JA3D-C1001265

Jabil PA 4535 CF Filament Technical Data Sheet _______________________________________________________________________________ Product Description PA 4535 CF is among the strongest PA6 co-polymer carbon fiber filaments available on the market, delivering increased strength and stiffness. Typical applications for PA 4535 CF are aluminum replacement parts, housings that require tight printing dimensional tolerances, clips, brackets, retainers, covers, in addition to jigs, fixtures, and tooling. Advantages PA 4535 CF has the highest carbon fiber loading available in the industry, providing 40% improvement in tensile strength, impact strength, Z strength and elongation at break, with the added benefit of being ESD safe. Additionally, the combination of carbon fiber in the already extremely low-warp nylon results in extraordinarily flat prints. Storage and Use PA 4535 CF is highly hygroscopic, meaning it will quickly absorb and retain moisture from the atmosphere, affecting visual quality and mechanical properties. For best results, print and store filament in a dry environment. If necessary, dry filament in an oven at up to 75 °C (165 °F) for 6 - 12 hours. Due to its high stiffness, material feeding may be challenging near the end of the spool or when the filament is very dry. Pre-heating the filament or allowing the filament to absorb a small amount of moisture from the atmosphere will make it more workable. Download Jabil's optimized print profile by clicking here. Properties Mechanical Properties - Dry as Printed1 Test Condition Tensile Modulus (MPa) Tensile Elongation at Break (%) Ultimate Tensile Strength (MPa) Flexural Modulus (MPa) Flexural Strength (MPa) Flexural Strain (%) Izod Impact, notched (J/m) Izod impact, un-notched (J/m) 1. Testing conducted on bars printed are for reference only. XY coupons, Ambient XY coupons, Ambient XY coupons, Ambient XY coupons, Ambient at 270 °C and tested at Typical Method Value 10600 ASTM D638, Type I 2.9 88.0 5420 ASTM D790 118 4.3 125 ASTM D256 525 5% Izod Impact, notched (J/m) XY coupons, Ambient 193 ASTM D256 Izod impact, un-notched (J/m) XY coupons, Ambient 653 1. Testing conducted on bars printed at 270 °C and conditioned for 14 days at 23 °C and 50 % RH. Typical values are for reference only. Test Condition Thermal Properties Test Condition Heat Deflection Temperature (°C) Heat Deflection Temperature (°C) Melt Temperature, Peak (°C) 0.455 Mpa 1.82 Mpa 20°C/min ramp Typical Value 162 91 190 Method DMA DMA DSC Other Physical Properties Test Condition Density (g/cm3) Ambient Typical Value 1.26 Method ASTM D792 Dimensional Properties Test Condition Diameter: Mean, Indiv. Axis (mm) In-line, 100% inspection Typical Value 1.75±0.05 2.85±0.05 Method Laser Micrometer ________________________________________________________________________________________ United States: en 19-MT60-00037 Rev A Page 2 of 3 Jabil PA 4535 CF Filament Technical Data Sheet _______________________________________________________________________________ Disclaimer: The information in this technical data sheet, including material properties, are obtained from testing representative samples under carefully controlled conditions and are provided for reference only. Material properties may be impacted by storage, handling, processing equipment/parameters, and product design, among other factors. The information is not a substitute for user testing to determine fitness for any specific use and the user is responsible for ensuring safe and lawful use of the product. No express or implied warranties are provided and the implied warranties of merchantability or fitness for a particular purpose are expressly disclaimed. No representations are made, and no liability is assumed arising from or relating to the product. Copyright/Trademark: © 2019 Jabil Inc. All rights reserved. JABIL® and the JABIL logo are registered trademarks of Jabil Inc. ________________________________________________________________________________________ United States: en 19-MT60-00037 Rev A Page 3 of 3