ER1020-000

MT-FEP FEP Heat Shrink Tubing Applications • Process aid for reflowing catheter shafts • Process aid for joint bonding PROFILE • Shrink ratio < _ 1.6:1 • Full recovery at 210°C (410°F) minimum • Tight longitudinal change control as low as ± 2% • Manufactured to ISO 10993 standards • Custom sizing, finishing options available • Translucent for high optical clarity • Color blending option available ABOUT • MT-FEP is a fluorinated ethylene propylene (FEP) heat shrink tubing. FEP offers excellent consistency, high dielectric strength and is chemically inert. MT-FEP is lubricious and semi-rigid with shrink ratios up to 2:1*. FEP is the industry gold standard for reflowing catheter shafts and bonding joints. • For our MT-FEP, we can control longitudinal growth ± 2% ensuring consistency on lot-to-lot, reducing waste and cost. *Upper limit on select applications. Optimal shrink ratio is 1.6:1 TABLE 1: DIMENSIONS As Supplied Size Recovered Inside Diameter Minimum (D) Inside Diameter Maximum (d) in. mm. in. mm. Minimum in. mm. Wall Thickness (W) Maximum in. mm. Nominal in. mm. 1/32 0.035 0.9 0.025 0.6 0.006 0.15 0.010 0.25 0.008 0.20 3/64 0.045 1.1 0.032 0.8 0.006 0.15 0.010 0.25 0.008 0.20 1/16 0.063 1.6 0.040 1.0 0.006 0.15 0.010 0.25 0.008 0.20 3/32 0.093 2.4 0.056 1.4 0.006 0.15 0.010 0.25 0.008 0.20 1/8 0.125 3.2 0.075 1.9 0.007 0.18 0.013 0.33 0.010 0.25 3/16 0.188 4.8 0.115 2.9 0.007 0.18 0.013 0.33 0.010 0.25 1/4 0.250 6.4 0.150 3.8 0.007 0.18 0.013 0.33 0.010 0.25 3/8 0.375 9.5 0.225 5.7 0.009 0.23 0.015 0.38 0.012 0.30 1/2 0.500 12.7 0.300 7.6 0.011 0.28 0.019 0.48 0.015 0.38 MEDICAL /// Heat Shrink Tubing — MT-FEP Heat Shrink Tubing — MT-FEP TABLE 3: PROPERTIES Property Unit Requirement Test Method Physical Dimensions* inches (mm) In accordance with Table 1 Longitudinal change* percent Concentricity as supplied* percent Tensile strength* Ultimate elongation* Secant modulus* (expanded) Heat resistance 168 hours at 175°C (347°F) Followed by test for: Ultimate elongation Electrical Dielectric strength psi (MPa) percent psi (MPa) +0, -10 maximum 70 minimum (2:1 Exp. ratio) 60 minimum (3:1 Exp. ratio) 2000 minimum (10:3) 200 minimum 2.5 x 104 maximum (172) percent 100 minimum ASTM D 2671, 20"/minute volts/mil (volts/mm) 500 minimum (19.7) ASTM D 2671 sec 60 minimum ASTM D 2671 Dielectric withstand 3000V, 60Hz Chemical Fluid resistance 24 hours at 23 ± 3°C (77 ± 5°F) Isopropyl alcohol 5% saline solution Disinfectant Followed by tests for: Dielectric strength ASTM D 2671 ASTM D 2671 ASTM D 2671, 20"/minute ASTM D 2671 ASTM D 2671 volts/mil (volts/mm) 400 minimum (15.7) Tensile strength psi (MPa) 1000 minimum (6.9) Heavy metals analysis Cadmium Mercury Lead Bismuth Antimony ppm 1 maximum (total of all metals) ASTM D 2671 USP XXII Physiochemical tests-plastic (Note 1) *Denotes lot acceptance test Note 1: Sample preparation and extraction is per USP XXII. Metals analysis may be colorimetric as described in USP XXII or by equivalent quantitative analytical method. te.com/medical AMERICAS EMEA ASIA +1 866 251 3352 +49 6151 607 1999 China +86 400 820 6015 Japan +81 44 844 8041 Korea +82 2 3415 4506 Singapore +86 512 6255 4384 MEDICAL /// Heat Shrink Tubing — MT-FEP TE Connectivity, TE, TE connectivity (logo) and Raychem are trademarks. © 2020 TE Connectivity Ltd. family of companies. All Rights Reserved.