JA3D-C1001163

Jabil PA 4035 CF Filament Technical Data Sheet _______________________________________________________________________________ Product Description PA 4035 CF is a carbon fiber PA12 copolymer which provides greater stiffness, strength and toughness over  similar products on the market. The high carbon fiber loading provides superior tensile strength and modulus  while the PA12 base promotes relatively high ductility and ease of handling. Special formulation and  processing reduce filament breakage during loading and printing. PA 4035 CF prints on any open-source  desktop filament 3D printer. PA 4035 CF is well suited for printing ducting in automotive and aerospace applications, casting patterns,  composite tooling and prosthetics. For demanding applications within the aerospace and automotive  industries, the filament provides high heat deflection temperatures. The dimensional stability also increases  compared to standard nylon due to the additional of carbon fiber. In addition, PA 4035 CF increases stiffness  and strength in load bearing orientations while showing less warping than standard nylon.  Available in black, 2.85 mm and 1.75 mm.  Advantages PA 4035 CF is an extremely strong and stiff material which is great for products that require additional  strength. Advantages are: •High strength, stiffness and toughness •Mechanical properties can be tailored by adjusting fill orientation •Superior printed part surface finish quality •Ease of handling filament during loading and printing •Surface resistivity of ≤E9 for ESD sensitive applications •Low print temperature enables the use on more machines Storage and Use PA 4035 CF is moderately hygroscopic, meaning it will absorb and retain some moisture from the atmosphere,  affecting visual quality and mechanical properties. For best results, print and store filament in a dry  environment. If necessary, dry filament in an oven at 80 °C (175 °F) for 3 – 4 hours.  Properties Mechanical Properties1 Test Condition  Tensile Modulus (GPa)  Tensile Elongation at Break (%)  Ultimate Tensile Strength (MPa)  Flexural Modulus (GPa)  Flexural Strength (MPa)  Izod Impact (J/m)  Izod impact (J/m)  +/- 45° Infill +/- 45° Infill Notched Un-Notched Typical Value  6.0 3.9 66 5.1 110 191 557 Method  ASTM D638, Type I  ASTM D790 ASTM D256  ________________________________________________________________________________________ United States: en 19-MT60-00016-B Page 1 of 3 Jabil PA 4035 CF Filament Technical Data Sheet _______________________________________________________________________________ 1. Testing conducted on bars printed in XY orientation at 250°C and tested dry. Typical values are  for reference only.  Thermal Properties1 Typical Method  Value  HDT @ 0.455 MPa (°C)  154 +/- 45° Infill DMA HDT @ 1.82 MPa (°C)  89 20 °C/min Melt Temperature (°C) 180 DSC 1. Testing conducted on bars printed in XY orientation at 250°C and tested dry. Typical values are  for reference only.  Test Condition  Other Properties  Test Condition  Density Diameter: Mean, Indiv. Axis (mm) N/A In-line, 100% inspection Typical Value  1.18 +/- 0.05  Method  Gas Pycnometer Laser Micrometer ________________________________________________________________________________________ United States: en 19-MT60-00016-B Page 2 of 3 Jabil PA 4035 CF Filament Technical Data Sheet _______________________________________________________________________________ Disclaimer: The information in this technical data sheet, including material properties, are obtained from testing  representative samples under carefully controlled conditions and are provided for reference only. Material properties  may be impacted by storage, handling, processing equipment/parameters, and product design, among other factors.  The information is not a substitute for user testing to determine fitness for any specific use and the user is responsible  for ensuring safe and lawful use of the product.   No express or implied warranties are provided and the implied warranties of merchantability or fitness for a particular  purpose are expressly disclaimed. No representations are made, and no liability is assumed arising from or relating to  the product.  Copyright/Trademark: © 2019 Jabil Inc. All rights reserved. JABIL® and the JABIL logo are registered trademarks  of Jabil Inc.   ________________________________________________________________________________________ United States: en 19-MT60-00016-B Page 3 of 3