85)± 0.10
NOTE
1. P0 pitch tolerance over any 10 pitches is 0.2 mm
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
BLISTER TAPE SPECIFICATION
P0
D0
K0
P2
E
F
cover tape
W
B0
A0
T2
SCM015
D1
P1
K0: so chosen that the orientation of the component
cannot change
For W = 8 mm: T2 = 3.5 mm max.
For W = 12 mm: T2 = 6.5 mm max.
direction of unreeling
Fig. 4 Blister tape
Table 11 Dimensions of blister tape for relevant chip size; see Fig.4
SYMBOL
SIZE
A0
B0
CODE
Unit: mm
K0
W
E
F
Min. Max. Min. Max. Min. Max.
Ø D0
Ø D1
P0
(2)
P1
P2
T2
Min.
Min. Max.
0805
1.29
1.65
2.09
2.60
1.25
1.62
8.1 ± 0.20
1.75 ± 0.1
3.5 ± 0.05
1.5 +0.1/-0.0 1 +0.1/-0.0
4.0 ± 0.10
4.0 ± 0.10
2.0 ± 0.05
1.30
1.67
1206
1.65
2.12
3.30
3.75
1.22
2.15
8.1 ± 0.20
1.75 ± 0.1
3.5 ± 0.05
1.5 +0.1/-0.0 1 +0.1/-0.0
4.0 ± 0.10
4.0 ± 0.10
2.0 ± 0.05
1.27
2.20
1210
2.55
3.02
3.31
3.88
0.97
2.92
8.1 ± 0.20
1.75 ± 0.1
3.5 ± 0.05
1.5 +0.1/-0.0 1 +0.1/-0.0
4.0 ± 0.10
4.0 ± 0.10
2.0 ± 0.05
1.02
2.97
1808
2.05
2.55
4.80
5.45
1.30
2.45
12.1 ± 0.20
1.75 ± 0.1
5.5 ± 0.05
1.5 +0.1/-0.0 1.5 +0.1/-0.0 4.0 ± 0.10
4.0 ± 0.10
2.0 ± 0.05
1.35
2.50
1812
3.35
3.75
4.70
5.33
0.70
2.40
12.1 ± 0.20
1.75 ± 0.1
5.5 ± 0.05
1.5 +0.1/-0.0 1.5 +0.1/-0.0 4.0 ± 0.10
8.0 ± 0.10
2.0 ± 0.05
0.75
2.45
NOTE
1. Typical capacitor displacement in pocket
2. P0 pitch tolerance over any 10 pitches is ±0.2 mm
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
REEL SPECIFICATION
W2
C
N
A
HBK039
W1
Fig. 5 Reel
Table12 Reel dimensions; see Fig.5
TAPE WIDTH
SYMBOL
Unit: mm
A
N
C
W1
W2max.
8 (Ø 178 mm/7")
178 ± 1.0
60 ± 1.0
13 +0.50/-0.20
9.4 ± 1.5
14.4
8 (Ø 330 mm/13")
330 ± 1.0
100 ± 1.0
13 +0.50/-0.20
9.0 ± 0.2
14.4
12 (Ø 178 mm/7")
178 ± 1.0
60 ± 1.0
13 +0.50/-0.20
13.4 ± 1.5
18.4
P ROPERTIES OF REEL
Material: polystyrene
Surface resistance: 220nF
* Applied 1.5 x Ur
0402/X7R/50V/>10nF
0603/X7R/25V/>220nF; 0603/X7R/50V/220nF
0603/X7R/100V/≥100nF
0805/X7R/100V/≥ 470nF
7
External Visual
Any applicable method using × 10 magnification
In accordance with specification
8
Physical Dimension
Verify physical dimensions to the applicable device
specification.
In accordance with specification
∆C/C
Three shocks in each direction shall be applied along the three NPO: Within ± 0.5% or 0.5 pF,
mutually perpendicular axes of the test specimen
whichever is greater
(18 shocks)
X7R: ± 10%
9
Mechanical Shock
Peak value: 1,500 g’s
Duration: 0.5 ms
Velocity change: 15.4 ft/s
Waveform: Half-sin
10
Vibration
5 g’s for 20 minutes, 12 cycles each of 3 orientations.
D.F.
Within initial specified value
IR
Within initial specified value
∆C/C
NP0: Within ± 0.5% or 0.5 pF,
whichever is greater
X7R: ± 10%
Test from 10-2000 Hz.
D.F: meet initial specified value
IR meet initial specified value
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
NO
11
AEC-Q200 TEST
Resistance to Soldering Heat
Automotive grade
NPO/X7R 6.3 V to 2000 V
TEST METHOD
REQUIREMENTS
Precondition: 150 +0/–10 °C for 1 hour, then keep for 24 ± 1
hours at room temperature
Preheating: for size ≤ 1206: 120 °C to 150 °C for 1 minute
Preheating: for size >1206: 100 °C to 120 °C for 1 minute and
170 °C to 200 °C for 1 minute
Solder bath temperature: 260± 5 °C
Dipping time: 10± 0.5 seconds
Recovery time: 24± 2 hours
Dissolution of the end face
plating shall not exceed 25% of
the length of the edge
concerned
∆C/C
NPO: Within ± 1% or 0.5 pF,
whichever is greater.
X7R: ± 10%
D.F. within initial specified value
IR within initial specified value
12
Thermal Shock
1. Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for 24± 1 hour at room
temp
2. Initial measure:
Spec: refer to initial spec C, D, IR
3. Rapid change of temperature test:
-55 °C to +125 °C; 300 cycles
15 minutes at -55°C ;
15 minutes at 125 °C
4. Recovery time:
NPO: 6 to 24 hours
X7R: 24± 2 hours
5. Final measure: C, D, IR
No visual damage
∆C/C
NPO: Within ± 1% or 1 pF,
whichever is greater
X7R: ± 15%
D.F: meet initial specified value
IR meet initial specified value
A component passes a voltage
level if all components stressed
at that voltage level pass.
Per AEC-Q200-002
YNM0053-1
6 kV
DC
FAIL
PASS
2 kV
DC
FAIL
13
ESD
12 kV
AD
PASS
1 kV
DC
FAIL
FAIL
< 500 V
DC
4 kV
DC
PASS
500 V
DC
FAIL
1 kV
DC
FAIL
2 kV
DC
PASS
8 kV
DC
PASS
4 kV
DC
FAIL
6 kV
DC
16 kV
AD
PASS
8 kV
DC
PASS
500 V
DC
FAIL
PASS
12 kV
AD
25 kV
AD
FAIL
PASS
16 kV
AD
25 kV
AD
Note: Classify the components according to the highest ESD voltage level survived during ESD testing.
Fig. 7 Passive component HBM ESD test flow diagram
(DC = Direct Contact Discharge, AD = Air Discharge)
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
NO
14
AEC-Q200 TEST
Solderability
Capacitance
15
Electrical
Characterization
Dissipation
Factor (D.F.)
Insulation
Resistance
(I.R.)
Automotive grade
NPO/X7R 6.3 V to 2000 V
TEST METHOD
REQUIREMENTS
1. Preheat at 155°C for 4 hours. After preheating, immerse the
capacitor in a solution of ethanol and rosin (25% rosin in
weight proportion). Immerse in eutectic solder solution for
5+0/-0.5 seconds at 235± 5°C.
2. Should be placed into steam aging for 8 hours± 15 minutes.
After preheating, immerse the capacitor in a solution of
ethanol and rosin (25% rosin in weight proportion).
Immerse in eutectic solder solution for 5+0/-0.5 seconds at
235± 5°C.
3. Should be placed into steam aging for 8 hours± 15 minutes.
After preheating, immerse the capacitor in a solution of
Ethanol and rosin (25% rosin in weight proportion).
Immerse in eutectic solder solution for 120± 5 seconds at
260± 5°C.
The solder should cover over
95% of the critical area of each
termination.
NPO:
f = 1 MHz for C ≤ 1nF, measuring at voltage 1 Vrms at 25 °C
f = 1 KHz for C > 1nF, measuring at voltage 1 Vrms at 25 °C
X7R:
At 25 °C, 24 hours after annealing
f = 1 KHz, measuring at voltage 1 Vrms at 25 °C
Within specified tolerance
NPO:
f = 1 MHz for C ≤ 1nF, measuring at voltage 1 Vrms at 25 °C
f = 1 KHz for C > 1nF, measuring at voltage 1 Vrms at 25°C
X7R:
At 25 °C, 24 hours after annealing
f = 1 KHz, measuring at voltage 1 Vrms at 25 °C
In accordance with specification
on Table 13
At Ur (DC) for 1 minute
In accordance with specification
on Table 13
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
NO
AEC-Q200 TEST
Temperature
coefficient
15
Electrical
Characterization
Automotive grade
TEST METHOD
NPO/X7R 6.3 V to 2000 V
REQUIREMENTS
Capacitance shall be measured by the steps shown in the
following table.
∆C/C
NPO: ± 30ppm /°C
The capacitance change should be measured after 5 min at
each specified temperature stage.
X7R: ± 15%
Step
Temperature(°C)
a
25± 2
b
Lower temperature± 3°C
c
25± 2
d
Upper Temperature± 2°C
e
25± 2
(1) NPO
Temperature Coefficient shall be calculated from the formula
as below
C2 - C1
Temp, Coefficient =
106 [ppm/°C]
C1 xΔT
C1: Capacitance at step c
C2: Capacitance at 125°C
∆T: 100°C (=125°C -25°C)
(2) X7R
Capacitance Change shall be calculated from the formula as
below
C2 - C1
∆C =
x 100%
C1
C1: Capacitance at step c
C2: Capacitance at step b or d
Voltage
Proof
1. Specified stress voltage applied for 1~5 seconds
2. Ur ≤ 100 V: series applied 2.5 Ur
3. 100 V < Ur ≤ 200 V series applied (1.5 Ur + 100)
4. 200 V < Ur ≤ 500 V series applied (1.3 Ur + 100)
5. Ur ≥ 500 V: 1.3 Ur
6. Ur ≥ 1000 V: 1.2 Ur
Charge/Discharge current is less than 50 mA
No breakdown or flashover
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
NO
AEC-Q200 TEST
Automotive grade
NPO/X7R 6.3 V to 2000 V
TEST METHOD
REQUIREMENTS
Part mounted on a 100mm × 40mm FR4 PCB board, which is
1.6± 0.2 mm thick and has a layer-thickness 35µm± 10 µm.
Part should be mounted using the following soldering reflow
profile.
Conditions:
∆C/C
NPO: Within ± 1% or 0.5 pF,
whichever is greater
X7R: ± 10%
NPO:
Bending 3 mm at a rate of 1 mm/s, radius jig 340 mm
X7R:
Bending 2 mm at a rate of 1 mm/s, radius jig 340 mm
16
Board Flex
Dimension(mm)
Test Substrate:
b
C
4.5
YNSC147
40
a
100
Type
a
b
c
0201
0.3
0.9
0.3
0402
0.4
1.5
0.5
0603
1.0
3.0
1.2
0805
1.2
4.0
1.65
1206
2.2
5.0
1.65
1210
2.2
5.0
2.0
1808
3.5
7.0
3.7
unit: mm
17
Terminal Strength
With the component mounted on a PCB obtained with the
device to be tested, apply a 17.7N (1.8Kg) force to the side of
a device being tested.
This force shall be applied for 60+1 seconds.
Also the force shall be applied gradually as not to apply a
shock to the component being tested.
* Apply 2N force for 0402 size.
* Apply 1N force for 0201 size.
Place the part in the beam load fixture. Apply a force until the
part breaks or the minimum acceptable force level required in
the user specification(s) is attained.
18
Beam Load Test
Magnification of 20X or greater
may be employed for
inspection of the mechanical
integrity of the device body,
terminals and body/terminal
junction.
Before, during and after the
test, the device shall comply
with all electrical requirements
stated in this specification.
≤ 0805
Thickness > 0.5mm: 20N
Thickness ≤ 0.5mm: 8N
≥ 1206
Thickness ≥1.25 mm: 54N
Thickness < 1.25 mm: 15N
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
REVISION HISTORY
REVISION DATE
CHANGE NOTIFICATION
-
DESCRIPTION
Version 17
Jan. 14, 2022
Version 16
Nov. 17, 2021 -
- Add 1206/X7R/500V to 1000V/220pF to 1nF
Version 15
Oct. 12, 2021
- Add 0603/NPO/25V/50V/2.7nF to 10nF
-
- Add 1206/NPO/2000V/10pF to 47pF
- I.R. for NPO change to " I.R. ≥ 100 GΩ or I.R. × C ≥ 1000Ω.F. whichever
is less"
Version 14
Aug. 09, 2021
-
- Add 1206/NPO/1kV/10pF to 220pF
1206/X7R/1kV/1nF
Version 13
Jun. 08, 2021
-
- Move out "Array" and "High Cap" to individual specification
Add 0603 NPO 50V/100V 1.2nF to 2.2nF
0402 X7R 50V 15nF to 100nF
0603 X7R 25V 330nF to 680nF
0603 X7R 50V 150nF to 220nF
0603 X7R 100V 68nF to 100nF
- Add 0201/ X7R/ 50V / 100 pF to 1nF
0603/ X7R/ 16V / 680nF to 1µF
0603/ X7R/ 25V / 150nF / 220nF/ 1µF
1210/ X7R/ 50V / 4.7µF
Version 12
Feb. 26, 2021
Version 11
Jun. 29, 2018
-
May. 2, 2018
-
- Add 0201 NPO 25V/ 50V, 0.2pF to 33pF, Add 0402 NPO 50V 270pF to
1nF, Add 0805 X7R 25V 2.2uF
- Add 0603 NPO 100V 820pF to 1nF,
- Add 0805 NPO 50V to 100V, 1.2nF to 10nF,
Version 10
- Add 0805 X7R 16V 2.2uF, 50V 680nF to 1uF,
- Add 1206 X7R 100V 330nF to 2.2uF, 250V 33nF to 100nF
Version 9
Mar. 22, 2018
Version 8
Nov. 22, 2017 -
- Add X7R/0201/25V/100pF~10nF
Version 7
Jul. 7, 2017
- Add X7R/0805/330nF to 470nF/50V, X7R/1206/10uF/6.3V
Version 6
Mar. 31, 2017
-
-
- Add 0402 X7R 100nF 25~50V
- Add NPO/0603/1nF/50V, X7R/0603/1uF/10V, X7R/0603/470nF/16V,
X7R/0603/220nF/25V
Version 5
Nov. 15, 2016 -
- Add Soldering Condition
Version 4
Jun. 14, 2016
-
- Add X7R/0805/2.2uF/10V and NPO/1206/1.2nF to 1.5nF/250V
Version 3
Jul. 21, 2015
-
- Tests and Requirements update
Version 2
Jul. 17, 2014
-
- Tests and Requirements update
Version 1
Apr. 19, 2013
-
- Capacitance range update
Version 0
Dec. 25, 2012
-
- New
www.yageo.com
Jan. 14, 2022 V.17
Product specification
Surface-Mount Ceramic Multilayer Capacitors
Automotive grade
NPO/X7R 6.3 V to 2000 V
LEGAL DISCLAIMER
YAGEO, its distributors and agents (collectively, “YAGEO”), hereby disclaims any and all liabilities for any
errors, inaccuracies or incompleteness contained in any product related information, including but not limited
to product specifications, datasheets, pictures and/or graphics. YAGEO may make changes, modifications and/or
improvements to product related information at any time and without notice.
YAGEO makes no representation, warranty, and/or guarantee about the fitness of its products for any
particular purpose or the continuing production of any of its products. To the maximum extent permitted by
law, YAGEO disclaims (i) any and all liability arising out of the application or use of any YAGEO product, (ii)
any and all liability, including without limitation s pecial, consequential or incidental damages, and (iii) any and all
implied warranties, including warranties of fitness for a particular purpose, non -infringement and
merchantability.
YAGEO products are designed for general purpose applications under normal operation and usage conditions.
Please contact YAGEO for the applications listed below which require especially high reliability for the
prevention of defects which might directly cause damage to the third party's life, body or property: Aerospace
equipment (artificial satellite, rocket, etc.), Atomic energy-related equipment, Aviation equipment, Disaster
prevention equipment, crime prevention equipment, Electric heating apparatus, burning equipment, Highly
public information network equipment, data-processing equipment , Medical devices, Military equipment, Power
generation control equipment, Safety equipment, Traffic signal equipment, Transportation equipment and
Undersea equipment, or for any other application or use in which the failure of YAGEO produ cts could result
in personal injury or death, or serious property damage.
Information provided here is intended to indicate product specifications only. YAGEO reserves all the rights
for revising this content without further notification, as long as produ cts are unchanged. Any product change
will be announced by PCN.
www.yageo.com
Jan. 14, 2022 V.17